02333nas a2200241   4500008004100000022001400041245011800055210006900173260008700242300001200329490000700341520139100348653003001739653002101769653001401790653002601804653003101830100002801861700002201889700002101911700002801932856013101960       2013                        eng d  a0954-008300aNew organosoluble aromatic poly(esterimide)s containing pendent pentadecyl chains: synthesis and characterization0 aNew organosoluble aromatic polyesterimides containing pendent pe  a1 OLIVERS YARD, 55 CITY ROAD, LONDON EC1Y 1SP, ENGLANDbSAGE PUBLICATIONS LTDcNOV  a735-7430 v253 a<p>A new diimide dicarboxylic acid, namely 2,2-(4-pentadecyl-1,3-phenylene)bis(1,3-dioxoisoindoline-5-carboxylic acid), containing preformed imide rings and pentadecyl chain, was synthesized by the reaction of 4-pentadecylbenzene-1,3-diamine with trimellitic anhydride. A series of new aromatic poly(esterimide)s (PEIs) was synthesized using diphenylchlorophosphate-activated direct polycondensation of 2,2-(4-pentadecyl-1,3-phenylene)bis(1,3-dioxoisoindoline-5-carboxylic acid), with five commercially available bisphenols, namely 4,4-isopropylidenediphenol (I), 4,4-(hexafluoroisopropylidene)diphenol (II), 4,4-oxydiphenol (III), 4,4-biphenol (IV), and 4,4-(9-fluorenylidene)diphenol (V) in the presence of pyridine and lithium chloride. Inherent viscosities of PEIs were in the range 0.54-0.83dLg(-1) in chloroform (CHCl3) at 30 +/- 0.1 degrees C. PEIs containing pendent pentadecyl chains were soluble in organic solvents such as CHCl3, m-cresol, N, N-dimethylacetamide, 1-methyl-2-pyrrolidinone, pyridine, and nitrobenzene. Tough, transparent, and flexible films of PEIs could be cast from their CHCl3 solutions. PEIs exhibited glass transition temperature in the range 145-198 degrees C. The temperature at 10% weight loss of PEIs, determined by thermogravimetric analysis under the nitrogen atmosphere, was in the range of 450-470 degrees C indicating good thermal stability.</p>10apendent pentadecyl chains10aPolycondensation10aPolyimide10aPreformed imide rings10aThermogravimetric analysis1 aSadavarte, Nilakshi, V.1 aPatil, Sachin, S.1 aAvadhani, C., V.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/new-organosoluble-aromatic-polyesterimides-containing-pendent-pentadecyl-chains-synthesis-0