02858nas a2200265   4500008004100000022001400041245013400055210006900189260000800258300001200266490000800278520193200286653002302218653002602241653002002267653002402287653002602311100002502337700001802362700000502380700002202385700003002407700002802437856012702465       2019                        eng d  a0014-305700aAromatic polyesters containing pendant azido groups: synthesis, characterization, chemical modification and thermal cross-linking0 aAromatic polyesters containing pendant azido groups synthesis ch  cJUL  a180-1890 v1163 a<p>A partially bio-based bisphenol containing pendant azido group viz., 4,4'-(5-azidopentane-2,2-diyl) diphenol (AZBPA) was synthesized starting from 4,4'-bis (4-hydroxyphenyl) pentanoic acid. AZBPA was reacted with isophthaloyl chloride (IPC), terephthaloyl chloride (TPC) and a mixture of IPC/TPC (50:50 mol%) by phase transfer-catalyzed interfacial polycondensation route to obtain aromatic polyesters containing pendant azido groups. Copolyesters containing pendant azido groups were also synthesized by polycondensation of different molar proportions of AZBPA and commercially available 4,4'-(1-phenylethane-1,1-diyl) diphenol (BPA-AP) with IPC. Inherent viscosities and number average molecular weights of (co)polyesters were in the range 0.85-1.64 dL/g and 58,900-190,400, respectively, indicating the formation of reasonably high molecular weight polymers. Tough, transparent, and flexible films could be cast from chloroform solutions of these polyesters. X-Ray diffraction analysis showed that (co)polyesters were amorphous in nature. (Co)polyesters were characterized using FT-IR, H-1 NMR spectroscopy, XRD, TGA and DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using copper-catalyzed azide-alkyne cycloaddition (CuAAC) with two alkynes viz., phenyl acetylene (PA) and ethynyl-4-nitrobenzene (ENB). Additionally, (co)polyesters containing pendant azido groups were thermally cross-linked (170 degrees C/12 h) leading to the formation of network structures based on azide to nitrene decomposition and subsequent reactions on polyester backbone. The selected cross-linked polyesters were characterized by stress-strain measurements. The cross-linked polymers exhibited higher tensile strength and Young's modulus and lower % elongation at break compared to corresponding pristine polyesters containing pendant azido groups.</p>
10aAromatic polyester10aChemical modification10aClick chemistry10aPendant azido group10aThermal cross-linking1 aNagane, Samadhan, S.1 aVerma, Savita1 a1 aSane, Prakash, S.1 aDhanmane, Sushilkumar, A.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/aromatic-polyesters-containing-pendant-azido-groups-synthesis-characterization-chemical02437nas a2200253   4500008004100000022001400041245009100055210006900146260000900215300001200224490000700236520160100243653001701844653002001861653001701881653001501898653002001913100002501933700002301958700002101981700003002002700002802032856012302060       2019                        eng d  a0887-624X00aDesign and synthesis of aromatic polyesters bearing pendant clickable maleimide groups0 aDesign and synthesis of aromatic polyesters bearing pendant clic  cMAR   a630-6400 v573 a<p>A bisphenol bearing pendant maleimide group, namely, N-maleimidoethyl-3, 3-bis(4-hydroxyphenyl)-1-isobenzopyrrolidone (PPH-MA) was synthesized starting from phenolphthalein. Aromatic (co)polyesters bearing pendant maleimide groups were synthesized from PPH-MA and aromatic diacid chlorides, namely, isophthaloyl chloride (IPC), terephthaloyl chloride (TPC), and 50:50 mol % mixture of IPC and TPC by low temperature solution polycondensation technique. Copolyesters were also synthesized by polycondensation of different molar proportions of PPH-MA and bisphenol A with IPC. Inherent viscosities and number-average molecular weights of aromatic (co)polyesters were in the range of 0.52-0.97 dL/g and 20,200-32,800 g/mol, respectively indicating formation of medium to reasonably high-molecular-weight polymers. C-13 NMR spectral analysis of copolyesters revealed the formation of random copolymers. The 10% weight loss temperature of (co)polyesters was found in the range 470-484 degrees C, indicating their good thermal stability. A selected aromatic polyester bearing pendant maleimide groups was chemically modified via thiol-maleimide Michael addition reaction with two representative thiol compounds, namely, 4-chlorothiophenol and 1-adamantanethiol to yield post-modified polymers in a quantitative manner. Additionally, it was demonstrated that polyester containing pendant maleimide groups could be used to form insoluble crosslinked gel in the presence of a multifunctional thiol crosslinker. (c) 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 630-640</p>10acrosslinking10amaleimide group10amodification10apolyesters10athiol-maleimide1 aNagane, Samadhan, S.1 aKuhire, Sachin, S.1 aJadhav, Uday, A.1 aDhanmane, Sushilkumar, A.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/design-and-synthesis-aromatic-polyesters-bearing-pendant-clickable-maleimide-groups