02506nas a2200253   4500008004100000022001400041245008900055210006900144260006700213300001200280490000700292520159100299653003501890653002501925653001501950653002501965653002201990100002602012700002602038700002402064700002202088700002802110856011402138       2016                        eng d  a0959-810300aSynthesis and properties of poly(arylene ether)s based on 3-pentadecyl 4,4'-biphenol0 aSynthesis and properties of polyarylene ethers based on 3pentade  a111 RIVER ST, HOBOKEN 07030-5774, NJ USAbWILEY-BLACKWELLcMAY  a567-5760 v653 a<p>A new biphenol, 3-pentadecyl 4,4-biphenol, was synthesized starting from 3-pentadecylphenol and was polycondensed with 4,4-difluorobenzophenone, 1,3-bis(4-fluorobenzoyl)benzene and bis(4-fluorophenyl)sulfone to obtain poly(arylene ether)s with biphenylene linkages in the backbone and pendent pentadecyl chains. Inherent viscosities and number-average molecular weights (M-n) of the poly(arylene ether)s were in the range 0.50 - 0.81 dL g(-1) and 2.2 x 10(4) - 8.3 x 10(4), respectively. Detailed NMR spectroscopic studies of the poly(arylene ether)s indicated the presence of constitutional isomerism which existed because of the non-symmetrical structure of 3-pentadecyl 4,4-biphenol. The poly(arylene ether)s readily dissolved in common organic solvents such as dichloromethane, chloroform and tetrahydrofuran and could be cast into tough, transparent and flexible films from their chloroform solutions. The poly(arylene ether)s exhibited T-g values in the range 35-60 degrees C which are lower than that of reference poly(arylene ether)s without pentadecyl chains. The 10% decomposition temperatures (T-10) of the poly(arylene ether)s were in the range 410-455 degrees C indicating their good thermal stability. A gas permeation study of poly(ether sulfone) containing pendent pentadecyl chains revealed a moderate increase in permeability for helium, hydrogen and oxygen. However, there was a large increase in permeability for carbon dioxide which could be attributed to the internal plasticization effect of pendent pentadecyl chains. (c) 2016 Society of Chemical Industry</p>10acashew nut shell liquid (CNSL)10agas permeation study10apentadecyl10apoly(arylene ether)s10athermal stability1 aTawade, Bhausaheb, V.1 aShaligram, Sayali, V.1 aValsange, Nitin, G.1 aKharul, Ulhas, K.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/synthesis-and-properties-polyarylene-ethers-based-3-pentadecyl-44-biphenol02628nas a2200145   4500008004100000245015400041210006900195260000800264490000700272520199600279100002602275700002402301700002802325856012902353       2017                        eng d00aSynthesis and characterization of polyhydrazides and poly(1,3,4-oxadiazole)s containing multiple arylene ether linkages and pendent pentadecyl chains0 aSynthesis and characterization of polyhydrazides and poly134oxad  cSEP0 v293 a<p>A new diacylhydrazide monomer, namely, 4-(4-(4-(4-(hydrazinocarbonyl)phenoxy)-2-pentadecylphenoxy)phenoxy) benzohydrazide (HPPDPB), was synthesized starting from 4-(4-hydroxyphenoxy)-3-pentadecylphenol. HPPDPB was polycondensed with terephthalic acid chloride (TPC), isophthalic acid chloride (IPC) and a mixture of TPC and IPC (50:50 mol%) to obtain polyhydrazides containing multiple arylene ether linkages in the backbone and pendent pentadecyl chains. Polyhydrazides were subsequently cyclized in the presence of phosphorus oxychloride to obtain the corresponding poly(1,3,4-oxadiazole)s. Polyhydrazides and poly(1,3,4-oxadiazole)s exhibited inherent viscosities in the range 0.65–0.72 dL g−1 and 0.54–0.62 dL g−1, respectively, which indicated the formation of reasonably high-molecular weight polymers. Polyhydrazides were soluble in polar aprotic solvents such as N,N-dimethylformamide, N,N-dimethylacetamide (DMAc), 1-methyl-2-pyrrolidinone and pyridine whereas poly(1,3,4-oxadiazole)s exhibited excellent solubility even in common organic solvents such as chloroform, dichloromethane and tetrahydrofuran. Tough, transparent and flexible films of polyhydrazides and poly(1,3,4-oxadiazole)s could be cast from DMAc and chloroform solutions, respectively. X-Ray diffraction studies revealed amorphous nature of polyhydrazides and poly(1,3,4-oxadiazole)s and the formation of layered structure was observed due to ordered packing of pentadecyl chains. The 10% decomposition temperature (T 10) values for poly(1,3,4-oxadiazole)s were in the range 425–440°C indicating their good thermal stability. Glass transition temperature (T g) values of polyhydrazides and poly(1,3,4-oxadiazole)s were in the range 175–192°C and 92–103°C, respectively. The excellent solubility characteristics and the large gap between T g (92–103°C) and T 10 (425–440°C) values give poly(1,3,4-oxadiazole)-containing pendent pentadecyl chains better opportunities for processability.</p>1 aTawade, Bhausaheb, V.1 aValsange, Nitin, G.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/synthesis-and-characterization-polyhydrazides-and-poly134-oxadiazoles-containing-multiple