02437nas a2200253   4500008004100000022001400041245009100055210006900146260000900215300001200224490000700236520160100243653001701844653002001861653001701881653001501898653002001913100002501933700002301958700002101981700003002002700002802032856012302060       2019                        eng d  a0887-624X00aDesign and synthesis of aromatic polyesters bearing pendant clickable maleimide groups0 aDesign and synthesis of aromatic polyesters bearing pendant clic  cMAR   a630-6400 v573 a<p>A bisphenol bearing pendant maleimide group, namely, N-maleimidoethyl-3, 3-bis(4-hydroxyphenyl)-1-isobenzopyrrolidone (PPH-MA) was synthesized starting from phenolphthalein. Aromatic (co)polyesters bearing pendant maleimide groups were synthesized from PPH-MA and aromatic diacid chlorides, namely, isophthaloyl chloride (IPC), terephthaloyl chloride (TPC), and 50:50 mol % mixture of IPC and TPC by low temperature solution polycondensation technique. Copolyesters were also synthesized by polycondensation of different molar proportions of PPH-MA and bisphenol A with IPC. Inherent viscosities and number-average molecular weights of aromatic (co)polyesters were in the range of 0.52-0.97 dL/g and 20,200-32,800 g/mol, respectively indicating formation of medium to reasonably high-molecular-weight polymers. C-13 NMR spectral analysis of copolyesters revealed the formation of random copolymers. The 10% weight loss temperature of (co)polyesters was found in the range 470-484 degrees C, indicating their good thermal stability. A selected aromatic polyester bearing pendant maleimide groups was chemically modified via thiol-maleimide Michael addition reaction with two representative thiol compounds, namely, 4-chlorothiophenol and 1-adamantanethiol to yield post-modified polymers in a quantitative manner. Additionally, it was demonstrated that polyester containing pendant maleimide groups could be used to form insoluble crosslinked gel in the presence of a multifunctional thiol crosslinker. (c) 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 630-640</p>10acrosslinking10amaleimide group10amodification10apolyesters10athiol-maleimide1 aNagane, Samadhan, S.1 aKuhire, Sachin, S.1 aJadhav, Uday, A.1 aDhanmane, Sushilkumar, A.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/design-and-synthesis-aromatic-polyesters-bearing-pendant-clickable-maleimide-groups02274nas a2200241   4500008004100000022001400041245008500055210006900140260000800209490000700217520146300224653003901687653001401726653001701740653002501757653002501782100002301807700002601830700000501856700002501861700002801886856011801914       2021                        eng d  a0959-810300aPartially bio-based furyl-functionalized organosoluble poly(ether ether ketone)s0 aPartially biobased furylfunctionalized organosoluble polyether e  cAUG0 v703 a<p>A new series of partially bio-based (co)poly(ether ether ketone)s bearing pendent furyl groups was synthesized by nucleophilic aromatic substitution polycondensation of varying molar proportions of 4,4 `-(furan-2-ylmethylene)bis(2-methoxyphenol) and bisphenol-A with 4,4 `-difluorobenzophenone. The chemical structures, compositions and random nature of (co)poly(ether ether ketone)s were confirmed by NMR spectroscopy. Inherent viscosities and number-average molecular weights of the (co)poly(ether ether ketone)s were in the range 0.74-2.90 dL g(-1) and 33 500-46 300 g mol(-1), respectively, indicating the formation of reasonably high molecular weight polymers. (Co)poly(ether ether ketone)s were readily soluble in common organic solvents and could be cast into tough, transparent and flexible films from chloroform solutions. (Co)poly(ether ether ketone)s exhibited 10% weight loss and glass transition temperatures in the range 429-464 and 152-156 degrees C, respectively. A representative copoly(ether ether ketone) was crosslinked with 1,1 `-(methylenedi-1,4-phenylene)bismaleimide via Diels-Alder reaction to form a crosslinked polymer which showed improved mechanical properties and was recycled twice without significant loss of mechanical properties. Diels-Alder/retro Diels-Alder reaction was demonstrated by studies of sol-gel transformation, solubility tests, DSC and stress-strain measurements. (c) 2020 Society of Chemical Industry</p>
10aaromatic poly(ether ether ketone)s10abio-based10acrosslinking10aDiels-Alder reaction10apendent furyl groups1 aKuhire, Sachin, S.1 aTalanikar, Aniket, A.1 a1 aNagane, Samadhan, S.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/partially-bio-based-furyl-functionalized-organosoluble-polyether-ether-ketones