02108nas a2200253 4500008004100000022001400041245015000055210006900205260007300274300001200347490000700359520113700366653003801503653000901541653002101550653001601571653000801587100002201595700002601617700003001643700002201673700002801695856013101723 2012 eng d a1381-514800aAromatic aldehyde functionalized polycaprolactone and polystyrene macromonomers: synthesis, characterization and aldehyde-aminooxy click reaction0 aAromatic aldehyde functionalized polycaprolactone and polystyren aPO BOX 211, 1000 AE AMSTERDAM, NETHERLANDSbELSEVIER SCIENCE BVcOCT a713-7210 v723 a

New bis-aldehyde functionalized initiators, viz, 4,4'-(4,4'-(5-hydroxypentane-2,2-diyl)bis(4,1-phenylene))bis(oxy)dibenza ldehyde (1) and 4,4'-bis(4-(4-(formylphenoxy) phenyl) pentyl 2-bromopropanoate (2) were synthesized starting from commercially available 4,4'-bis(4-hydroxyphenyl) pentanoic acid. These initiators were utilized, respectively, for ring opening polymerization of E-caprolactone and atom transfer radical polymerization of styrene. Well-defined polycaprolactone macromonomers (M-n(GPC): 2600-19400, PDI: 1.37-1.47) and polystyrene macromonomers (M-n(GPC): 2800-28200, PDI: 1.11-1.16) with bis-aldehyde functionality were synthesized. The kinetic study of styrene polymerization showed controlled polymerization behaviour. The presence of aldehyde functionality in macromonomers was confirmed by H-1 NMR spectroscopy. The reactivity of aldehyde functionality was demonstrated by carrying out aldehyde-aminooxy click reaction of polycaprolactone macromonomer with O-(2-azidoethyl) hydroxylamine which proceeded in a quantitative manner without backbone degradation. (C) 2012 Elsevier Ltd. All rights reserved.

10aAldehyde-terminated macromonomers10aATRP10aPolycaprolactone10aPolystyrene10aROP1 aSane, Prakash, S.1 aTawade, Bhausaheb, V.1 aPalaskar, Dnyaneshwar, V.1 aMenon, Shamal, K.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/aromatic-aldehyde-functionalized-polycaprolactone-and-polystyrene-macromonomers-synthesis-002210nas a2200265 4500008004100000022001400041245010700055210006900162260000900231300000700240490000700247520130000254653002401554653002401578653001501602653002201617100002501639700002801664700002401692700002601716700002901742700002301771700002801794856012201822 2017 eng d a1022-976000aAromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups: synthesis and characterization0 aAromatic polyesters containing pendent 4phenylsulfonylphenyl gro cMAR  a570 v243 a

A new bisphenol, 1,1-bis-[(4-hydroxyphenyl)-1-(4-phenylsulfonyl) phenyl)] ethane (DPSBP) was synthesized starting from diphenylsulfide and was characterized by spectroscopic methods. DPSBP was polycondensed with isophthalic acid chloride (IPC), terephthalic acid chloride (TPC) and a mixture of IPC and TPC (50: 50 mol%) by phase-transfer catalysed interfacial polymerization method to obtain aromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups. A series of copolyesters was also obtained by polycondensation of varying molar proportions of DPSBP and bisphenol-A (BPA) with TPC. (Co) polyesters exhibited inherent viscosities in the range 0.56-1.57 dLg(-1) and number average molecular weights (Mn) were in the range 28,650-80,230 g/mol. Polyesters dissolved readily in common organic solvents such as dichloromethane, chloroform, tetrahydrofuran and aprotic polar solvents such as N-methylpyrrolidone, and N, N-dimethylacetamide. Tough, transparent and flexible films of polyesters could be cast from their chloroform solutions. X-Ray diffraction studies indicated amorphous nature of aromatic polyesters. Polyesters showed T-g values in the range 223-257 degrees C while T-10 values were in the range of 469-484 degrees C indicating their excellent thermal stability.

