@article { ISI:000239542900032, title = {Direct synthesis of nanocrystalline silver from the reaction between silver carboxylates and n-trioctylphosphine}, journal = {Journal of Nanoscience and Nanotechnology}, volume = {6}, number = {7}, year = {2006}, month = {JUL}, pages = {2095-2102}, publisher = {AMER SCIENTIFIC PUBLISHERS}, type = {Article}, address = {26650 THE OLD RD, STE 208, VALENCIA, CA 91381-0751 USA}, abstract = {

Neat n-Trioctylphosphine (TOP) has been used for the first ever time for reduction of silver nitrate and silver carboxylates (citrate, oleate, and myristate) under mild thermal reaction conditions. UV-visible absorption measurements of re-dispersible silver particles that were obtained by reduction of silver myristrate (product-IV) and silver nitrate (product-I) showed surface plasmon resonance absorption peak at 400 nm. The powder XRD pattern of fcc zero-valent silver resulted in diameters in the range of about 25-30 nm. TEM analysis showed particle diameter similar to that was observed by the XRD. FTIR spectroscopy revealed that the organics from the carboxylate group are retained by the nano-particles in case of product-IV however, presence of TOP is observed in product-I. It is found that when silver nitrate is reduced by TOP, spherical silver nano-particles with poor redispersity are formed but extended heating results in formation of long silver rods of micrometer size however, the re-dispersible nano-particles are easily formed when silver carboxylates are reduced by TOP.

}, keywords = {Chemical synthesis, Nanocrystalline, noble metal, XRD}, issn = {1533-4880}, doi = {10.1166/jnn.2006.339}, author = {Charan, Shobhit and Singh, Narendra and Khanna, P. K. and Patil, K. R.} } @article { ISI:000260776800023, title = {Superparamagnetic nanocrystalline ZnFe2O4 with a very high curie temperature}, journal = {Journal of Nanoscience and Nanotechnology}, volume = {8}, number = {8}, year = {2008}, month = {AUG}, pages = {3955-3958}, publisher = {AMER SCIENTIFIC PUBLISHERS}, address = {25650 NORTH LEWIS WAY, STEVENSON RANCH, CA 91381-1439 USA}, abstract = {

Studies on the magnetic properties of nanocrystalline ZnFe2O4 synthesized by an autocombustion method are reported. Superparamagnetic behavior is observed for the nanocrystalline materials with particle sizes of 8 nm and 17 nm, with superparamagnetic blocking temperatures of 65 K and 75 K, respectively. Magnetic hysteresis with very large coercivities of 533 Oe and 325 Oe, respectively, are observed at 12 K. Studies on the temperature variation of the magnetization above room temperature indicate that the Curie temperature is as high as similar to 800 K when compared to the paramagnetic nature of bulk zinc ferrite at room temperature.

}, keywords = {Curie temperature, Nanocrystalline, Superparamagnetism, Zinc Ferrite}, issn = {1533-4880}, doi = {10.1166/jnn.2008.201}, author = {Deka, Sasanka and Joy, Pattayil Alias} } @article { ISI:000263070700020, title = {Enhanced solar-radiation induced photocatalytic activity of surface-modified nanocrystalline anatase-titania}, journal = {Catalysis Letters}, volume = {128}, number = {1-2}, year = {2009}, month = {MAR}, pages = {137-143}, publisher = {SPRINGER}, address = {233 SPRING ST, NEW YORK, NY 10013 USA}, abstract = {

Sol-gel derived pure nanocrystalline (similar to 20-30 nm) anatase-titania has been surface-modified by depositing silver(I) oxide and silver (predominantly the former) via UV-reduction process. The pure and surface-modified nanocrystalline anatase-titania have been characterized using different analytical techniques for determining the average nanocrystallite size, phase-contents, surface-chemistry, as well as the absorption and photoluminescence characteristics. It is demonstrated that, the latter exhibits an enhanced solar-radiation induced photocatalytic activity as compared to that of the former as a result of the absorption in the visible-region and enhanced photo-induced e(-)/h(+) life-time, both caused by the surface-deposition of silver(I) oxide and silver.

