02687nas a2200361 4500008004100000022001400041245021300055210006900268260000800337300001400345490000700359520141200366653002201778653002601800653003401826653001101860653001301871653001501884653001401899653002301913653002401936653002501960653003301985653002502018653001802043653002502061653001302086100002302099700002002122700002302142700002802165856013202193 2017 eng d a0887-624X00aPartially bio-based poly(amide imide)s by polycondensation of aromatic diacylhydrazides based on lignin-derived phenolic acids and aromatic dianhydrides: synthesis, characterization, and computational studies0 aPartially biobased polyamide imides by polycondensation of aroma cNOV a3636-36450 v553 a

Two new bio-based diacylhydrazide monomers, namely, 4,4-(propane-1,3-diylbis(oxy))bis(3-methoxybenzohydrazide) and 4,4-(propane-1,3-diylbis(oxy))bis(3,5-dimethoxybenzohydrazide) were synthesized starting from lignin-derived phenolic acids, namely, vanillic acid and syringic acid. A series of poly(amide imide)s was synthesized by polycondensation of these diacylhydrazide monomers with commercially available aromatic dianhydrides. Poly(amide imide)s showed inherent viscosity in the range 0.44-0.56 dLg(-1) and exhibited good solubility in organic solvents. Poly(amide imide)s could be cast into transparent, flexible, and tough films from their N,N-dimethylacetamide solutions. Poly(amide imide)s showed 10% weight loss in the temperature range 340-364 degrees C indicating their good thermal stability. Glass transition temperature (T-g) of poly(amide imides)s were measured by DSC and DMA which were in the range 201-223 degrees C and 214-248 degrees C, respectively. The T-g values of poly(amide imide)s were dependent on the number methoxy substituents on aromatic rings of diacylhydrazide monomers. Molecular dynamics simulation studies revealed that chain rigidity is the dominant factor for observed trends in T-g. (c) 2017 Wiley Periodicals, Inc.

10aBiobased Polymers10aComputational studies10aGlass-transaction temperature10alignin10aMonomers10aPlant oils10aPolyimide10aReneable resources10aRenewable resources10aStep-growth polymers10astructure-property relations10aSustanaible Polymers10aThermal night10aThermosetting resins10aVanillin1 aKuhire, Sachin, S.1 aSharma, Pragati1 aChakrabarty, Suman1 aWadgaonkar, Prakash, P. uhttps://library.ncl.res.in/content/partially-bio-based-polyamide-imides-polycondensation-aromatic-diacylhydrazides-based-lignin