02340nas a2200265   4500008004100000022001400041245011700055210006900172260000800241300001100249490000800260520142700268653002501695653001801720653002201738100001701760700001701777700002001794700002001814700002301834700003701857700002101894700002701915856013201942       2025                        eng d  a0141-813000aExtraction of highly crystalline and thermally stable cellulose nanofiber from Heliconia psittacorum L.f. leaves0 aExtraction of highly crystalline and thermally stable cellulose   cMAY  a1422640 v3083 a<p>
	Extracting cellulose nanofibers (CNF) from agro-waste is one of the promising and practical ways to develop sustainable nanocomposites. In this study, cellulose nanofibers were extracted from the leaves of Heliconia psittacorum for the first time. The combination of oxalic acid hydrolysis (5 wt%) and steam explosion was used for the isolation of CNF from the leaves of Heliconia psittacorum. The structural and chemical features of the prepared CNF were analyzed using various techniques, including Fourier Transform Infrared Spectroscopy (FTIR), Solid state 13C Nuclear Magnetic Resonance Spectroscopy (13C NMR), Scanning Electron Microscopy (SEM), Energy Dispersive X ray analysis (EDX), Transmission electron Microscopy (TEM), X-Ray Diffraction (XRD) and Thermogravimetric analysis (TGA). TEM micrographs reported 15 to 40 nm diameter for the nanofibers synthesized. XRD analysis reported 91 % crystallinity index for CNF, whereas that of the untreated sample was 76 %. The maximum degradation of the CNF is reported at 355 degrees C, exceeds the untreated sample (316 degrees C). The tensile strength of the CNF derived paper was found to be 23 MPa. The recovered nanocellulose can be further utilized for various applications such as the automobile industry for developing lightweight parts, biosensors, super capacitors, absorption of greenhouse gases, wastewater treatment, and packaging applications.</p>
10abiomass valorization10aNanocellulose10aWaste to resource1 aPaul, Sharon1 aJoseph, Anto1 aHridhya, P., D.1 aBadawi, Michael1 aAjithkumar, T., G.1 aParameswaranpillai, Jyotishkumar1 aAsrofi, Mochamad1 aDominic, C., D. Midhun  uhttps://library.ncl.res.in/content/extraction-highly-crystalline-and-thermally-stable-cellulose-nanofiber-heliconia-psittacorum