@article {43899, title = {Copper Cobalt Sulfide Nanosheets Realizing a Promising Electrocatalytic Oxygen Evolution Reaction}, journal = {ACS Catalysis}, volume = {7}, year = {2017}, month = {SEP}, chapter = {5871-5879}, abstract = {

Nanostructured CuCo2S4, a mixed metal thiospinel, is found to be a benchmark electrocatalyst for oxygen evolution reaction (OER) in this study with a low overpotential, a low Tafel slope, a high durability, and a high turnover frequency (TOF) at lower mass loadings. Nanosheets of CuCo2S4 are realized from a hydrothermal synthesis method in which the average thickness of the sheets is found to be in the range of 815 nm. Aggregated nanosheets form a highly open hierarchical structure. When used as an electrocatalyst, CuCo2S4 nanosheets offer an overpotential value of 310 mV at a 10 mA cm(2) current density, which remains consistent for 10000 measured cycles in a 1 M KOH electrolyte. A chronoamperometric study reveals constant oxygen evolution for 12 h at a 10 mV s(-1) scan rate without any degradation of the activity. Furthermore, the calculated mass activity of the CuCo2S4 electrocatalyst is found to be 14.29 A/g and to afford a TOF value of 0.1431 s(-1) at 310 mV at a mass loading of 0.7 mg cm(-2). For comparison, nanostructures of Co3S4 and Cu0.5Co2.5S4 have been synthesized using a similar method followed for CuCo2S4. When compared to the OER activities among these three thiospinels and standard IrO2, CuCo2S4 nanosheets offered the highest OER activities at the same mass loading (0.7 mg/cm(-2)). Extensive X-ray photoelectron spectroscopy and electron paramagnetic resonance analyses for a mechanistic study reveal that introduction of Cu into the Co3S4 lattice enhances the oxygen evolution and kinetics by offering Cu2+ sites for utilitarian adsorption of OH, O, and OOH reactive species and also by offering a highly active high-spin state of octahedral Co3+ for OER catalysis.

}, keywords = {Bifunctional Electrocatalyst, Catalyst, Cuco2s4, Efficient Electrocatalyst, electrocatalyst, Electronic-structure, Nanoparticles, Nanosheet, oxide, oxygen evolution, performance, Recent Progress, Water oxidation, Water Splitting Hydrogen Evolution}, doi = { 10.1021/acscatal.7b01831}, author = {Chauhan, Meenakshi and Reddy, Kasala Prabhakar and Gopinath, Chinnakonda S. and Deka, Sasanka} } @article {43870, title = {NiZn double hydroxide nanosheet-anchored nitrogen-doped graphene enriched with the gamma-NiOOH phase as an activity modulated water oxidation electrocatalyst}, journal = {Nanoscale}, volume = {9}, year = {2017}, month = {SEP}, pages = {12590-12600}, type = {Journal Article}, chapter = {12590-12600}, abstract = {

Herein, we report a facile solvothermal process to synthesize an active electrocatalyst for the oxygen evolution reaction (OER) in an alkaline medium by anchoring nanosheets of a NiZn double hydroxide over nitrogen doped reduced graphene oxide after enriching the system with the γ-NiOOH phase. This catalyst possesses a thin, porous and open layered structure, which makes the system more efficient and accessible for a better electrochemical water oxidation reaction. Moreover, we experimentally demonstrated that incorporation of Zn via a single-step solvothermal method provides an easy approach to obtain plenty of exposed γ-NiOOH phases to make the system more viable for OER with a small overpotential of 290 mV at 10 mA cm-2 and a Tafel slope of 44 mV per decade. In addition to this, the oxophilic nature of Zn in the (Zn)Ni-LDH/N-rGO catalyst helps to improve the long-term stability of the whole system. The obtained results open up possibilities for the design of future robust OER electrocatalysts by the use of very cheap and abundant materials like Ni and Zn in place of expensive Ir and Ru in the present commercial electrocatalysts.

}, keywords = {catalysis, Efficient Electrocatalyst, kinetics, Metal, Nickel-Hydroxide, oxide, Oxygen Evolution Reaction, performance, XPS Spectra, zinc}, issn = {2040-3364}, doi = {10.1039/c7nr02225e}, author = {Nadeema, Ayasha and Dhavale, Vishal M. and Kurungot, Sreekumar} }