02436nas a2200241   4500008004100000022001400041245015800055210006900213260000900282300001400291490000800305520154300313100002801856700002301884700002701907700001901934700001801953700002201971700002201993700003202015700002002047856012702067       2020                        eng d  a0002-786300aConnecting microscopic structures, mesoscale assemblies, and macroscopic architectures in 3D-printed hierarchical porous covalent organic framework foams0 aConnecting microscopic structures mesoscale assemblies and macro  cMAY   a8252-82610 v1423 a<p>The induction of macro and mesopores into two-dimensional porous covalent organic frameworks (COFs) could enhance the exposure of the intrinsic micropores toward the pollutant environment, thereby, improving the performance. However, the challenge is to build a continuous hierarchically porous macro-architecture of crystalline organic materials in the bulk scale. In this regard, we have strategized a novel synthetic method to create hierarchically porous COF foams consisting of ordered micropores (2-2.2 nm) and disordered meso and macropores (50 nm to 200 mu m) as well as ordered macropores (1.5 mm to 2 cm). Herein, graphene oxide was used for creating disordered macro and mesopores in COF-GO foams. Considering the rheological features of the precursor hydrogel, we could integrate crystalline and porous COF-GO foams into self-supported three-dimensional (3D)-printed objects with the desired shapes and sizes. Therefore, we have engineered the 3D macro-architecture of COF-GO foams into complex geometries keeping their structural order and continuous porosity intact over a range of more than a million (10(-9) m to 10(-3) m). The interconnected 3D openings in these COF-GO foams further enhance the rapid and efficient uptake of organic and inorganic pollutants from water (&gt;95% removal within 30 s). The abundant distribution of interconnected macroporous volume (55%) throughout the COF-GO foam matrix enhances the flow of water (1.13 x 10(-3) m.s(-1)) which results in efficient mass transport and adsorption.</p>
1 aMohammed, Abdul, Khayum1 aUsgaonkar, Saurabh1 aKanheerampockil, Fayis1 aKarak, Suvendu1 aHalder, Arjun1 aTharkar, Minakshi1 aAddicoat, Matthew1 aAjithkumar, Thalasseril, G.1 aBanerjee, Rahul  uhttps://library.ncl.res.in/content/connecting-microscopic-structures-mesoscale-assemblies-and-macroscopic-architectures-3d01942nas a2200229   4500008004100000245009800041210006900139260000900208300001200217490000700229520115200236100002501388700002201413700002201435700002401457700002201481700002201503700002301525700002401548700002401572856011601596       2022                        eng d00aThe effects of cis and trans butenedioic acid on the physicochemical behavior of lumefantrine0 aeffects of cis and trans butenedioic acid on the physicochemical  cJAN   a156-1680 v243 aThe present work investigates the effects of cis and trans butenedioic acid isomers (maleic acid and fumaric acid) on the crystallinity and pharmaceutical behavior of lumefantrine. Differential scanning calorimetry (DSC), powder X-ray diffraction (PXRD), attenuated total reflectance infrared spectroscopy (ATR-IR), solid-state nuclear magnetic resonance spectroscopy (ss-NMR), and single-crystal X-ray diffraction (SC-XRD) studies were employed. Lumefantrine-fumaric acid crystallized as a salt in the monoclinic space group P2(1)/c. In comparison, DSC and PXRD showed the formation of a co-amorphous solid with maleic acid. Complete proton transfer with a strong ionic interaction led to crystalline salt formation with the trans isomer, whereas weaker/fewer hydrogen bonds with the cis isomer of butenedioic acid led to a co-amorphous salt. The in vitro dissolution of both salts resulted in a similar 2.6-2.7-fold improvement in dissolution rate when compared to that of the crystalline lumefantrine. The crystalline and co-amorphous salts were stable under accelerated stability conditions (40 +/- 2 degrees C and 75 +/- 5% RH) for one month.1 aTomar, Devendrasingh1 aLodagekar, Anurag1 aGunnam, Anilkumar1 aAllu, Suryanarayana1 aChavan, Rahul, B.1 aTharkar, Minakshi1 aAjithkumar, T., G.1 aNangia, Ashwini, K.1 aShastri, Nalini, R.  uhttps://library.ncl.res.in/content/effects-cis-and-trans-butenedioic-acid-physicochemical-behavior-lumefantrine