02344nas a2200289   4500008004100000022001400041245011300055210006900168260007300237300001200310490000800322520134400330653002101674653002201695653001601717653002401733653001801757100002001775700001701795700001401812700001601826700002101842700002501863700001901888700001801907856012901925       2006                        eng d  a0304-885300aModifications in magnetic anisotropy of M-type strontium hexaferrite crystals by swift heavy ion irradiation0 aModifications in magnetic anisotropy of Mtype strontium hexaferr  aPO BOX 211, 1000 AE AMSTERDAM, NETHERLANDSbELSEVIER SCIENCE BVcOCT  a392-4020 v3053 a<p>Using vibrating sample magnetometery (VSM) 50 MeV Li(3+) ion irradiation effects on magnetic properties of single crystals of SrGa(x)In(y)Fe(12-(x+y))O(19) (where x = 0, 5, 7, 9; y = 0, 0.8, 1.3, 1.0), are reported. The substitution of Ga and In in strontium hexaferrite crystals decreases the value of magnetization sharply, which is attributed to shifting of collinear magnetic order to a non-collinear one. Reduction of magnetization is also explained to be as a result of the occupation of the crystallographic sites of Fe(3+) by Ga(3+) and In(3+). The Li(3+) ion irradiation decreases the value of magnetization, irrespective of whether the crystals are Ga-In substituted or unsubstituted crystals of SrFe(12)O(19). The result is interpreted in terms of the occurrence of a paramagnetic doublet in crystals replacing magnetic sextuplet as a result of irradiation. Substitution of Ga-In in Strontium hexaferrite decreases the value of anisotropy constant. Irradiation with Li(3+) ions increases the values of anisotropy field for both substituted as well as unsubstituted crystals. Substitution with Ga-In also decreases the Curie temperature (T(c)) but the irradiation with Li(3+) ions does not affect the curie temperature of either Ga-In substituted or pure SrFe(12)O(19) crystals. (C) 2006 Elsevier B.V. All rights reserved.</p>10aanisotropy field10aCurie temperature10airradiation10aMagnetic anisotropy10aMagnetization1 aKaur, Balwinder1 aBhat, Monita1 aLicci, F.1 aKumar, Ravi1 aKulkarni, S., D.1 aJoy, Pattayil, Alias1 aBamzai, K., K.1 aKotru, P., N.  uhttps://library.ncl.res.in/content/modifications-magnetic-anisotropy-m-type-strontium-hexaferrite-crystals-swift-heavy-ion-0