}, keywords = {Nanocrystalline, Photocatalysis, Silver, sol-gel, titania, UV-reduction}, issn = {1011-372X}, doi = {10.1007/s10562-008-9704-1}, author = {Priya, R. and Baiju, K. V. and Shukla, S. and Biju, S. and Reddy, M. L. P. and Patil, K. R. and Warrier, K. G. K.} } @article { ISI:000207804200008, title = {Single step synthesis and properties of M/MFe2O4 and PVDF/M/MFe2O4 (M = Co, Ni) magnetic nanocomposites}, journal = {Science of Advanced Materials}, volume = {1}, number = {3}, year = {2009}, month = {DEC}, pages = {262-268}, publisher = {AMER SCIENTIFIC PUBLISHERS}, address = {26650 THE OLD RD, STE 208, VALENCIA, CA 91381-0751 USA}, abstract = {

Metal/ferrite nanocomposites (M/MFe2O4; M = Co, Ni), consisting of nanoparticles of a metal and the corresponding metal ferrite, have been synthesized under in situ conditions by a simple and single step process. The metal/ferrite nanocomposites embedded in a polymer matrix have been prepared by a simple hot-pressing method. The performance parameters such as magnetization, coercivity, permeability and dielectric constant of the two- and three-phase nanocomposite systems are compared. The coercivity increases and the permeability decreases with increasing polymer content in the three-phase composite. Enhancement of the dielectric constant is observed at low frequencies.

}, keywords = {Dielectric, Ferrite, magnetic properties, Nanocomposite, Nanocrystalline, permeability}, issn = {1947-2935}, doi = {10.1166/sam.2009.1053}, author = {Deka, Sasanka and Joy, Pattayil Alias and Kumar, A. Pratheep} } @article { ISI:000313149800004, title = {Enhancement in the magnetostriction of sintered cobalt ferrite by making self-composites from nanocrystalline and bulk powders}, journal = {ACS Applied Materials \& Interfaces}, volume = {4}, number = {12}, year = {2012}, month = {DEC}, pages = {6421-6425}, publisher = {AMER CHEMICAL SOC}, address = {1155 16TH ST, NW, WASHINGTON, DC 20036 USA}, abstract = {

Sintered polycrystalline cobalt ferrite is a potential magnetostrictive smart material for applications as sensors and actuators. A novel concept of enhancing the magnetostrictive strain of sintered cobalt ferrite by making self-composites from nanosized and bulk powders with different particle sizes of the same material as components is reported. The self-composites give higher magnetostriction coefficient and strain derivative when compared to the sintered products obtained from the individual powders. The individual components give a maximum magnetostriction up to similar to 310 ppm, whereas up to similar to 370 ppm is obtained for a two-component system consisting of powders of two different sizes. On the other hand, a three-component self-composite made from starting powders of 3 nm, 40 nm and \>1 mu m give very high magnetostriction of similar to 400 ppm at 800 kA/m, suitable for making devices.

}, keywords = {Cobalt ferrite, Magnetostriction, Nanocrystalline, self-composite, Sintering}, issn = {1944-8244}, doi = {10.1021/am302053q}, author = {Mohaideen, Kamal Khaja and Joy, Pattayil Alias} } @article { ISI:000324099300024, title = {High magnetostriction coefficient of Mn substituted cobalt ferrite sintered from nanocrystalline powders and after magnetic field annealing}, journal = {Current Applied Physics}, volume = {13}, number = {8}, year = {2013}, month = {OCT}, pages = {1697-1701}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Magnetostriction characteristics of Mn substituted cobalt ferrite, CoFe2-xMnxO4 (0 \<= x \<= 0.3), sintered from nanocrystalline powders of average particle size of similar to 4 nm have been studied. Larger value of magnetostriction at lower magnetic field is achieved after substitution of Mn for Fe. The maximum value of magnetostriction coefficient is not much affected and the slope of the magnetostriction is increased with increasing Mn content. Higher maximum value of magnetostriction coefficient (lambda) of 234 ppm comparable to that of the unsubstituted composition with larger strain derivative (d lambda/dH) is obtained for x = 0.2 in CoFe2-xMnxO4. The magnetostriction coefficient is increased to 262 ppm with further enhancement in the strain derivative after annealing the sintered compact at 300 degrees C in a magnetic field of 400 kA/m for 30 min. (C) 2013 Elsevier B.V. All rights reserved.

