02139nas a2200253   4500008004100000022001400041245016900055210006900224260000800293300001400301490000600315520119100321653001901512653003001531653002001561653003201581653002801613100002801641700002501669700001801694700002101712700002401733856012801757       2017                        eng d  a2196-021600aNitrogen-doped graphene with a three-dimensional architecture assisted by carbon nitride tetrapods as an efficient metal-free electrocatalyst for hydrogen evolution0 aNitrogendoped graphene with a threedimensional architecture assi  cOCT  a2643-26520 v43 aCurrent polymer membrane-based electrolyzers use Pt as a cathode catalyst for efficient reduction of water. The high cost of Pt-based catalysts forces researchers to develop alternative electrocatalysts. Here, a simple strategy has been proposed to synthesize a metal-free electrocatalyst for the hydrogen evolution reaction (HER) by high-temperature annealing of graphene oxide-coated melamine foam. The prepared catalyst possesses both structural and functional advantages with its three-dimensional (3D) interconnected arms of carbon nitride (CNx) backbone wrapped with nitrogen-doped graphene (N-RGO) sheets (CNx@N-RGO). CNx@N-RGO faces only a 193 mV overpotential to achieve a current density of 10mAcm(-2), which is far superior to the previously reported Pt-free systems. Along with the high exchange current density 34.7 x 10(-6)A cm(-2) and low Tafel slope of 54 mV dec(-1), CNx@N-RGO follows a Volmer-Heyrovsky mechanism for the HER. DFT calculations show that the synergy between CNx and N-RGO facilitates good electrical coupling between the two moieties and provides optimal binding to H+ ions on the catalyst that, in turn, results in efficient reduction of hydrogen ions.10acarbon nitride10aDensity functional theory10aelectrocatalyst10ahydrogen evolution reaction10anitrogen doped graphene1 aGangadharan, Pranav, K.1 aUnni, SreeKuttan, M.1 aKumar, Nandha1 aGhosh, Prasenjit1 aKurungot, Sreekumar  uhttps://library.ncl.res.in/content/nitrogen-doped-graphene-three-dimensional-architecture-assisted-carbon-nitride-tetrapods02731nas a2200277   4500008004100000022001400041245015700055210006900212260000900281300001400290490000600304520175500310653001902065653003002084653003202114653001802146653001802164100001702182700001902199700001702218700002302235700002202258700003002280700001802310856012502328       2021                        eng d  a2574-096200aOne-dimensional multichannel g-C3N4.7 nanostructure realizing an efficient photocatalytic hydrogen evolution reaction and its theoretical investigations0 aOnedimensional multichannel gC3N47 nanostructure realizing an ef  cAPR   a3118-31290 v43 a<p>The emerging metal-free carbon nitride (C3N4) offers prominent possibilities for realizing the highly effective hydrogen evolution reaction (HER). However, its poor surface conductivity and insufficient catalytic sites hinder the HER performance. Herein, a one-dimensional vermicular rope-like graphitic carbon nitride nanostructure is demonstrated that consists of multichannel tubular pores and high nitrogen content, which is fabricated through a cost-effective approach having the final stoichiometry g-C3N4.7 for HER application. The present g-C3N4.7 is unique owing to the presence of abundant channels for the diffusion process, modulated surface chemistry with rich- electroactive sites from N-electron lone pairs, greatly reduced recombination rate of photoexcited exciton pairs, and a high donor concentration (4.26 x 10(17) cm(3)). The catalyst offers a visible-light-driven photocatalytic H-2 evolution rate as high as 4910 mu mol h(-1)g(-1) with an apparent quantum yield of 14.07% at band gap absorption (2.59 eV, 479 nm) under 7.68 mW cm(-2) illumination. The number of hydrogen gas molecules produced is 1.307 x 10(15) s(-1) cm(-2), which remained constant for a minimum of 18 h of repeated cycling in the HER without any degradation of the catalyst. In density functional theory calculations, a significant change in the band offset is observed due to N doping into the system in favor of electron catalysis. The theoretical band gap of a monolayer of g-C3N4.7 was enormously reduced because of the presence of additional densities of states from the doped N atom inside the band gap. These impurity or donor bands are formed inside the band gap region, which ultimately enhance the hydrogen ion reduction reaction enormously.</p>10acarbon nitride10aDensity functional theory10ahydrogen evolution reaction10anitrogen-rich10aPhotocatalyst1 aAntil, Bindu1 aKumar, Lakshya1 aRanjan, Ravi1 aShenoy, Sulakshana1 aTarafder, Kartick1 aGopinath, Chinnakonda, S.1 aDeka, Sasanka  uhttps://library.ncl.res.in/content/one-dimensional-multichannel-g-c3n47-nanostructure-realizing-efficient-photocatalytic