02443nas a2200289   4500008004100000022001400041245012500055210006900180260007300249300001200322490000700334520143500341653001301776653002201789653001101811653003401822653002001856653000901876653002201885653000901907100001901916700002801935700001901963700002001982700002302002856012802025       2009                        eng d  a0926-337300aSupport modification to improve the sulphur tolerance of Ag/Al2O3 for SCR of NOx with propene under lean-burn conditions0 aSupport modification to improve the sulphur tolerance of AgAl2O3  aPO BOX 211, 1000 AE AMSTERDAM, NETHERLANDSbELSEVIER SCIENCE BVcAUG  a416-4250 v903 a<p>Ag/Al2O3 catalysts with 1 wt% SiO2 or TiO2 doping in alumina support have been prepared by wet impregnation method and tested for sulphur tolerance during the selective catalytic reduction (SCR) of NOx using propene under lean conditions, Ag/Al2O3 showed 44% NOx conversion at 623 K, which was drastically reduced to 21% when exposed to 20 ppm SO2. When Al2O3 support in Ag/Al2O3 Was doped with 1 wt% SiO2 or TiO2 the NOx conversion remained constant in presence of SO2 showing the improved sulphur tolerance of these catalysts. Subsequent water addition does not induce significant deactivation. On the contrary, a slight promotional effect on the activity of NO conversion to nitrogen is observed after Si and Ti incorporation. FTIR study showed the sulphation of silver and aluminum sites of Ag/Al2O3 catalysts resulting in the decrease in the formation of reactive intermediate species such as -NCO, which in turn decreases NOx conversion to N-2. In the case of Ag/Al2O3 doped with SiO2 or TiO2, formation of silver sulphate and aluminum sulphate was drastically reduced, which was evident in FTIR resulting in remarkable improvement in the sulphur tolerance of Ag/Al2O3 catalyst. These catalysts before and after the reaction have been characterized with various techniques (XRD, BET surface area, transmittance FTIR and pyridine adsorption) for physico-chemical properties. (C) 2009 Elsevier B.V. All rights reserved.</p>10aAg/Al2O310aAluminum sulphate10aDRIFTS10aSelective catalytic reduction10aSilver sulphate10aSiO210aSulphur tolerance10aTiO21 aJagtap, Neelam1 aUmbarkar, Shubhangi, B.1 aMiquel, Pierre1 aGranger, Pascal1 aDongare, Mohan, K.  uhttps://library.ncl.res.in/content/support-modification-improve-sulphur-tolerance-agal2o3-scr-nox-propene-under-lean-burn-002690nas a2200265   4500008004100000022001400041245013600055210006900191260007300260300001200333490000800345520169200353653003002045653002002075653001502095653002702110653002002137100002002157700002002177700002002197700002502217700002302242700002802265856013102293       2015                        eng d  a0926-337300aActivation by pretreatment of Ag-Au/Al2O3 bimetallic catalyst to improve low temperature HC-SCR of NOx for lean burn engine exhaust0 aActivation by pretreatment of AgAuAl2O3 bimetallic catalyst to i  aPO BOX 211, 1000 AE AMSTERDAM, NETHERLANDSbELSEVIER SCIENCE BVcSEP  a145-1560 v1743 a<p>Bimetallic Ag-Au/Al2O3 catalyst was synthesised by successive impregnation of 1% Au and 1% Ag on in-house prepared high surface area alumina (450 m(2)/g). The corresponding monometallic catalysts were also prepared by loading 1% Ag or 1% Au on the same high surface area alumina for comparison. The catalysts were characterised by various physico-chemical techniques and tested for SCR activity under lean burn engine exhaust conditions. Ag-Au/Al2O3 catalyst prepared by successive impregnation method showed considerably higher NO reduction (100%) to N-2 compared to 1% Au/Al2O3 (70%) whereas the activity was comparable with that of 1% Ag/Al2O3 (96%). The effect of various pretreatments on SCR activity of Ag-Au/Al2O3 was studied and pretreatment at 250 degrees C in flow of hydrogen was found to give the best results with 100% NO conversion to N-2 at 353 degrees C. Further ageing of the catalyst under reaction feed at 500 degrees C resulted in considerable increase in low temperature activity of bimetallic catalyst with similar to 40% NO conversion at 222 degrees C. Even though the SCR activity of pretreated Ag-Au/Al2O3 and Ag/Al2O3 were comparable, after ageing the Ag-Au/Al2O3 showed significantly higher NO conversion (95%) compared to Ag/Al2O3 (83%) and Au/Al2O3 (70%). The formation of H-2 and CO due to steam reforming of higher hydrocarbon (decane) was evidenced at the temperature of highest deNO(x) activity. Detailed investigation of the textural properties of the pretreated and aged catalysts showed presence of well dispersed metallic Au and Ag-n(delta+) clusters after pretreatment in hydrogen at 250 degrees C. (C) 2015 Elsevier B.V. All rights reserved.</p>10aAg-Au bimetallic catalyst10aCatalyst ageing10adispersion10aLow temperature HC-SCR10aSteam reforming1 aMore, Pavan, M.1 aNguyen, Duy, L.1 aGranger, Pascal1 aDujardin, Christophe1 aDongare, Mohan, K.1 aUmbarkar, Shubhangi, B.  uhttps://library.ncl.res.in/content/activation-pretreatment-ag-aual2o3-bimetallic-catalyst-improve-low-temperature-hc-scr-nox-0