10aAromatic polyesters10aBulky pendent group10asolubility10athermal stability1 aBapat, Snehalata, P.1 aJadhav, Sushilkumar, A.1 aValsange, Nitin, G.1 aTawade, Bhausaheb, V.1 aHonkhambe, Pandurang, N.1 aChavan, Nayaku, N.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/aromatic-polyesters-containing-pendent-4-phenylsulfonylphenyl-groups-synthesis-and02298nas a2200253 4500008004100000022001400041245012500055210006900180260000800249300000600257490000700263520141900270653002701689653001801716653002001734653002901754653001601783100002501799700002301824700002101847700002401868700002801892856012401920 2019 eng d a1022-976000aAromatic polycarbonates bearing pendant maleimide groups via functional monomer approach: synthesis and characterization0 aAromatic polycarbonates bearing pendant maleimide groups via fun cDEC a80 v273 a

A new bisphenol containing pendant maleimide group, viz., 4, 4'-(5-maleimidopentane-2, 2-diyl) diphenol (BPA-MA), was synthesized starting from commercially available 4, 4'-bis (4-hydroxyphenyl) pentanoic acid. Aromatic (co)polycarbonates possessing pendant maleimide groups were synthesized by solution polycondensation of BPA-MA or varying mixtures of BPA-MA and bisphenol-A (BPA) with triphosgene in dry dichloromethane in the presence of triethylamine as a base. Inherent viscosities and number average molecular weights of (co)polycarbonates were in the range 0.46-0.66 dL/g and 24,600-36,700, respectively, indicating the formation of reasonably high molecular weight polymers. Tough, transparent, and flexible films could be cast from chloroform solutions of these (co)polycarbonates. (Co)polycarbonates were characterized using FT-IR, H-1 NMR, C-13 NMR spectroscopy, XRD, TGA and DSC analysis. The chemical modification of a representative copolycarbonate containing pendant maleimide groups was carried out quantitatively using thiol-maleimide Michael addition reaction with two thiol compounds, namely, 4-chlorothiophenol and 1-adamantanethiol. Additionally, it was demonstrated that copolycarbonate containing pendant maleimide groups could be used to form insoluble cross-linked gel by reaction with a multifunctional thiol cross-linker, namely, pentaerythritol tetrakis(3-mercaptopropionate).

10aAromatic polycarbonate10aCross-linking10amaleimide group10aThiol-maleimide reaction10aTriphosgene1 aNagane, Samadhan, S.1 aKuhire, Sachin, S.1 aIchake, Amol, B.1 aRajamohanan, P., R.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/aromatic-polycarbonates-bearing-pendant-maleimide-groups-functional-monomer-approach02858nas a2200265 4500008004100000022001400041245013400055210006900189260000800258300001200266490000800278520193200286653002302218653002602241653002002267653002402287653002602311100002502337700001802362700000502380700002202385700003002407700002802437856012702465 2019 eng d a0014-305700aAromatic polyesters containing pendant azido groups: synthesis, characterization, chemical modification and thermal cross-linking0 aAromatic polyesters containing pendant azido groups synthesis ch cJUL a180-1890 v1163 a

A partially bio-based bisphenol containing pendant azido group viz., 4,4'-(5-azidopentane-2,2-diyl) diphenol (AZBPA) was synthesized starting from 4,4'-bis (4-hydroxyphenyl) pentanoic acid. AZBPA was reacted with isophthaloyl chloride (IPC), terephthaloyl chloride (TPC) and a mixture of IPC/TPC (50:50 mol%) by phase transfer-catalyzed interfacial polycondensation route to obtain aromatic polyesters containing pendant azido groups. Copolyesters containing pendant azido groups were also synthesized by polycondensation of different molar proportions of AZBPA and commercially available 4,4'-(1-phenylethane-1,1-diyl) diphenol (BPA-AP) with IPC. Inherent viscosities and number average molecular weights of (co)polyesters were in the range 0.85-1.64 dL/g and 58,900-190,400, respectively, indicating the formation of reasonably high molecular weight polymers. Tough, transparent, and flexible films could be cast from chloroform solutions of these polyesters. X-Ray diffraction analysis showed that (co)polyesters were amorphous in nature. (Co)polyesters were characterized using FT-IR, H-1 NMR spectroscopy, XRD, TGA and DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using copper-catalyzed azide-alkyne cycloaddition (CuAAC) with two alkynes viz., phenyl acetylene (PA) and ethynyl-4-nitrobenzene (ENB). Additionally, (co)polyesters containing pendant azido groups were thermally cross-linked (170 degrees C/12 h) leading to the formation of network structures based on azide to nitrene decomposition and subsequent reactions on polyester backbone. The selected cross-linked polyesters were characterized by stress-strain measurements. The cross-linked polymers exhibited higher tensile strength and Young's modulus and lower % elongation at break compared to corresponding pristine polyesters containing pendant azido groups.

