02167nas a2200265   4500008004100000022001400041245009100055210006900146260000900215300001200224490000800236520130800244653001501552653001901567653001301586653002701599653001501626100002401641700002001665700002801685700002201713700002101735700002601756856011901782       2024                        eng d  a1226-086X00aPerformance of Li exchange hierarchical X zeolite for CO2 adsorption and H2 separation0 aPerformance of Li exchange hierarchical X zeolite for CO2 adsorp  cMAY   a505-5140 v1333 a<p>
	Li exchange hierarchical X zeolite (Li-H-X) was prepared by decationization of X zeolite by NH4Cl solution followed by Li exchange and subsequent calcination. NH4-X and Li-X were prepared to compare the results of LiH-X. XRD, FE-SEM, EDS, N2 adsorption-desorption, and micro-/mesoporous volume were performed. The higher mesoporosity was confirmed in Li-H-X due to the framework dealumination during decationization. Static and dynamic sorption capacity of sorbents was evaluated to identify the performance of sorbent. The CO2 and H2 equilibrium adsorption capacity of Li-H-X was found to be 9.6 mmol g-1 and 0.78 mmol g-1, respectively, at 298 K and 20 bar, which was 25 % (CO2) and 30 % (H2) higher than Li-X. Static experimental data were validated using the Langmuir, Freundlich, and Sips models. The CO2 &amp; H2 dynamic sorption capacity of Li-H-X sorbent for binary gas (CO2/H2, 25/75 %) was 4.145 mmol g-1 and 0.258 mmol g-1 at 303 K and 10 bar. The higher sorption capacity of Li-H-X was obtained due to large micro-/mesoporous volume of sorbent, which may allow to access unoccupied sites at higher pressure. This result reveals that micro-/mesoporous structure of zeolite adsorbs significantly higher CO2 from binary gas stream, which can use to separate pure H2 from gas stream.</p>
10aAdsorption10aCarbon dioxide10aHydrogen10aMicroporous-mesoporous10aSeparation1 aShrotri, Aadesh, R.1 aBirje, Amit, R.1 aNiphadkar, Prashant, S.1 aBokade, Vijay, V.1 aMali, Nilesh, A.1 aNandanwar, Sachin, U.  uhttps://library.ncl.res.in/content/performance-li-exchange-hierarchical-x-zeolite-co2-adsorption-and-h2-separation02358nas a2200313   4500008004100000022001400041245014700055210006900202260000900271300001200280490000800292520132300300653001501623653001101638653001601649653001201665653000801677653001501685100002201700700002401722700002301746700002001769700002801789700002101817700002601838700002201864700002601886856013201912       2025                        eng d  a1226-086X00aBinderless low silica X zeolite for methane separation from binary CO2/CH4 biogas stream: A comprehensive experimental and computational study0 aBinderless low silica X zeolite for methane separation from bina  cSEP   a705-7190 v1493 a<p>
	This study presents the synthesis of binderless Na-LSX (B-Na-LSX) and binderless NaK-LSX (B-NaK-LSX). XRD, SEM, EDS, and N-2 physisorption were used for characterization of samples. Computational modelling of prepared sorbent was performed for the fundamental understanding of zeolite topology and adsorption behaviour. The breakthrough experiments are used to evaluate the adsorption capacities on CO2/CH4 (40/60 vol%) binary biogas stream. The results were compared with commercial Na-LSX (C-Na-LSX). The breakthrough adsorption capacity of B-Na-LSX was 3.08 mmol g(-1) and 0.29 mmol g(-1) of CO2 and CH4, respectively, at 300 K and 1 bar. CO2 sorption capacity of B-Na-LSX was similar to 11 % and similar to 17 % higher than B-NaK-LSX (2.77 mmol g(-1)) and C-Na-LSX (2.56 mmol g(-1)), respectively. DFT study reveals that the higher adsorption of CO2 over CH4 was attributed to higher charge transfer from CO2 to zeolite framework. Dual-bed six-step Pressure Swing Adsorption (PSA) was performed on B-Na-LSX at 6 bar. similar to 232 cycles were run with above 98 % of CH4 purity and similar to 74 % of recovery. The life-cycle test of sorbent was studied. It was implied that the designed sorbent is effective to produce the high purity of CH4 and can be utilized for a longer period for CH4 production.</p>
10aBinderless10aBiogas10aLSX zeolite10amethane10aPSA10aSeparation1 aYadav, Tushar, R.1 aShrotri, Aadesh, R.1 aKate, Pranjali, N.1 aDevasia, George1 aNiphadkar, Prashant, S.1 aMali, Nilesh, A.1 aKrishnamurty, Sailaja1 aBokade, Vijay, V.1 aNandanwar, Sachin, U.  uhttps://library.ncl.res.in/content/binderless-low-silica-x-zeolite-methane-separation-binary-co2ch4-biogas-stream-comprehensive