01762nas a2200193   4500008004100000022001400041245015200055210006900207260012500276300001100401490000700412520090600419100002101325700002201346700001601368700003001384700002201414856013201436       2005                        eng d  a0003-695100aEnhancement of double-layer capacitance behavior and its electrical conductivity in layered poly (3, 4-ethylenedioxythiophene)-based nanocomposites0 aEnhancement of doublelayer capacitance behavior and its electric  aCIRCULATION & FULFILLMENT DIV, 2 HUNTINGTON QUADRANGLE, STE 1 N O 1, MELVILLE, NY 11747-4501 USAbAMER INST PHYSICScDEC  a2435110 v873 a<p>In this letter, we report on the enhanced double-layer capacitance of a layered poly (3, 4-ethylene dioxythiophene) PEDOT-MoO3 nanocomposite, which has been synthesized by a novel microwave irradiation method. The x-ray photoelectron spectroscopy analysis shows the changes in electron density and the shift in binding energy suggesting charge transfer from sulfur atoms upon PEDOT intercalation between MoO3 layers. The room-temperature conductivity for the PEDOT-MoO3 composite is found to be 1.82x10(-1) S cm(-1), which is four orders of magnitude higher than that of the pristine oxide (3.78x10(-5) S cm(-1)). The enhanced double-layer capacitance of the PEDOT-MoO3 nanocomposite (similar to 300 F g(-1)) compared to that (similar to 40 mF g(-1)) of pristine MoO3 is attributed to higher electronic conductivity, enhanced bidimensionality, and increase in surface area of the nanocomposite.</p>1 aMurugan, Vadivel1 aViswanath, A., K.1 aCampet, Guy1 aGopinath, Chinnakonda, S.1 aVijayamohanan, K.  uhttps://library.ncl.res.in/content/enhancement-double-layer-capacitance-behavior-and-its-electrical-conductivity-layered-poly-3