02281nas a2200241   4500008004100000022001400041245010600055210006900161260000800230300001600238490000600254520145900260653002301719653001901742653002201761653002201783653002201805653001901827100002701846700001701873700002701890856012201917       2024                        eng d  a2637-610500aBiobased reusable nonisocyanate polyurethane hot-melt adhesives with potential chemical degradability0 aBiobased reusable nonisocyanate polyurethane hotmelt adhesives w  cSEP  a11180-111920 v63 a<p>
	Hot-melt adhesives (HMAs) derived from renewable resources are always attractive, as they promote less dependence on fossil resources and aid in developing environmentally friendly materials. However, developing sustainable HMAs exhibiting good adhesive performance and biodegradability remains challenging. Herein, reusable biobased HMAs with a high bio content of 88-90%, biodegradability, and tunable adhesive nature were developed as a possible alternative to conventional petroleum-based hot-melt adhesives. Moreover, the structure-property relationship of the product was investigated in detail. By tailoring the monomer composition, NIPU-40 HMA exhibited a good bonding ability with a superior adhesion strength of 6.39 MPa. To the best of our knowledge, this is the highest adhesion strength observed when bonding with an Al substrate among the biobased thermoplastic NIPU-HMAs. Impressively, NIPU-HMAs could display excellent reusability even after three bonding and debonding cycles without a significant drop in the adhesive strength and were found to exhibit good adhesion performance under wet conditions. More importantly, the NIPU-HMAs are prone to degradation under acid-catalyzed conditions. Considering their features, these biobased NIPU thermoplastic hot-melt adhesives offer an opportunity to create environmentally friendly, degradable adhesives that possess excellent adhesive strength and can be reused multiple times.</p>
10aacid degradability10abiobased NIPUs10acyclic carbonates10ahot meltadhesives10alap shearstrength10aspiro-aromatic1 aGhuge, Gorakh, Hiraman1 aTorris, Arun1 aNair, Kiran, Sukumaran  uhttps://library.ncl.res.in/content/biobased-reusable-nonisocyanate-polyurethane-hot-melt-adhesives-potential-chemical