02085nas a2200229   4500008004100000022001400041245013800055210006900193260000800262300001400270490000600284520125800290100002701548700001701575700001801592700002401610700001701634700002301651700002501674700002401699856013201723       2021                        eng d  a2398-490200aSulfonated polyvinyl alcohol ionomer membrane favoring smooth electrodeposition of zinc for aqueous rechargeable zinc metal batteries0 aSulfonated polyvinyl alcohol ionomer membrane favoring smooth el  cOCT  a5557-55640 v53 aOne of the failure mechanisms of aqueous rechargeable zinc metal batteries (AZMBs) involves high surface area zinc (HSAZ)/dendrite-like deposits over the Zn-metal anode during long-term cycling. Negatively charged (anionic) polymeric ionomer electrolyte membranes and separators are known for suppressing the dendrite-/HSAZ-induced failure of AZMBs. However, the preparation of cost-effective and non-fluorinated ionomers from cheap and environmentally friendly polymers is essential to leverage the feasibility of AZMBs. The current work demonstrates the potential of an ionomer electrolyte membrane (P-AS-C-Zn) made by the crystallization-induced physical cross-linking of sulfonated poly (vinyl alcohol) (PVS) and poly (vinyl alcohol) (PVA) as a dendrite-/HSAZ-inhibiting separator for AZMBs. The P-AS-C-Zn membranes exhibited excellent Zn plating/stripping behavior with a stable voltage vs. time profile beyond 1100 h, compared to their neutral PVA-C-Zn counterpart without any ionomer character (cell failure at close to 280 h). Applying the optimized P-AS-C-Zn membrane in a MnO2||Zn full cell helps retain about 50% of the initial capacity close to 600 cycles in the absence of extra manganese salt in the electrolyte, which is indeed promising.1 aVijayakumar, Vidyanand1 aTorris, Arun1 aKurian, Maria1 aMathew, Megha, Mary1 aGhosh, Meena1 aKhairnar, Ajay, B.1 aBadiger, Manohar, V.1 aKurungot, Sreekumar  uhttps://library.ncl.res.in/content/sulfonated-polyvinyl-alcohol-ionomer-membrane-favoring-smooth-electrodeposition-zinc-aqueous