02465nas a2200253   4500008004100000022001400041245010100055210006900156260000900225300001400234490000700248520158800255653002701843653001601870653002001886653002601906100002201932700002501954700002101979700002502000700002602025700002802051856013202079       2019                        eng d  a0887-624X00aNew cardo bisphenol monomer containing pendant azido group and the resulting aromatic polyesters0 aNew cardo bisphenol monomer containing pendant azido group and t  cJUL   a1516-15260 v573 a<p>Expanding on our strategy to synthesize aromatic step-growth polymers containing pendant clickable azido groups via functional monomer approach, we have now designed and synthesized a new cardo bisphenol, viz., 2-(2-azidoethyl)-3, 3-bis(4-hydroxyphenyl) isoindolin-1-one (PPH-N-3). PPH-N-3 was conveniently synthesized starting from commercially available phenolphthalein by a three-step route in an overall yield of 65% using simple organic transformations. Aromatic (co)polyesters bearing pendant azido groups were synthesized by low-temperature solution polycondensation of PPH-N-3 or different molar ratios of PPH-N-3 and bisphenol-A (BPA) with aromatic diacid chlorides in dry dichloromethane in the presence of triethylamine (TEA) as a base. The formation of medium to reasonably high-molecular-weight (co)polyesters was evidenced from intrinsic viscosity and number-average molecular-weight measurements that were in the range 0.52-0.85 dL/g and 16,700-28,200, respectively. Tough, transparent, and flexible films could be cast from chloroform solutions of these (co)polyesters. (Co)polyesters were characterized using FTIR, H-1 NMR, C-13 NMR spectroscopy, XRD, and TGA. The thermal curing reaction of (co)polyesters involving decomposition of azido groups was studied by DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using catalyst-free azide-maleimide cycloaddition reaction with two maleimides, namely, N-methylmaleimide and N-hexylmaleimide. (c) 2019 Wiley Periodicals, Inc.</p>
10aaromatic (co)polyester10aazido group10acardo bisphenol10aChemical modification1 aMaher, Deepak, M.1 aNagane, Samadhan, S.1 aJadhav, Uday, A.1 aSalunkhe, Pravin, H.1 aTawade, Bhausaheb, V.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/new-cardo-bisphenol-monomer-containing-pendant-azido-group-and-resulting-aromatic-polyesters02543nas a2200253   4500008004100000022001400041245012700055210006900182260000800251300001200259490000700271520162900278653002701907653002601934653002401960653002501984653002902009100002502038700002202063700001802085700002602103700002802129856013202157       2022                        eng d  a1060-132500aPendant propargyloxy-functionalized aromatic (co)polycarbonates: synthesis, thermal crosslinking and chemical modification0 aPendant propargyloxyfunctionalized aromatic copolycarbonates syn  cNOV  a752-7630 v593 a<p>
	A bisphenol monomer bearing pendant propargyloxy group viz, 1, 1-bis (4-hydoxyphenyl)-1-(4 `-propargyloxyphenyl) ethane (BPP) was synthesized starting from commercially available 1, 1, 1-tris (4-hydroxyphenyl) ethane (THPE) by mono O-propargylation reaction using propargyl bromide. A new series of pendant propargyloxy-functionalized aromatic (co)polycarbonates was synthesized by low-temperature solution polycondensation of BPP or different molar ratios of BPP and bisphenol-A with triphosgene in dichloromethane in the presence of triethylamine. The formation of reasonably high molecular weight (co)polycarbonates was confirmed by inherent viscosity (0.52-0.83 dL/g) and gel permeation chromatography (M-n 37,000-69,800 g/mol, polystyrene standards) measurements. C-13 NMR spectral studies supported formation of random copolycarbonates in copolymerization of BPP and BPA with triphosgene. The 10% weight loss temperature (T-10) values of (co)polycarbonates, determined by thermogravimetric analysis under nitrogen atmosphere, were in the range 427-438 degrees C indicating their good thermal stability. The glass transition temperature (T-g) values of (co)polycarbonates were observed in the range 147-152 degrees C. The crosslinking ability of (co)polycarbonates involving pendant propargyloxy groups leading to formation of networked structure was evaluated via non-isothermal curing studies by DSC. As a proof-of-concept, the post-modification of a representative polycarbonate bearing pendant propargyloxy groups with 1-octane thiol as a model compound via thiol-yne click reaction was briefly studied.</p>
10aAromatic polycarbonate10aChemical modification10apropargyloxy groups10athermal crosslinking10athiol-yne click reaction1 aNagane, Samadhan, S.1 aMaher, Deepak, M.1 aVerma, Savita1 aTalanikar, Aniket, A.1 aWadgaonkar, Prakash, P.  uhttps://library.ncl.res.in/content/pendant-propargyloxy-functionalized-aromatic-copolycarbonates-synthesis-thermal-crosslinking