02098nas a2200205 4500008004100000022001400041245011100055210006900166260007100235300001600306490000800322520129100330100002801621700001801649700002101667700002501688700002501713700002901738856012501767 2013 eng d a1932-744700aSpin transport and magnetic correlation parameters for graphene-like nanocarbon sheets doped with nitrogen0 aSpin transport and magnetic correlation parameters for graphenel a1155 16TH ST, NW, WASHINGTON, DC 20036 USAbAMER CHEMICAL SOCcDEC a27105-271130 v1173 a

Globally, graphene magnetism has captivated the attention of researchers in recent years. To obtain magnetic ordering, irregularities in the carbon network, like defects, adatoms, etc., are essential. Herein, we report on spin transport and magnetic correlations in graphene-like nanocarbon sheets (GNCs) that were doped with nitrogen by use of tetrakis(dimethylamino)ethylene (TDAE). The spin transport measurements, performed by electron spin resonance technique, showed that both spin-spin and spin-lattice relaxation times are increased by nitrogen doping. The magnetic correlations, measured on a vibrating sample magnetometer, showed that ordering parameters are reduced for nitrogen-loaded GNCs. Chemical analysis, carried out via electron spectroscopy, revealed that nitrogen atoms exchange couples electron-to-hole with the carbon network Analysis of I-V measurements showed that higher-order resistance is appreciably decreased for nitrogen-doped GNCs. The observed decrease is due to an increase in nonbonding states baying small local density. After doping, states in this region may be localized pi spin populated around the doped region. By and large, the approximately 20% magnetization that exists in GNCs is found to be reduced to 5% by introduction of nitrogen.

1 aAlegaonkar, Ashwini, P.1 aKumar, Arvind1 aPatil, Sagar, H.1 aPatil, Kashinath, R.1 aPardeshi, Satish, K.1 aAlegaonkar, Prashant, S. uhttps://library.ncl.res.in/content/spin-transport-and-magnetic-correlation-parameters-graphene-nanocarbon-sheets-doped-001890nas a2200181 4500008004100000022001400041245010100055210006900156260005700225300001400282490000700296520118100303100002201484700002101506700002601527700002501553856013001578 2014 eng d a0022-246100aFacile room temperature synthesis of ZnO nanoflower thin films grown at a solid-liquid interface0 aFacile room temperature synthesis of ZnO nanoflower thin films g a233 SPRING ST, NEW YORK, NY 10013 USAbSPRINGERcSEP a5945-59540 v493 a

Hierarchical ZnO films consisting of nanoflower particulates are successfully grown by a solid-liquid interface reaction technique at room temperature without additives like surfactants, capping agent, or complexing agent. The structural, morphological, and photocatalytic properties of these films are studied using scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and UV-Vis spectroscopy. The nucleation, growth processes and hence the resulting morphology of the end product can be regulated by changing the concentration of LiOH and the time of reaction. SEM throws light on the chronology of the flower formation by studying the intermediate morphology. Electron microscopy results indicated that these ZnO nanostructures self-assembled to produce flower-like nanostructures. The highest photocatalytic efficiency was observed for the films prepared at the concentration of LiOH 0.5 mg/mL in ethanol at 24 h. On the basis of the results, a plausible growth mechanism for the formation of flower-like ZnO nanostructures is discussed.

1 aJadhav, Aarti, H.1 aPatil, Sagar, H.1 aSathaye, Shivaram, D.1 aPatil, Kashinath, R. uhttps://library.ncl.res.in/content/facile-room-temperature-synthesis-zno-nanoflower-thin-films-grown-solid-liquid-interface-002446nas a2200325 4500008004100000022001400041245015900055210006900214260005700283300001400340490000800354520126400362653003101626653002801657653001301685653001501698653001601713653001801729653002701747653001501774100002801789700002101817700002701838700002401865700002401889700002601913700002601939700002501965856013001990 2014 eng d a0303-402X00aStudies on morphology of polyaniline films formed at liquid-liquid and solid-liquid interfaces at 25 and 5 A degrees C, respectively, and effect of doping0 aStudies on morphology of polyaniline films formed at liquidliqui a233 SPRING ST, NEW YORK, NY 10013 USAbSPRINGERcMAY a1079-10890 v2923 a

