02713nas a2200265 4500008004100000022001400041245009700055210006900152260009900221300001400320490000700334520176400341653002802105653000902133653001502142653002002157653001402177653001502191653001502206100002102221700002202242700002402264700002802288856013102316 2010 eng d a0141-391000aSynthesis and characterization of aromatic polyazomethines bearing pendant pentadecyl chains0 aSynthesis and characterization of aromatic polyazomethines beari aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLANDbELSEVIER SCI LTDcSEP a1727-17350 v953 a

Aromatic diamine monomer viz., 4-(4'-aminophenoxy)-2-pentadecylbenzenamine containing pendant pentadecyl chain was synthesized starting from cashew nut shell liquid - a renewable resource material and was characterized by FTIR, (1)H and (13)C NMR spectroscopy. A series of new (co) polyazomethines containing pendant pentadecyl chains and flexibilizing ether linkages was synthesized by polycondensation of 4-(4'-aminophenoxy)-2-pentadecyl benzenamine with commercially available aromatic dialdehydes viz., terephthaldehyde (TPA), isophthaldehyde (IPA) and varying mixture of TPA and IPA. Inherent viscosities and number average molecular weights of (co) polyazomethines were in the range 0.50-0.70 dL/g and 10,490-40-800 (GPC, polystyrene standard), respectively indicating formation of medium to reasonably high molecular weight polymers. (Co) polyazomethines containing pendant pentadecyl chains were found to be soluble in common organic solvents such as chloroform, dichloromethane, tetrahydrofuran, pyridine, m-cresol and could be cast into transparent and stretchable films from their solution in chloroform. (Co) polyazomethines were essentially amorphous in nature and the formation of loosely-developed layered structure was observed arising from the packing of pendant pentadecyl chains. Polyazomethines exhibited glass transition temperatures (T(g)) in the range 21-48 degrees C. The observed depression of glass transition temperature could be ascribed to the ``internal plasticization'' effect of pentadecyl chains. The temperature at 10% wt loss (T(10)), determined from TGA in nitrogen atmosphere of polyazomethines were in the range 434-441 degrees C indicating their good thermal stability. (C) 2010 Elsevier Ltd. All rights reserved.

10aCashew nut shell liquid10aCNSL10apentadecyl10apolyazomethines10arenewable10aSide-chain10asolubility1 aMore, Arvind, S.1 aSane, Prakash, S.1 aPatil, Anandrao, S.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/synthesis-and-characterization-aromatic-polyazomethines-bearing-pendant-pentadecyl-chains-002813nas a2200241 4500008004100000022001400041245011400055210006900169260009800238300001400336490000700350520192500357653002702282653000902309653001502318653001502333653001402348100002102362700002202383700002402405700002802429856011402457 2010 eng d a0959-810300aSynthesis and characterization of polyesters based on 1,1,1-[bis(4-hydroxyphenyl)-4 `-pentadecylphenyl]ethane0 aSynthesis and characterization of polyesters based on 111bis4hyd aTHE ATRIUM, SOUTHERN GATE, CHICHESTER PO19 8SQ, W SUSSEX, ENGLANDbJOHN WILEY & SONS LTDcOCT a1408-14140 v593 a

Aromatic polyesters are of considerable interest because of their excellent mechanical properties, chemical resistance and thermal stability. However, most aromatic polyesters are difficult to process due to their high glass transition temperatures coupled with their insolubility in common organic solvents. The present article describes a series of organosoluble polyesters and copolyesters based on 1,1,1-[bis(4-hydroxyphenyl)-4'-pentadecylphenyl]ethane. A series of new aromatic polyesters containing pendant pentadecyl chains was synthesized by interfacial polycondensation of 1,1,1-[bis(4-hydroxyphenyl)-4'-pentadecylphenyl]ethane with terephthalic acid chloride (TPC), isophthalic acid chloride (IPC) and a mixture of TPC and IPC. A series of copolyesters was synthesized from 4,4'-isopropylidenediphenol with TPC by incorporating 1,1,1-[bis(4-hydroxyphenyl)-4'-pentadecylphenyl]ethane as a comonomer. Inherent viscosities of the polyesters and copolyesters were in the range 0.72-1.65 dL g(-1) and number-average molecular weights were in the range 18 170-87 220. The polyesters and copolyesters containing pendant pentadecyl chains dissolved readily in organic solvents such as chloroform, dichloromethane, pyridine and m-cresol and could be cast into transparent, flexible and apparently tough films. Wide-angle X-ray diffraction data revealed the amorphous nature of the polyesters and copolyesters. The formation of loosely developed layered structure was observed due to the packing of pendant pentadecyl chains. The temperature at 10% weight loss, determined using thermogravimetric analysis in nitrogen atmosphere, of the polyesters and copolyesters containing pendant pentadecyl chains was in the range 400-460 degrees C. The polyesters and copolyesters exhibited glass transition temperatures in the range 63-82 degrees C and 177-183 degrees C, respectively. (C) 2010 Society of Chemical Industry

