01963nas a2200241   4500008004100000022001400041245012400055210006900179260000800248300001200256490000700268520114900275653002301424653001101447653001701458653001601475653003001491100001901521700001901540700002101559700001901580856012201599       2022                        eng d  a2194-428800aThiocyanate- and thiol-functionalized p-doped quantum dot colloids for the development of bulk homojunction solar cells0 aThiocyanate and thiolfunctionalized pdoped quantum dot colloids   cSEP  a22004550 v103 a<p>
	Progress in device engineering and surface passivation strategies has led to steady progress in colloidal quantum dot (QD) solar cells. Bulk homojunction (BHJ) device architecture has several advantages over the conventional planar junction in developing QD solar cells. Herein, surface ligand chemistry is utilized to control the doping type and dispersibility of oppositely doped PbS QDs to develop BHJ solar cells. Thiocyanate and thiol ligand combination is introduced to develop p-PbS QD ink, which is blended with halide-passivated n-PbS QDs to build BHJ solar cells. It is shown that BHJ solar cells are benefited from high energy offset and higher hole mobility. This leads to the superior carrier extraction from a thicker active layer without compromising fill factor and open circuit voltage. Power conversion efficiency has reached 10.7% in 530 nm-thick BHJ solar cells, a 24% improvement over the best performing planar solar cells. With the help of the 1D solar cell capacitance simulator, it is shown that a 15% efficient QD solar cell can be realized by further improving the hole mobility above 0.1 cm(2) V-1 s(-1).</p>
10abulk homojunctions10aDoping10aquantum dots10asolar cells10asurface functionalization1 aDambhare, Neha1 aSharma, Ashish1 aMahajan, Chandan1 aRath, Arup, K.  uhttps://library.ncl.res.in/content/thiocyanate-and-thiol-functionalized-p-doped-quantum-dot-colloids-development-bulk