02028nas a2200181   4500008004100000022001400041245009800055210006900153260000800222300001400230490000700244520137000251100002401621700002801645700002201673700002601695856012501721       2023                        eng d  a0021-956800aEquilibrium adsorption of nitrogen, oxygen, and argon on silver-exchanged hierarchical ETS-100 aEquilibrium adsorption of nitrogen oxygen and argon on silverexc  cJUL  a2159-21720 v683 a<p>
	Silver-exchanged hierarchical ETS-10(Ag-H-ETS-10) was synthesizedusing Ag+ exchange with hierarchical Engelhard titanosilicate(H-ETS-10) using silver nitrate solution. The physical propertiesof the adsorbent were analyzed using X-ray diffraction (XRD), BETsurface area, nitrogen adsorption-desorption, pore volume,energy dispersive spectroscopy (EDS), and high resolution-transmissionelectron microscopy (HR-TEM). N-2 physisorption data confirmedthat a micro-mesoporous (bimodal) structure was created in the Ag-H-ETS-10.The equilibrium adsorbent data of pure gases N-2, O-2, and Ar were investigated in the temperature range from 288to 318 K up to 10 bar. The equilibrium adsorption capacity of Ag-H-ETS-10was found to be 1.12 mmol g(-1) for N-2,0.87 mmol g(-1) for O-2, and 1.09 mmol g(-1) for Ar at 298 K and &amp; SIM;10 bar. &amp; SIM;20% higheradsorption capacity was found for N-2 and Ar in Ag-H-ETS-10compared to Ag-ETS-10. The higher sorption capacity was attributedto the formation of a bimodal structure and &amp; pi;-complexation interactionby the Ag cation, which allows a multilayer of N-2 and Armolecules. The Sips isotherm model was well fitted for the Ag-H-ETS-10experimental data among Langmuir, Freundlich, Toth, and Temkin models.The measured equilibrium adsorption data for Ag-H-ETS-10 can be usefulfor the O-2 purification process.</p>
1 aShrotri, Aadesh, R.1 aNiphadkar, Prashant, S.1 aBokade, Vijay, V.1 aNandanwar, Sachin, U.  uhttps://library.ncl.res.in/content/equilibrium-adsorption-nitrogen-oxygen-and-argon-silver-exchanged-hierarchical-ets-10