02050nas a2200229   4500008004100000022001400041245008400055210006900139260000800208300001100216490000800227520128700235653001301522653003201535653001301567653002701580653001301607100002701620700003701647700002701684856010901711       2023                        eng d  a0021-899500aEvaluation of the adhesive properties of vanillin-derived polyhydroxy urethanes0 aEvaluation of the adhesive properties of vanillinderived polyhyd  cDec  ae546470 v1403 a<p>
	Poly(hydroxy urethanes) (PHUs) have been considered attractive and safer variants of conventional polyurethanes (PUs). To improve the prerequisites of green and sustainable chemistry herein, we propose the synthesis and utilization of cyclic carbonate monomers majorly derived from vanillin, a lignin derivative, and CO2 for the development of PHUs. Kinetic evaluation on the polymerization temperature ascertained 80 degrees C as the optimum condition for PHU synthesis. The structural evaluation of PHUs was carried out by various spectroscopic techniques, such as FTIR, (HNMR)-H-1, and C-13-NMR, molar masses were determined by gel permeation chromatography (Mn varied between 2500 and 11,100 g/mol), and thermal properties evaluated by differential scanning calorimeter (Tg in the ranges of 28-42 degrees C), and thermogravimetric analysis (stable above 180 degrees C). Since the PHUs are enriched with pendant hydroxyl groups on their backbone which can promote adhesion, lap shear studies on the aluminum substrate exhibited a maximum shear strength of 1.65 +/- 0.37 MPa. This study demonstrates an attractive and environment-friendly pathway for developing novel PHUs network using renewable biobased resources and further explores its applicability as adhesives.</p>
10aadhesive10abiobased cyclic dicarbonate10adiamines10apoly(hydroxyurethane)s10aVanillin1 aGhuge, Gorakh, Hiraman1 aKambikanam, Karthika, Vayalacher1 aNair, Kiran, Sukumaran  uhttps://library.ncl.res.in/content/evaluation-adhesive-properties-vanillin-derived-polyhydroxy-urethanes02477nas a2200301   4500008004100000022001400041245012900055210006900184260000800253300001100261490000800272520146800280653002901748653001301777653001801790653001601808653001401824653001401838653002301852100002201875700002301897700002601920700002301946700002501969700002601994700002802020856012702048       2024                        eng d  a0014-305700aCatechol- and phenolic hydroxyl-functionalized partially bio-based (Co) poly(ether sulfone)s with multifarious applicability0 aCatechol and phenolic hydroxylfunctionalized partially biobased   cNOV  a1134840 v2203 a<p>
	A largely bio-based new bisphenol, namely, 4,4 `-((3,4-dimethoxyphenyl)methylene)-bis(2-methoxyphenol) (DMBM) was synthesized by the reaction of veratraldehyde with guaiacol. DMBM and varying compositions of DMBM and bisphenol A were polycondensed with bis(4-fluorophenyl) sulfone to afford reasonably high molecular weight film-forming (co)poly(ether sulfone)s possessing built-in methoxyl groups. T10 and Tg values of (co)poly(ether sulfone)s were in the range 382-478 degrees C and 171-187 degrees C, respectively indicating their good thermal stability and the values decreased with increase in mol % incorporation of DMBM. The methoxyl groups present in (co)poly (ether sulfone)s were quantitatively de-blocked resulting in the formation of corresponding polymers possessing pendant catechol moieties and free phenolic hydroxyl groups. By virtue of the presence of these functional moieties, (co)poly(ether sulfone)s are amenable for post-polymerization modifications, and exhibited properties such as antimicrobial (23 mm against Staphylococcus aureus and 18 mm against Escherichia coli)), antioxidant (72 % scavenger of free radicals), adhesive (2.24 MPa lap shear strength) and usefulness as redox-active agent in zinc-ion batteries. These data underscore the promise of DMBM as a versatile monomer of wider utility for the synthesis of functional (co)poly(ether sulfone)s capable of expanding their applicability beyond the conventional ones.</p>
10a(Co)poly(ether sulfone)s10aadhesive10aAntimicrobial10aAntioxidant10abio-based10abisphenol10aZinc-ion batteries1 aWale, Apparav, K.1 aJagtap, Ashish, S.1 aPandey, Priyanshi, R.1 aDastager, Syed, G.1 aShelke, Manjusha, V.1 aAmbade, Ashootosh, V.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/catechol-and-phenolic-hydroxyl-functionalized-partially-bio-based-co-polyether-sulfones