10aAromatic polyester10aChemical modification10aClick chemistry10aPendant azido group10aThermal cross-linking1 aNagane, Samadhan, S.1 aVerma, Savita1 a1 aSane, Prakash, S.1 aDhanmane, Sushilkumar, A.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/aromatic-polyesters-containing-pendant-azido-groups-synthesis-characterization-chemical02012nas a2200253 4500008004100000022001400041245013600055210006900191260000900260300001200269490000700281520112100288653002301409653000601432653002401438653002001462653002301482653002401505100002601529700002501555700002801580700002701608856012301635 2024 eng d a1060-132500aAromatic (co)polycarbonates bearing pendant 2,3-dimethylmaleimido group based upon a new phthalimidine-containing "cardo" bisphenol0 aAromatic copolycarbonates bearing pendant 23dimethylmaleimido gr cOCT  a795-8040 v613 a

A new ``cardo'' bisphenol viz., 1-(2-(1,1-bis(4-hydroxyphenyl)-3-oxoisoindolin-2-yl)ethyl)-3,4-dimethyl- 1H-pyrrole-2,5-dione (PPH-MA) was synthesized in a two-step reaction sequence starting from phenolphthalein. PPH-MA was utilized as a step-growth monomer for the synthesis of a homo- and fourco-polycarbonates bearing pendant 2,3-dimethylmaleimido groups (PC-MAs) via solution polycondensation of PPH-MA or various mol % compositions of PPH-MA and bisphenol-A, respectively, with triphosgene.H-1 NMR spectroscopy confirmed the chemical structure and composition of PC-MAs. Inherent viscosity and number average molecular weight values of PC-MAs were in the range 0.45-0.64 dL g(-1) and 18,300 - 36,200 g mol(-1), respectively, indicating the formation of polymers of medium to reasonably high molecular weights. Tough, transparent and flexible films of PC-MAs could be cast from chloroform solution. X-ray diffraction studies indicated the amorphous nature of PC-MAs. The 10% weight loss temperature (T-10) values of PC-MAs were in the range 373-443 degrees C indicating their good thermal stability.

10a(co)polycarbonates10a210a3-dimethylmaleimido10aphenolphthalein10aphthalimidine ring10a``cardo'' bisphenol1 aTalanikar, Aniket, A.1 aNagane, Samadhan, S.1 aWadgaonkar, Prakash, P.1 aRashinkar, Gajanan, S. uhttps://library.ncl.res.in/content/aromatic-copolycarbonates-bearing-pendant-23-dimethylmaleimido-group-based-upon-new01973nas a2200217 4500008004100000022001400041245013300055210006900188260000800257520111800265653002301383653002301406653003701429653003301466653001901499100002601518700002501544700002801569700002701597856013101624 2024 eng d a0954-008300aAromatic (Co)polycarbonates bearing pendant norbornenyl groups: Synthesis, characterization and post-polymerization modification0 aAromatic Copolycarbonates bearing pendant norbornenyl groups Syn cAUG3 a

A homo- and three co-polycarbonates (PC-NBs) bearing pendant norbornenyl groups were synthesized via solution polycondensation of triphosgene with 4, 4'-(bicyclo (2.2.1) hept-5-en-2 yl methylene) bis (2-methoxyphenol) (BPA-NB) or various mol % compositions of BPA-NB and bisphenol-A, respectively. 1H-NMR spectroscopy confirmed the chemical structure and composition of PC-NBs. Inherent viscosity and number-average molecular weight (Mn) values of PC-NBs were in the range 0.44 - 0.64 dL g-1 and 21,800 - 34,100 g mol-1, respectively, indicating the formation of polymers of medium to reasonably high molecular weights. Tough, transparent, and flexible films of PC-NBs could be cast from chloroform solution. X-Ray diffraction studies indicated the amorphous nature of PC-NBs. Glass transition temperature (Tg) values, determined by DSC analysis, of PC-NBs were in the range 154 - 175 degrees C and Tg values increased with the increase in mol % of BPA-NB. The post-polymerization modification of a representative PC-NB was demonstrated using 3,6-diphenyl-1,2,4,5-tetrazine via tetrazine-ene reaction.

10a(co)polycarbonates10anorbornenyl groups10apost-polymerization modification10atetrazine-ene click reaction10athermoplastics1 aTalanikar, Aniket, A.1 aNagane, Samadhan, S.1 aWadgaonkar, Prakash, P.1 aRashinkar, Gajanan, S. uhttps://library.ncl.res.in/content/aromatic-copolycarbonates-bearing-pendant-norbornenyl-groups-synthesis-characterization-and