02056nas a2200217   4500008004100000022001400041245014600055210006900201260007900270300001200349490000600361520118200367653002601549653002201575653001801597653002301615100002101638700003001659700002201689856012701711       2005                        eng d  a1388-248100aElectrochemical studies of poly (3,4-ethylenedioxythiophene) PEDOT/VS2 nanocomposite as a cathode material for rechargeable lithium batteries0 aElectrochemical studies of poly 34ethylenedioxythiophene PEDOTVS  a360 PARK AVE SOUTH, NEW YORK, NY 10010-1710 USAbELSEVIER SCIENCE INCcFEB  a213-2180 v73 a<p>Here, we demonstrate the electrochemical characterization of a new type of layered poly (3,4-ethylenedioxythiophene) PEDOT/ VS2 nanocomposite. It has been prepared via flocculation of delaminated VS2 with subsequent in situ oxidative polymerization of 3,4-ethylenedioxythiophene (EDOT) with VS2 as a host material in the presence of an external oxidizing agent. The interlayer spacing Of VS2 expands from 5.71 to 14.01 A and this interlayer separation is consistent with the existence of a monolayer of PEDOT in the VS2 framework. X-ray diffraction, XPS and TEM studies have been;shown the change in interlayer separation is consistent with the existence of two phases of organic and inorganic species in the nanocomposites corresponding to the intercalation of PEDOT in the VS2 framework. The application potential of the nanocomposite as a cathode material for rechargeable lithium batteries is also demonstrated by the electrochemical intercalation of lithium into the PEDOT/VS2 nanocomposite, where a significant enhancement in the discharge capacity is observed (similar to130 mAh/g) compared to that (80 mAh/g) for pristine VS2. (C) 2004 Published by Elsevier B.V.</p>10alayered nanocomposite10alithium batteries10apolythiophene10avanadium disulfide1 aMurugan, Vadivel1 aGopinath, Chinnakonda, S.1 aVijayamohanan, K.  uhttps://library.ncl.res.in/content/electrochemical-studies-poly-34-ethylenedioxythiophene-pedotvs2-nanocomposite-cathode-0