02992nas a2200241   4500008004100000022001400041245009100055210006900146260009900215300001200314490000700326520209300333653001302426653002802439653002202467653001902489653002202508653002202530100002102552700002402573700002802597856012502625       2010                        eng d  a0141-391000aPoly(amideimide)s containing pendant pentadecyl chains: synthesis and characterization0 aPolyamideimides containing pendant pentadecyl chains synthesis a  aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLANDbELSEVIER SCI LTDcMAY  a837-8440 v953 a<p>A new aromatic diacylhydrazide monomer viz., 4-[4'-(hydrazinocarbonyl)phenoxy]-2- pentadecylbenzo-hydrazide was synthesized starting from cardanol, which in turn is obtainable from cashew nut shell liquid a renewable resource material. A series of new poly(amideimide)s containing flexibilizing ether linkages and pendant pentadecyl chains was synthesized from 4-[4'-(hydrazinocarbonyl)phenoxy]-2-pentade-cylbenzohydrazide and commercially available aromatic dianhydrides, viz., benzene-1,2,4,5-tetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, benzophenone-3,3',4,4'-tetracarboxylic dianhydride, 4,4'-oxydiphthalic anhydride and 4,4'-(hexafluoro isopropylidene)diphthalic anhydride by a two-step solution polycondensation in N,N-dimethylacetamide via the poly(hydrazide acid) intermediate. Inherent viscosities of poly(amideimide)s were in the range 0.60-0.64 dL/g in N,N-dimethylacetamide at 30 +/- 0.1 degrees C. Poly(amideimide)s could be solution cast into tough, transparent and flexible films from their N,N-dimethylacetamide solutions. The solubility of poly(amideimide)s was significantly improved by incorporation of pendant pentadecyl chains and were found to be soluble in N,N-dimethylacetamide, 1-methyl-2-pyrrolidinone, pyridine and m-cresol at room temperature or upon heating. Wide angle X-ray diffraction patterns of poly(amideimide)s revealed a broad halo at around 2 theta = similar to 19 degrees suggesting that polymers were amorphous in nature. In the small-angle region, diffuse to sharp reflections of a typically layered structure resulting from the packing of pentadecyl side chains were observed. The temperature at 10% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of poly(amideimide)s was in the range of 388-410 degrees C indicating their good thermal stability. Glass transition temperatures of poly(amideimide)s were in the range 162-198 degrees C. It was observed that the plasticization effect of attached pentadecyl side chains induced the depression of T(g). (C) 2010 Elsevier Ltd. All rights reserved.</p>10aCardanol10aCashew nut shell liquid10aPentadecyl chains10aPlasticization10aPoly(amideimide)s10athermal stability1 aMore, Arvind, S.1 aPatil, Anandrao, S.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/polyamideimides-containing-pendant-pentadecyl-chains-synthesis-and-characterization-002596nas a2200229   4500008004100000022001400041245008600055210006900141260010600210300001200316490000700328520174000335653002102075653001302096653002802109653002202137653001502159100002102174700002302195700002802218856012002246       2010                        eng d  a0014-305700aSynthesis and characterization of polyamides containing pendant pentadecyl chains0 aSynthesis and characterization of polyamides containing pendant   aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLANDbPERGAMON-ELSEVIER SCIENCE LTDcMAR  a557-5670 v463 a<p>A new aromatic diacid monomer viz., 4-(4'-carboxyphenoxy)-2-pentadecylbenzoic acid was synthesized starting from cardanol and was characterized by FTIR, (1)H- and (13)C NMR spectroscopy. A series of new aromatic polyamides containing ether linkages and pendant pentadecyl chains was prepared by phosphorylation polycondensation of 4-(4'-carboxyphenoxy)-2-pentadecylbenzoic acid with five commercially available aromatic diamines viz., 1,4-phenylenediamine, 4,4'-oxydianiline, 4,4'-methylenedianiline, 1,3-phenylenediamine, and 4,4'-(hexafluoroisopropylidene)dianiline. Inherent viscosities of the polyamides were in the range 0.45-0.66 dL/g in N,N-dimethylacetamide at 30 +/- 0.1 degrees C. The introduction of ether linkages and pendant pentadecyl chains into polyamides led to an enhanced solubility in N,N-dimethylacetamide and 1-methyl-2-pyrrolidinone at room temperature or upon heating. The polyamides could be solution-cast into tough, flexible and transparent films from their N,N-dimethylacetamide solution. Wide angle X-ray diffraction patterns exhibited broad halo indicating that the polymers were essentially amorphous in nature. X-Ray diffractograms also displayed a diffuse to sharp reflection in the small-angle region (20 = similar to 2-5 degrees) for the polyamides characteristics of formation of loosely to well-developed layered structure arising from packing of flexible pentadecyl chains. The glass transition temperature observed for the polyamides was in range 139-189 degrees C. The temperature at 10% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of the polyamides was in the range 425-453 degrees C indicating their good thermal stability. (C) 2009 Elsevier Ltd. All rights reserved.</p>10aalkyl side-chain10aCardanol10aCashew nut shell liquid10aPentadecyl chains10apolyamides1 aMore, Arvind, S.1 aPasale, Sharad, K.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/synthesis-and-characterization-polyamides-containing-pendant-pentadecyl-chains-0