02168nas a2200241 4500008004100000022001400041245014700055210006900202260007700271300001400348490000700362520124400369653002101613653001501634653001301649653002001662653001601682100002501698700002801723700002501751700002401776856012601800 2013 eng d a2192-650600aRedox-mediated synthesis of functionalised graphene: a strategy towards 2D multifunctional electrocatalysts for energy conversion applications0 aRedoxmediated synthesis of functionalised graphene a strategy to aBOSCHSTRASSE 12, D-69469 WEINHEIM, GERMANYbWILEY-V C H VERLAG GMBHcOCT a1296-13030 v783 a

A simple, one-step synthetic route for developing a two-dimensional multifunctional electrocatalyst is reported, by the functionalisation of graphene using oxidised ethylenedioxythiophene (O-EDOT). The mutually assisted redox reaction between graphene oxide (GO) and EDOT facilitates the reduction of GO to graphene with a concomitant deposition of O-EDOT on the surface of the graphene. The oxidised surface of GO catalyses the reaction without using an added reducing agent, so a controlled and uniform deposition of O-EDOT is ensured on the surface of graphene, which essentially prevents the restacking of the layers. UV/Visible, IR, Raman and X-ray photoelectron spectroscopy give valid evidence for the reduction and functionalisation of graphene sheets. The functional groups present on the surface of graphene are found to tune the physical and chemical properties of graphene. Consequently, the functionalised material displays enhanced electrocatalytic activity for the reduction of oxygen to water and I3- to I- relative to pristine graphene. These distinct property characteristics make the material a versatile cathode electrocatalyst for both alkaline anion-exchange membrane fuel cells and dye-sensitised solar cells.

10aelectrocatalysts10afuel cells10agraphene10aredox chemistry10asolar cells1 aUnni, SreeKuttan, M.1 aBhange, Siddheshwar, N.1 aAnothumakkool, Bihag1 aKurungot, Sreekumar uhttps://library.ncl.res.in/content/redox-mediated-synthesis-functionalised-graphene-strategy-towards-2d-multifunctional-001863nas a2200253 4500008004100000022001400041245010900055210006900164260007700233300001400310490000700324520092400331653002501255653001501280653002901295653002101324653002201345100002501367700002501392700002001417700002401437700002101461856012701482 2014 eng d a1433-785100aTwo-in-one: inherent anhydrous and water-assisted high proton conduction in a 3D metal-organic framework0 aTwoinone inherent anhydrous and waterassisted high proton conduc aBOSCHSTRASSE 12, D-69469 WEINHEIM, GERMANYbWILEY-V C H VERLAG GMBHcMAR a2638-26420 v533 a

The development of solid-state proton-conducting materials with high conductivity that operate under both anhydrous and humidified conditions is currently of great interest in fuel-cell technology. A 3Dmetal-organic framework (MOF) with acid-base pairs in its coordination space that efficiently conducts protons under both anhydrous and humid conditions has now been developed. The anhydrous proton conductivity for this MOF is among the highest values that have been reported for MOF materials, whereas its water-assisted proton conductivity is comparable to that of the organic polymer Nafion, which is currently used for practical applications. Unlike other MOFs, which conduct protons either under anhydrous or humid conditions, this compound should represent a considerable advance in the development of efficient solid-state proton-conducting materials that work under both anhydrous and humid conditions.

10aconducting materials10afuel cells10ametal-organic frameworks10aporous materials10aproton conduction1 aNagarkar, Sanjog, S.1 aUnni, SreeKuttan, M.1 aSharma, Amitosh1 aKurungot, Sreekumar1 aGhosh, Sujit, K. uhttps://library.ncl.res.in/content/two-one-inherent-anhydrous-and-water-assisted-high-proton-conduction-3d-metal-organic-001962nas a2200241 4500008004100000022001400041245013300055210006900188260007500257300001400332490000600346520103800352653002101390653001801411653001501429653003001444653001301474100002501487700002901512700002401541700002601565856012901591 2015 eng d a2196-021600aCoSe2 supported on nitrogen-doped carbon nanohorns as a methanol-tolerant cathode for air-breathing microlaminar flow fuel cells0 aCoSe2 supported on nitrogendoped carbon nanohorns as a methanolt aPOSTFACH 101161, 69451 WEINHEIM, GERMANYbWILEY-V C H VERLAG GMBHcSEP a1339-13450 v23 a

The synthesis of CoSe2 nanoparticles supported on nitrogendoped carbon nanohorns (CoSe2/NCNH) and the influence of the interaction of the metal centre with the NCNH on the oxygen reduction reaction (ORR) are reported. CoSe2/NCNH shows a 50 mV lower onset overpotential and a 150 mV positive shift in the half-wave potential compared to CoSe2 supported on carbon and carbon nanohorns. This suggests that the intrinsic activity and the density of active reaction centres of CoSe2 are modified by NCNHs. An air-breathing direct meth-anol microlaminar flow fuel cell (mLFFC) is constructed using CoSe2/NCNH as a methanol-tolerant cathode catalyst. A maximum power density of 10.05 mWcm(-2) and a maximum current density of 124.20 mAcm(-2) are achieved with CoSe2/NCNH compared to the non-doped catalyst, CoSe2/C and Pt/C with 5m methanol as the fuel. The improved activity of CoSe2/ NCNH is attributed to the peculiar morphology and the nitrogen doping of the carbon nanohorns. This catalyst could be a suitable alternative to Pt.

10acarbon nanohorns10achalcogenides10afuel cells10aoxygen reduction reaction10aplatinum1 aUnni, SreeKuttan, M.1 aMora-Hernandez, Juan, M.1 aKurungot, Sreekumar1 aAlonso-Vante, Nicolas uhttps://library.ncl.res.in/content/cose2-supported-nitrogen-doped-carbon-nanohorns-methanol-tolerant-cathode-air-breathing-0