@article { ISI:000230685200006, title = {Biphenyl hydrogenation over supported transition metal catalysts under supercritical carbon dioxide solvent}, journal = {Applied Catalysis A - General}, volume = {288}, number = {1-2}, year = {2005}, month = {JUL}, pages = {43-47}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Catalytic hydrogenation of biphenyl to bicyclohexyl, an organic hydrogen storage medium, was examined over supported transition metal catalysts in supercritical carbon dioxide solvent. The yield of bicyclohexyl was almost 100\% over the charcoal-supported rhodium (Rh/C) and ruthenium (Ru/C) catalysts at the temperature of 323 K, which was much lower than that required for biphenyl hydrogenation in organic solvents (573 K). The initial activity was higher over the Rh/C catalyst, while the initial selectivity to bicyclohexyl was higher over the Ru/C catalyst. The conversion of biphenyl increased with increase in hydrogen and carbon dioxide pressures, while the selectivity to bicyclohexyl was independent of hydrogen and carbon dioxide pressures over both catalysts. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {bicyclohexyl, biphenyl, charcoal-supported rhodium catalyst, charcoal-supported ruthenium catalyst, Hydrogen storage, Hydrogenation, Supercritical carbon dioxide}, issn = {0926-860X}, doi = {10.1016/j.apcata.2005.04.021}, author = {Hiyoshi, Norihito and Rode, C. V. and Sato, O. and Shirai, M.} } @article { ISI:000231197500017, title = {Vanadium-containing ordered mesoporous silicas: synthesis, characterization and catalytic activity in the hydroxylation of biphenyl}, journal = {Applied Catalysis A - General}, volume = {290}, number = {1-2}, year = {2005}, month = {AUG}, pages = {148-158}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A series of vanadium-containing ordered mesoporous MCM-41 materials (V-OMS) have been synthesized by direct hydrothermal (VMCM-41) and grafting (V/MCM-41) methods using hexadecyl trimethyl ammonium bromide (HDTMABr) as the structure-directing agent. The physico-chemical properties of the vanadium-containing materials were characterized in detail by ICP-OES, XRD, Fr-IR, N-2 adsorption-desorption, DRUV-VIS, TPR, XPS and SEM techniques. The redox performances of the vanadium-modified mesoporous materials were tested in the hydroxylation of biphenyl using aqueous H2O2 (30 wt.\%) as oxidant. For a better exploitation of the catalytic activity, the reaction parameters are optimized in terms of temperature, solvent, oxidant, etc. A comparison between the catalytic activity values of the vanadium-containing mesoporous materials prepared by the two routes shows that vanadium-substituted (V-MCM-41) materials had increased activity and improved selectivity for mono hydroxyl products in the hydroxylation reaction of biphenyl compared to the V/MCM-41 catalysts. The heterogenity of the catalysts was verified by a series of leaching studies. Both the catalysts enhance the leaching of active vanadia species during the reaction; among them, V/MCM-41 shows the least heterogenity. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {biphenyl, heterogenity, MCM-41, Mesoporous molecular sieves, Vanadium}, issn = {0926-860X}, doi = {10.1016/j.apcata.2005.05.012}, author = {George, J. and Shylesh, S and Singh, AP} } @article { ISI:000319610100003, title = {Synthesis and characterization of poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant biphenyl and naphthyl groups}, journal = {High Performance Polymers}, volume = {25}, number = {3}, year = {2013}, month = {MAY}, pages = {260-267}, publisher = {SAGE PUBLICATIONS LTD}, address = {1 OLIVERS YARD, 55 CITY ROAD, LONDON EC1Y 1SP, ENGLAND}, abstract = {

New poly(ether ether ketone)s (PEEKs) and poly(ether ether ketone ketone)s (PEEKKs) containing pendant biphenyl and naphthyl groups were synthesized by nucleophilic substitution reaction of each of the four bisphenols viz., 1-(4- biphenylyl)- 1,1- bis(4- hydroxyphenyl) ethane, 1-(4- biphenylyl)- 1,1- bis(3- methyl, 4- hydroxyphenyl) ethane, 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-phenol and 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-3-methylphenol with 4,4{\textquoteright}- difluorobenzophenone and 1,3- bis(4- fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene in the presence of anhydrous potassium carbonate. Inherent viscosities and number-average molecular weights of polymers were in the range of 0.42-0.86 dl/g and 2.40-7.55 x 10(4), respectively. PEEKs and PEEKKs were amorphous in nature and were readily soluble in a wide range of organic solvents and could be cast into flexible and tough films from chloroform solution. Glass transition temperature of PEEKs and PEEKKs were in the range of 180 degrees C -200 degrees C. T-10 values of PEEKs and PEEKKs were in the range of 424 degrees C-512 degrees C in nitrogen atmosphere, indicating their good thermal stability.

}, keywords = {biphenyl, bisphenol, naphthyl, poly(ether ether ketone ketone)s, poly(ether ether ketone)s, Polycondensation, Thermal properties}, issn = {0954-0083}, doi = {10.1177/0954008312462731}, author = {Honkhambe, Pandurang N. and Dhamdhere, Neelam A. and Tawade, Bhausaheb V. and Salunkhe, Manikrao M. and Wadgaonkar, Prakash P.} }