01616nas a2200205   4500008004100000245005400041210005400095260000800149300002700157490000800184520096300192100002301155700002401178700002401202700002301226700002101249700003001270700002401300856008601324       2015                        eng d00aGraphene nanoribbons as prospective field emitter0 aGraphene nanoribbons as prospective field emitter  cJAN  aArticle Number: 0231110 v1063 a<p>Field emission characteristics of graphene nanoribbons (GNRs) synthesized by unzipping of multiwall carbon nanotubes using a facile hydrothermal route have been investigated at a base pressure of 1 x 10(-8) mbar. The values of turn-on field, required to draw an emission current densities of 1 and 10 mu A/cm(2), are found to be 2.8 and 5.8 V/mu m, respectively, and a maximum emission current density of 500 mu A/cm(2) has been drawn at an applied field of 9.8 V/mu m. The emission current stability of the GNRs emitter was studied at preset values of 1 and 10 mu A over a period of 3 h, and is found to be excellent. The field emission results demonstrated herein suggest that GNRs based field emitters can open up many opportunities for their potential utilization as large area field emitters in various vacuum micro-nanoelectronic devices such as flexible field emission displays, portable X-ray, and microwave tubes. (C) 2015 AIP Publishing LLC.</p>1 aKhare, Ruchita, T.1 aShinde, Dhanraj, B.1 aBansode, Sanjeewani1 aMore, Mahendra, A.1 aMajumder, Mainak1 aPillai, Vijayamohanan, K.1 aLate, Dattatray, J.  uhttps://library.ncl.res.in/content/graphene-nanoribbons-prospective-field-emitter02150nas a2200205   4500008004100000020002200041245013100063210006900194260023600263520118000499653001901679653000901698653001601707653001001723100002201733700002401755700001901779700001701798856012901815       2016                        eng d  a978-1-5090-2419-300aField emission investigation of composites of polypyrrole with graphene oxide, reduced graphene oxide and graphene nanoribbons0 aField emission investigation of composites of polypyrrole with g  a345 E 47th St, New York,NY 10017 USAbIEEE; IEEE Electron Devices Soc; ZEISS; Modern Electron; Amer Vacuum Soci; Paul Scherrer Inst; Elect & Comp Engn; Univ British Columbia, Peter Wall Inst Adv Studies; Dept Elect & Comp EngncJUL3 a<p>The monomer pyrrole has been polymerized by chemical route in the presence of graphene oxide (GO), reduced graphene oxide (rGO) and graphene nanoribbons (GNR) separately to prepare nanocomposites as Polypyrrole-GO (PGO), PPy-rGO (PRGO), PPy-GNR (PGNR), respectively. The morphological, chemical and structural characterization of the as-synthesized products was carried out using scanning electron microscopy (SEM), Raman and fourier transform infrared (FTIR) spectroscopy. Field emission (FE) studies of PGO, PRGO, PGNR emitters were performed at the base pressure of 1x10(-8) mbar in planar `diode' configuration. Onset and threshold field values corresponding to emission current densities of 1 and 100 mu A/cm(2) are observed to be 1.5 and 2.3V/mu m for PGO, 1.4 and 2.2 V/mu m for PRGO and lowest for PGNR as 0.9 and 1.2V/mu m, respectively. The maximum emission current density of 2.5 mA/cm(2) drawn for PGO at the applied electric field of 3.2V/mu m, 1.2 mA/cm(2) at 3.6V/mu m from the PRGO and 8 mA/cm(2) at the field of 2.2 V/mu m from the PGNR emitters. An emission current versus time (I-t) plot shows stable emission behavior for the preset current values.</p>10afield emission10aFTIR10apolypyrrole10aRaman1 aHarpale, Kashmira1 aBansode, Sanjeewani1 aMore, Mahendra1 aLate, D., J.  uhttps://library.ncl.res.in/content/field-emission-investigation-composites-polypyrrole-graphene-oxide-reduced-graphene-oxide