02012nas a2200253   4500008004100000022001400041245013600055210006900191260000900260300001200269490000700281520112100288653002301409653000601432653002401438653002001462653002301482653002401505100002601529700002501555700002801580700002701608856012301635       2024                        eng d  a1060-132500aAromatic (co)polycarbonates bearing pendant 2,3-dimethylmaleimido group based upon a new phthalimidine-containing "cardo" bisphenol0 aAromatic copolycarbonates bearing pendant 23dimethylmaleimido gr  cOCT   a795-8040 v613 a<p>
	A new ``cardo'' bisphenol viz., 1-(2-(1,1-bis(4-hydroxyphenyl)-3-oxoisoindolin-2-yl)ethyl)-3,4-dimethyl- 1H-pyrrole-2,5-dione (PPH-MA) was synthesized in a two-step reaction sequence starting from phenolphthalein. PPH-MA was utilized as a step-growth monomer for the synthesis of a homo- and fourco-polycarbonates bearing pendant 2,3-dimethylmaleimido groups (PC-MAs) via solution polycondensation of PPH-MA or various mol % compositions of PPH-MA and bisphenol-A, respectively, with triphosgene.H-1 NMR spectroscopy confirmed the chemical structure and composition of PC-MAs. Inherent viscosity and number average molecular weight values of PC-MAs were in the range 0.45-0.64 dL g(-1) and 18,300 - 36,200 g mol(-1), respectively, indicating the formation of polymers of medium to reasonably high molecular weights. Tough, transparent and flexible films of PC-MAs could be cast from chloroform solution. X-ray diffraction studies indicated the amorphous nature of PC-MAs. The 10% weight loss temperature (T-10) values of PC-MAs were in the range 373-443 degrees C indicating their good thermal stability.</p>
10a(co)polycarbonates10a210a3-dimethylmaleimido10aphenolphthalein10aphthalimidine ring10a``cardo'' bisphenol1 aTalanikar, Aniket, A.1 aNagane, Samadhan, S.1 aWadgaonkar, Prakash, P.1 aRashinkar, Gajanan, S.  uhttps://library.ncl.res.in/content/aromatic-copolycarbonates-bearing-pendant-23-dimethylmaleimido-group-based-upon-new