02028nas a2200253   4500008004100000022001400041245010000055210006900155260006800224300001200292490000800304520116300312653001301475653002401488653000901512653001901521653001401540100002401554700001801578700002001596700001801616700002001634856012001654       2007                        eng d  a0021-899500aUse of poly(o-toluidine)/ZrO2 nanocomposite coatings for the corrosion protection of mild steel0 aUse of polyotoluidineZrO2 nanocomposite coatings for the corrosi  a111 RIVER ST, HOBOKEN, NJ 07030 USAbJOHN WILEY & SONS INCcOCT  a220-2290 v1063 a<p>This study explored the possibility of using poly(o-toluidine) (POT)/ZrO2 nanocomposite coatings for the corrosion protection of mild steel in a chloride environment. POT/ZrO2 nanocomposite coatings were synthesized on steel substrates through an electrochemical route. These coatings were characterized with cyclic voltammetry, ultraviolet-visible absorption spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and X-ray photoelectron spectroscopy. The performance of POT/ZrO2 nanocomposites as protective coatings against the corrosion of mild steel in aqueous 3 wt % NaCl was evaluated with the potentiodynamic polarization technique and electrochemical impedance spectroscopy. The results of this study demonstrate that POT/ZrO2 nanocomposite coatings provide better protection for mild steel against corrosion than pure POT coatings. The corrosion potential was about 0.312 V versus a saturated calomel electrode, more positive in aqueous 3 wt % NaCl for the nanocomposite-coated steel than the uncoated steel, and the corrosion rate of steel was reduced by a factor of almost 51. (c) 2007 Wiley Periodicals, Inc.</p>10aCoatings10aconjugated polymers10aFTIR10aNanocomposites10asynthesis1 aChaudhari, Sudeshna1 aPatil, P., P.1 aMandale, A., B.1 aPatil, K., R.1 aSainkar, S., R.  uhttps://library.ncl.res.in/content/use-polyo-toluidinezro2-nanocomposite-coatings-corrosion-protection-mild-steel-001936nas a2200265   4500008004100000022001400041245011800055210006900173260005700242300001200299490000600311520097800317653000801295653003201303653003301335653002301368653003501391653001501426653001901441653002201460100002401482700002001506700001801526856012601544       2010                        eng d  a1547-009100aSynthesis and corrosion protection aspects of poly(o-toluidine)/CdO nanoparticle composite coatings on mild steel0 aSynthesis and corrosion protection aspects of polyotoluidineCdO   a233 SPRING ST, NEW YORK, NY 10013 USAbSPRINGERcJAN  a119-1290 v73 a<p>This study examines the possibility of using poly(o-toluidine)/CdO (POT-CdO) nanoparticle composite coating for corrosion protection of mild steel in chloride environment. The POT-CdO nanoparticle composite coating was synthesized on mild steel from aqueous tartrate solution containing CdO-nanoparticles (size similar to 18 nm) by using cyclic voltammetry. These coatings were characterized by cyclic voltammetry, UV-Visible absorption spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and X-ray diffraction measurements. The corrosion protection aspects of the resulting POT-CdO nanocomposite structure were investigated in aqueous 3% NaCl solution by potentiodynamic polarization technique and electrochemical impedance spectroscopy. The results of these investigations reveal that the POT-CdO nanoparticle composite acts as a protective coating on mild steel and reduces the corrosion rate of mild steel almost by factor of 70.</p>10aCdO10aConducting polymer coatings10aCorrosion resistant coatings10acyclic voltammetry10aElectrochemical polymerization10aMild steel10aNanocomposites10aPoly(o-toluidine)1 aChaudhari, Sudeshna1 aGaikwad, A., B.1 aPatil, P., P.  uhttps://library.ncl.res.in/content/synthesis-and-corrosion-protection-aspects-polyo-toluidinecdo-nanoparticle-composite-0