02605nas a2200205   4500008004100000022001400041245010700055210006900162260011000231300001600341490000600357520176600363100002402129700001802153700001602171700002602187700002702213700003002240856012902270       2015                        eng d  a2040-336400aM-Au/TiO2 (M = Ag, Pd, and Pt) nanophotocatalyst for overall solar water splitting: role of interfaces0 aMAuTiO2 M Ag Pd and Pt nanophotocatalyst for overall solar water  aTHOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLANDbROYAL SOC CHEMISTRYcJUL  a13477-134880 v73 a<p>M-Au/TiO2 (M = Ag, Pd, Pt) composites were prepared through a facile one-pot photodeposition synthesis and evaluated for solar water splitting (SWS) with and without a sacrificial agent. The M-Au combination exhibits a dominant role in augmenting the H2 generation activity by forming a bi-metallic system. Degussa P25 was used as a TiO2 substrate to photodeposit Au followed by Au + M (M = Ag/Pd/Pt). The SWS activity of the M-Au/TiO2 was determined through photocatalytic H-2 production in the presence of methanol as a sacrificial agent under one sun conditions with an AM1.5 filter. The highest H-2 yield was observed for Pt-0.5-Au-1/TiO2 and was around 1.3 +/- 0.07 mmol h(-1) g(-1), with an apparent quantum yield (AQY) of 6.4%. Pt-0.5-Au-1/TiO2 also demonstrated the same activity for 25 cycles of five hours each for 125 h. Critically, the same Pt-0.5-Au-1/TiO2 catalyst was active in overall SWS (OSWS) without any sacrificial agent, with an AQY = 0.8%. The amount of Au and/or Pt was varied to obtain the optimum composition and it was found that the Pt0.5-Au1/TiO2 composition exhibits the best activity. Detailed characterization by physico-chemical, spectral and microscopy measurements was carried out to obtain an in-depth understanding of the origin of the photocatalytic activity of Pt-0.5-Au-1/TiO2. These in-depth studies show that gold interacts predominantly with oxygen vacancies present on titania surfaces, and Pt preferentially interacts with gold for an effective electron-hole pair separation at Pt-Au interfaces and electron storage in metal particles. The Pt in Pt-0.5-Au-1/TiO2 is electronically and catalytically different from the Pt in Pt/TiO2 and it is predicted that the former suppresses the oxygen reduction reaction.</p>1 aMelvin, Ambrose, A.1 aIllath, Kavya1 aDas, Tanmay1 aRaja, Thirumalaiswamy1 aBhattacharyya, Somnath1 aGopinath, Chinnakonda, S.  uhttps://library.ncl.res.in/content/m-autio2-m-ag-pd-and-pt-nanophotocatalyst-overall-solar-water-splitting-role-interfaces-002170nas a2200205   4500008004100000022001400041245010200055210006900157260006700226300001200293490000600305520141000311100001901721700002001740700002101760700002401781700002001805700001801825856012101843       2016                        eng d  a2196-735000aMolecular-Pillar-supported functionalized reduced graphene-oxide for energy efficient lubrication0 aMolecularPillarsupported functionalized reduced grapheneoxide fo  a111 RIVER ST, HOBOKEN 07030-5774, NJ USAbWILEY-BLACKWELLcJUL  a16001610 v33 a<p>Molecular-pillar-supported basal plane of reduced graphene oxide (rGO) is fabricated by polymerizing polyaniline (PANI). In the presence of poly(ethylene glycol) (PEG200), the gamma-radiolysis is used for modifying the functionalization and improving the structural symmetry of PANI and PEG grafted rGO (PANI-PEG-g-rGO). The PANI is covalently and noncovalently grafted onto the surface of the graphene sheets. Carboxyl groups of rGO are linked to the nitrogen atoms in the PANI backbone and an accompanying noncovalent interaction between alkyl chains of grafted PANI and hydrooxylated rGO is formed. Raman and Fourier transform infra-red results confirm existence of stretching vibrations of benzenoid and quinonoid rings in PANI-PEG-g-rGO-functionalized composite, indicating grafting between PANI and rGO through pi-pi interaction. Furthermore, PEG-functionalization through hydrogen bonding with rGO is confirmed when hydroxyl group from the rGO combines with oxygen of PEG. X-ray photoelectron spectroscopy reveals significant increase in carbon, while loading PANI network with rGO followed by gamma-irradiation. Antifriction and antiwear properties of graphene nanocomposite are considerably enhanced to 68.4% and 48%, respectively, as compared to pristine PEG. The unique lubrication properties are explained by PEG functionalized molecular PANI-pillar structure across basal plane of rGO.</p>1 aGupta, Bhavana1 aKumar, Niranjan1 aPanda, Kalpataru1 aMelvin, Ambrose, A.1 aJoshi, Shailesh1 aDash, Sitaram  uhttps://library.ncl.res.in/content/molecular-pillar-supported-functionalized-reduced-graphene-oxide-energy-efficient