02461nas a2200253   4500008004100000022001400041245017300055210006900228260000900297300001600306490000600322520151900328653002801847653001801875653001401893653001901907653002501926100002101951700002701972700002301999700002502022700003002047856013002077       2021                        eng d  a2574-096200aAqueous methanol to formaldehyde and hydrogen on Pd/TiO2 by photocatalysis in direct sunlight: structure dependent activity of nano-Pd and atomic Pt-coated counterparts0 aAqueous methanol to formaldehyde and hydrogen on PdTiO2 by photo  cNOV   a13347-133600 v43 aIn the present investigation, facet-controlled Pd nanoparticles with nanocube (Pd-NC) and truncated octahedron (Pd-TO) morphologies, and their counterparts with half-a-monolayer of atomic Pt coated (0.5 theta(Pt)-Pd-NC and 0.5 theta(Pt)-Pd-TO) surfaces were prepared. All of them were characterized and evaluated as cocatalyst after supporting them on commercial titania (P25) (Pd-NC/P25, Pd-TO/P25, 0.5 theta(Pt)-Pd-NC/P25, and 0.5 theta(Pt)-Pd-TO/P25) under direct sunlight and/or one sun conditions for the oxidation of methanol to formaldehyde along with solar hydrogen production. Pd-NC/P25 shows higher activity for hydrogen generation compared to Pd-TO/P25; however, activity reversal occurs with the above cocatalysts, but, after Pt-coating with further enhanced activity. The highest conversion of methanol (0.2 mu mol/h.mg) to 100% selective formaldehyde was observed with 0.5 theta(Pt)-Pd-TO/P25, while other catalysts show significantly lower methanol conversion in the following order: 0.5 theta(Pt)-Pd-TO/P25 > 0.5 theta(Pt)-Pd-NC/P25 > Pd-NC/P25 > Pd-TO/P25. Pt-coated on (111) facets of Pd-TO simulates the activity associated as that of Pt(111) facets and demonstrating the highest and facet dependent activity. The present study is truly in resonance with exploiting the surface properties for heterogeneous catalysis, and highlights that less than a monolayer of Pt is sufficient to simulate the activity as that of bulk Pt. It is worth exploring this concept to other metals and substrates too.10aheterogeneous catalysis10aNanomaterials10aOxidation10aPhotocatalysis10asurface modification1 aNalajala, Naresh1 aSalgaonkar, Kranti, N.1 aChauhan, Inderjeet1 aMekala, Siva, Prasad1 aGopinath, Chinnakonda, S.  uhttps://library.ncl.res.in/content/aqueous-methanol-formaldehyde-and-hydrogen-pdtio2-photocatalysis-direct-sunlight-structure01936nas a2200265   4500008004100000022001400041245013300055210006900188260000800257300001200265490000700277520102200284653002801306653002001334653001901354653001101373653002801384653001901412100002101431700002301452700002101475700001901496700003001515856012501545       2021                        eng d  a2194-428800aElectronically integrated mesoporous Ag-TiO2 nanocomposite thin films for efficient solar hydrogen production in direct sunlight0 aElectronically integrated mesoporous AgTiO2 nanocomposite thin f  cAUG  a21003560 v103 a<p>
	The synthesis of mesoporous TiO2 by a solution-based assembly process and Ag/TiO2 nanocomposites is provided. The efficacy of Ag/TiO2 nanocomposite as photocatalyst in thin-film form is demonstrated for solar hydrogen generation in sunlight. Integration of Ag with TiO2 dramatically enhanced the H-2 production: with 1 wt% Ag on TiO2 (TiAg-1), the H-2 yield was observed to be 4.59 mmol h(-1) g(-1), which is 2.3 (30) times larger than 0.5 wt% Ag on TiO2. TiAg-1 shows 4.3 times higher activity in film form compared with its powder counterpart. High photocatalytic efficiency is attributed to the surface plasmon resonance effect of Ag, electronic integration of Ag with TiO2, and subsequent valence band broadening, large distribution of Ag nanoparticles and abundant Ag-TiO2 Schottky junctions, and the later minimizes electron-hole recombination. Interparticle mesoporous network increases necking and the high surface area offers easy accessibility of the reactants to a large number of active sites.</p>
10aheterogeneous catalysis10aheterojunctions10aplasmon effect10aSilver10asolar energy conversion10aSolar hydrogen1 aMani, Sunesh, S.1 aRajendran, Sivaraj1 aNalajala, Naresh1 aMathew, Thomas1 aGopinath, Chinnakonda, S.  uhttps://library.ncl.res.in/content/electronically-integrated-mesoporous-ag-tio2-nanocomposite-thin-films-efficient-solar