It is well accepted that the morphology of the nanomaterials has great effect on the properties and hence their applications. Therefore, morphology of materials has become a focus of research in the scientific world. The present study shows that interfacial polymerization and subsequent self-assembly provides a control over the morphology, nanorod/nanosheet, of polyaniline (PANI) films synthesized by liquid-liquid interface reaction technique and solid-liquid interface reaction technique. The synthesized PANI films and its particulate structure are characterized by using various spectroscopic techniques such as UV-visible, ATR-IR, Raman and XPS. The study confirmed the formation, the structure, the size and shape of particles and morphology of PANI by using analytical techniques namely, SAED, SEM and TEM. An important observation is that doping with HCl significantly improves the nanorod formation at the interface. The doped PANI electrode exhibits a higher area with rectangular shape in CV cycle and better cycle stability when compared with the performance of undoped PANI films. We believe that the results of these studies can give valuable leads to manoeuvre formation of PANI films with desired morphology for various applications.

10ainterfacial polymerization10aLiquid-liquid interface10aNanorods10ananosheets10apolyaniline10aSelf-assembly10aSolid-liquid interface10aThin films1 aWaghmode, Babasaheb, J.1 aPatil, Sagar, H.1 aJahagirdar, Mandar, M.1 aPatil, Virendra, S.1 aWaichal, Rupali, P.1 aMalkhede, Dipalee, D.1 aSathaye, Shivaram, D.1 aPatil, Kashinath, R. uhttps://library.ncl.res.in/content/studies-morphology-polyaniline-films-formed-liquid-liquid-and-solid-liquid-interfaces-25-001930nas a2200253 4500008004100000022001400041245011800055210006900173260009500242300001200337490000800349520100900357653000801366653002001374653001401394653002301408653001401431653000801445100002201453700002101475700002601496700002501522856012901547 2015 eng d a0021-979700aMethod to form semiconductor quantum dot (QD) thin films by igniting a flame at air-liquid interface: CdS and WO30 aMethod to form semiconductor quantum dot QD thin films by igniti a525 B ST, STE 1900, SAN DIEGO, CA 92101-4495 USAbACADEMIC PRESS INC ELSEVIER SCIENCEcFEB a121-1280 v4393 a

We reveal an easy, inexpensive, efficient one step flame synthesis of semiconductor/metal oxide thin films at air-liquid interface, subsequently, transferred on suitable substrate. The method has been illustrated by the formation of CdS and Wo(3) QDs thin films. The features of the present method are (1) Growth of thin films consisting of 0.5-2.0 nm sized Quantum Dots (QDs)/(ultra-small nanoparticles) in a short time, at the air-liquid interface which can be suitably transferred by a well-known Blodgett technique to an appropriate substrate, (2) The method is suitable to apply layer by layer (LbL) technique to increase the film thickness as well as forming various compositions as revealed by AFM measurements. The films are characterized for their structure (SAED), morphology (TEM), optical properties (UV-Vis.) and photoluminescence (PL). Possible mechanism of formation of QDs thin film and effect of capping in case of COS QDs is discussed. (C) 2014 Elsevier Inc. All rights reserved.

10aCdS10aFlame synthesis10ainterface10aQuantum Dots (QDs)10athin film10aWO31 aJadhav, Aarti, H.1 aPatil, Sagar, H.1 aSathaye, Shivaram, D.1 aPatil, Kashinath, R. uhttps://library.ncl.res.in/content/method-form-semiconductor-quantum-dot-qd-thin-films-igniting-flame-air-liquid-interface-001848nas a2200289 4500008004100000022001400041245013100055210006900186260007700255300001400332490000700346520079400353653002301147653001301170653001401183653002401197653002201221100001401243700002101257700002301278700002401301700002601325700002501351700002101376700002901397856013201426 2015 eng d a2192-650600aReduced graphene oxide composite with oxidizable manganese/cobalt mixed oxide for p-cresol oxidation by using molecular oxygen0 aReduced graphene oxide composite with oxidizable manganesecobalt aBOSCHSTRASSE 12, D-69469 WEINHEIM, GERMANYbWILEY-V C H VERLAG GMBHcJUL a1164-11690 v803 a