10acashew nutshell liquid10aCNSL10apentadecyl10apolyesters10arenewable1 aMore, Arvind, S.1 aNaik, Parimal, V.1 aKumbhar, Kishor, P.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/synthesis-and-characterization-polyesters-based-111-bis4-hydroxyphenyl-4-002867nas a2200277 4500008004100000022001400041245015300055210006900208260006700277300001400344490000800358520184000366653002102206653002802227653000902255653001502264653002502279653002402304653001502328653001402343100002102357700002302378700002902401700002802430856013102458 2011 eng d a0021-899500aSynthesis and characterization of organo-soluble poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing pendant pentadecyl chains0 aSynthesis and characterization of organosoluble polyether ether  a111 RIVER ST, HOBOKEN 07030-5774, NJ USAbWILEY-BLACKWELLcSEP a3689-36950 v1213 a

Poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant pentadecyl chains were synthesized by polycondensation of each of the two bisphenol monomers viz, 1,1,1-[bis(4-hydroxyphenyl)-4'-pentadecylphenyl] ethane and 1,1-bis(4-hydroxyphenyl)-3-pentadecyl cyclohexane with activated aromatic dihalides namely, 4,4'-difluorobenzophenone, and 1,3-bis(4-fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene, in the presence of anhydrous potassium carbonate. Polymers were isolated as white fibrous materials with inherent viscosities and number average molecular weights in the range 0.70-1.27 dL g(-1) and 76,620-1,36,720, respectively. Poly(ether ether ketone) s and poly(ether ether ketone ketone) s were found to be soluble at room temperature in organic solvents such as chloroform, dichloromethane, tetrahydrofuran, and pyridine and could be cast into tough, transparent, and flexible films from their solutions in chloroform. Wide angle X-ray diffraction patterns exhibited a broad halo at around 2 theta = similar to 19 degrees indicating that the polymers containing pentadecyl chains were amorphous in nature. In the small-angle region, diffuse reflections of a typically layered structures resulting from the packing of pentadecyl side chains were observed. The temperature at 10% weight loss, obtained from TG curves, for poly(ether ether ketone) s and poly(ether ether ketone ketone) s were in the range 416-459 degrees C, indicating their good thermal stability. A substantial drop in glass transition temperatures (68-78 degrees C) was observed for poly(ether ether ketone) s and poly(ether ether ketone ketone) s due to ``internal plasticization'' effect of flexible pendant pentadecyl chains. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 121: 3689-3695, 2011

10aalkyl side-chain10aCashew nut shell liquid10aCNSL10apentadecyl10apoly(arylene ether)s10apoly(ether ketone)s10apolyethers10arenewable1 aMore, Arvind, S.1 aPasale, Sharad, K.1 aHonkhambe, Pandurang, N.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/synthesis-and-characterization-organo-soluble-polyether-ether-ketones-and-polyether-ether-002810nas a2200253 4500008004100000022001400041245009500055210006900150260007600219300001400295490000800309520192100317653000602238653001902244653002802263653001502291653001102306653001902317653002202336100002102358700002202379700002802401856012702429 2012 eng d a0021-899500aNew poly(1,3,4-oxadiazole)s bearing pentadecyl side chains: synthesis and characterization0 aNew poly134oxadiazoles bearing pentadecyl side chains synthesis  aCOMMERCE PLACE, 350 MAIN ST, MALDEN 02148, MA USAbWILEY-BLACKWELLcAPR a1281-12890 v1243 a

The 4-[4'-(Hydrazinocarbonyl)phenoxy]-2-pentadecylbenzohydrazide was polycondensed with aromatic diacid chlorides viz., terephthalic acid chloride (TPC), isophthalic acid chloride (IPC), and a mixture of TPC : IPC (50 : 50 mol %) to obtain polyhydrazides which on subsequent cyclodehydration reaction in the presence of phosphoryl chloride yielded new poly(1,3,4-oxadiazole)s bearing flexibilizing ether linkages and pentadecyl side chains. Inherent viscosities of polyhydrazides and poly(1,3,4-oxadiazole)s were in the range 0.530.66 dL g(-1) and 0.490.53 dL g(-1), respectively, indicating formation of medium to reasonably high molecular weight polymers. The number average molecular weights (M-n) and polydispersities (M-w/M-n) of poly(1,3,4-oxadiazole)s were in the range 14,660-21,370 and 2.22.5, respectively. Polyhydrazides and poly(1,3,4-oxadiazole)s were soluble in polar aprotic solvents such as N,N-dimethylacetamide, 1-methyl-2-pyrrolidinone, and N,N-dimethylformamide. Furthermore, poly(1,3,4-oxadiazole)s were also found to be soluble in solvents such as chloroform, dichloromethane, tetrahydrofuran, pyridine, and m-cresol. Transparent, flexible, and tough films of polyhydrazides and poly(1,3,4-oxadiazole)s could be cast from N,N-dimethylacetamide and chloroform solutions, respectively. Both polyhydrazides and poly(1,3,4-oxadiazole)s were amorphous in nature and formation of layered structure was observed due to packing of pentadecyl chains. A decrease in glass transition temperature was observed both in polyhydrazides (143-166 degrees C) and poly(1,3,4-oxadiazole)s (90-102 degrees C) which could be ascribed to internal plasticization effect of pentadecyl chains. The T-10 values, obtained from TG curves, for poly(1,3,4-oxadiazole)s were in the range of 433-449 degrees C indicating their good thermal stability. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 124:1281-1289, 2012

10a310a4-oxadiazole)s10aCashew nut shell liquid10apentadecyl10apoly(110apolyhydrazides10athermal stability1 aMore, Arvind, S.1 aMenon, Shamal, K.1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/new-poly134-oxadiazoles-bearing-pentadecyl-side-chains-synthesis-and-characterization-0