A composite of graphene oxide (GO) with mixed oxide (MnCo) was prepared by using a solvothermal method. During the synthesis, both the reduction of GO and growth of metal oxides took place simultaneously. The as-prepared composite material was highly selective for the liquid-phase oxidation of p-cresol to form p-hydroxybenzaldehyde in 71% yield within 1h. The composite material was characterised by SEM, X-ray photoelectron spectroscopy, high-resolution TEM and cyclic voltammetry (CV). A CV study revealed that the increase in the redox potential of the mixed oxide after being supported on GO, led to its higher activity of the catalyst for the oxidation reaction. The stability of the catalyst under the reaction conditions was studied by its successful reuse in three cycles.

10acyclic voltammetry10agraphene10aOxidation10asupported catalysts10atransition metals1 aJha, Ajay1 aPatil, Sagar, H.1 aSolanki, Bhanu, P.1 aRibeiro, Ana, P. C.1 aCastro, Carlos, A. N.1 aPatil, Kashinath, R.1 aCoronas, Alberto1 aRode, Chandrashekhar, V. uhttps://library.ncl.res.in/content/reduced-graphene-oxide-composite-oxidizable-manganesecobalt-mixed-oxide-p-cresol-oxidation-002144nas a2200205 4500008004100000245012100041210006900162260000800231300002500239490000600264520140300270100001901673700001801692700002201710700001801732700001801750700002101768700001801789856013101807 2018 eng d00aNew insights towards strikingly improved room temperature ethanol sensing properties of p-type Ce-doped SnO2 sensors0 aNew insights towards strikingly improved room temperature ethano cMAY aArticle Number: 80790 v83 aIn this article, room temperature ethanol sensing behavior of p-type Ce doped SnO2 nanostructures are investigated successfully. Interestingly, it is examined that the abnormal n to p-type transition behavior is caused by Ce doping in SnO2 lattice. In p-type Ce doped SnO2, Ce ion substituting the Sn is in favor of generating excess holes as oxygen vacancies, which is associated with the improved sensing performance. Although, p-type SnO2 is one of the important materials for practical applications, it is less studied as compared to n-type SnO2. Pure and Ce doped SnO2 nanostructures were successfully synthesized by chemical co-precipitation method. The structure, surface morphology, unpaired electrons (such as free radicals), and chemical composition of obtained nanoparticleswere studied by various kinds of characterization techniques. The 9% Ce doped SnO2 sensors exhibit maximum sensor response of similar to 382 for 400 ppm of ethanol exposure with fast response time of similar to 5 to 25 sec respectively. Moreover, it is quite interesting that such enhancement of ethanol sensing is unveiled at room temperature, which plays a key role in the quest for better ethanol sensors. These remarkably improved sensing results are attributed to uniformly distributed nanoparticles, lattice strain, complex defect chemistry and presence of large number of unpaired electrons on the surface.1 aKumar, Manjeet1 aBhatt, Vishwa1 aAbhyankar, A., C.1 aKim, Joondong1 aKumar, Akshay1 aPatil, Sagar, H.1 aYun, Ju-Hyung uhttps://library.ncl.res.in/content/new-insights-towards-strikingly-improved-room-temperature-ethanol-sensing-properties-p-type03124nas a2200241 4500008004100000022001400041245017300055210006900228260000900297300001200306490000800318520223900326653000802565653003002573653002002603653001602623653002002639100002102659700002302680700002602703700002502729856012802754 2018 eng d a0013-468600aTo form layer by layer composite film in view of its application as supercapacitor electrode by exploiting the techniques of thin films formation just around the corner0 aTo form layer by layer composite film in view of its application cMAR  a556-5680 v2653 aA method is described to form robust composite supercapacitor electrodes consisting of polyaniline (PANI)-graphene (GNS) and PANI-MoS2 nanosheets wherein composites are formed by Layer by Layer (LbL) deposition. PANI layer consisting of 10-15 nm particle size was formed by LLIRT, while GNS and MoS2 layers were formed by modified LLIRT. A special feature of the development is the architecture which is rarely found in the literature wherein singular components are stacked over each other to form a composite. The architecture is found to show strong synergistic effects suitable for high performance supercapacitor applications. The composites were characterized by using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM) etc. The characterization indicates the formation of composites having uniform distribution of PANI nanoparticles over the 2D nanosheets of GNS and MoS2 respectively. The electrochemical performance of the composites was evaluated by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and Galvanostatic Charge Discharge (GCD). The composite layer consisting of PANI-GNS alternate layers, showed an excellent specific capacitance (C-sp) of 549 Fg(-1) while PANI-MoS2 alternate layers and PANI layers showed C-sp to be (413 F g(-1)) and (185 F g(-1)) respectively. It is proposed that C-sp stability of the composites is greatly enhanced by the architecture of composite formation through LbL deposition approach. PANI-GNS showed high stability (95% retention of C-sp), PANI-MoS2 (94% retention of C-sp) as against single component capacitance of PANI (67% retention of C-sp). The results reveal the importance of the architecture of composite formation. The architecture of depositing alternate layers of components to form a composite would have special properties leading to synergistic effect in the applications. The present communication is a proof of this concept. It shows the boost in the charge storage resulting in stable robust supercapacitors formation. We predict similar advantages in other applications such as solar energy conversion, sensors, catalysis, etc. (C) 2018 Elsevier Ltd. All rights reserved.10aGNS10aLayer-by-Layer deposition10aMoS2 nanosheets10apolyaniline10aSupercapacitors1 aPatil, Sagar, H.1 aGaikwad, Aarti, P.1 aSathaye, Shivaram, D.1 aPatil, Kashinath, R. uhttps://library.ncl.res.in/content/form-layer-layer-composite-film-view-its-application-supercapacitor-electrode-exploiting02155nas a2200193 4500008004100000022001400041245014300055210006900198260000800267300001400275490000700289520141100296100002101707700002301728700002801751700002601779700002501805856013101830 2020 eng d a1144-054600aGraphene-MnO2 composite supercapacitor material accomplished tactically using liquid-liquid and solid-liquid interface reaction techniques0 aGrapheneMnO2 composite supercapacitor material accomplished tact cMAY a6853-68610 v443 a

A novel methodology is described to grow architectures of 3-dimensional graphene nanosheet (GNS)-manganese oxide (MnO2) composite materials to be used in supercapacitors. The in situ growth of the three-dimensional MnO2 fiber-network over the surface of graphene layers is achieved at the solid-liquid interface. The composite electrode shows good electron and charge transfer, rapid plus reversible faradaic reactions and excellent cyclic ability in electrochemical studies. The electrochemical properties of the as-prepared GNS-MnO2/FTO electrode material were assessed by cyclic voltammetry and galvanostatic charge/discharge tests. The specific capacitance of GNS-MnO2 reaches 683 F g(-1) at a current density of 2.2 A g(-1) and shows excellent cycle stability, retaining 96.9% of its initial capacitance up to 5000 cycles. A coulomb efficiency of about 99% displayed by the GNS-MnO2/FTO electrode is an excellent performance for a desired supercapacitor material. Herein, the charge storage mechanism in 3-dimensional graphene nanosheet (GNS)-manganese oxide (MnO2) composite is discussed in detail. Furthermore, at an elevated current density of similar to 10.86 A g(-1), a power density of similar to 6.235 kW kg(-1) is achieved, maintaining an energy density of similar to 7.99 kW h kg(-1); thus, it demonstrates promising potential as an electrode material for supercapacitor application.

1 aPatil, Sagar, H.1 aGaikwad, Aarti, P.1 aWaghmode, Babasaheb, J.1 aSathaye, Shivaram, D.1 aPatil, Kashinath, R. uhttps://library.ncl.res.in/content/graphene-mno2-composite-supercapacitor-material-accomplished-tactically-using-liquid-liquid