}, keywords = {Cobalt ferrite, Magnetic field annealing, Magnetostriction, Mn substitution, Nanocrystalline}, issn = {1567-1739}, doi = {10.1016/j.cap.2013.06.030}, author = {Mohaideen, Kamal Khaja and Joy, Pattayil Alias} } @article { ISI:000324311200017, title = {Influence of initial particle size on the magnetostriction of sintered cobalt ferrite derived from nanocrystalline powders}, journal = {Journal of Magnetism and Magnetic Materials}, volume = {346}, year = {2013}, month = {NOV}, pages = {96-102}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The role of initial particle size on the magnetostriction coefficient of sintered cobalt ferrite derived from nanocrystalline powders is studied. Nanoparticles of cobalt ferrite with different sizes in the range 3-80 nm are synthesized by an autocombustion method using metal nitrates and glycine. It has been observed that the initial particle size of the starting powders has a strong influence on the magnetostrictive behavior of sintered cobalt ferrite. Highest magnetostrictive strain and strain derivative are obtained for sintered ferrite derived from nanoparticles of size \< 5 nm. The results show that higher magnetostriction coefficient for sintered cobalt ferrite can be achieved by compacting nanocrystalline particles of very small size. (C) 2013 Elsevier B.V. All rights reserved.

}, keywords = {Cobalt ferrite, magnetic properties, Magnetostriction, Microstructure, Nanocrystalline, Particle size}, issn = {0304-8853}, doi = {10.1016/j.jmmm.2013.07.016}, author = {Mohaideen, Kamal Khaja and Joy, Pattayil Alias} } @article { ISI:000329554400013, title = {Studies on the effect of sintering conditions on the magnetostriction characteristics of cobalt ferrite derived from nanocrystalline powders}, journal = {Journal of the European Ceramic Society}, volume = {34}, number = {3}, year = {2014}, month = {MAR}, pages = {677-686}, publisher = {ELSEVIER SCI LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

The effect of sintering conditions on the magnetostriction characteristics of sintered cobalt ferrite derived from nanocrystalline powders is studied. It is observed that the magnetostriction coefficient as well as the slope of the magnetostriction as a function of field depends on the microstructure of the sintered product. There is a direct correlation between the magnetostriction characteristics and density as well as porosity of the sintered products. Intragranular pores are found to be strongly influencing the magnetostriction characteristics. Similarly, correlation is found between the magnetostriction parameters and the Curie temperature, indicating the role of cation distribution which affects the magnetic anisotropy. Sintering the compacts made from nanocrystalline powders at 1450 degrees C for a very short duration is found to give high values of magnetostriction coefficient. However, higher values of magnetostriction at low magnetic fields are obtained for samples sintered at lower temperatures for longer duration and having relatively lower density. (C) 2013 Elsevier Ltd. All rights reserved.

}, keywords = {Cobalt ferrite, Magnetostriction, Microstructure, Nanocrystalline, Sintering}, issn = {0955-2219}, doi = {10.1016/j.jeurceramsoc.2013.09.018}, author = {Mohaideen, Kamal Khaja and Joy, Pattayil Alias} } @article {43882, title = {Activity tuning of cobalt ferrite nanoparticles anchored on N-doped reduced graphene oxide as a potential oxygen reduction electrocatalyst by Zn substitution in the spinel matrix}, journal = {Chemistry Select}, volume = {2}, year = {2017}, month = {SEP}, pages = {7845-7853}, type = {Article}, abstract = {

Development of highly efficient and durable ORR catalysts by using non-platinum group metals (such as Co, Fe, Mn, and Zn) is a challenging task in the forward path towards the realization of low-cost energy devices in the commercial stream. The present work deals with an effective strategy wherein an efficient Pt-free electrocatalyst for oxygen reduction reaction (ORR) is prepared by stoichiometrically substituting some fraction of Fe with Zn in cobalt ferrite and anchoring these spinel nanoparticles on nitrogen doped reduced graphene oxide (N-rGO). Zn substitution is found to be significantly altering the ratio of Fe2+/Fe3+ in the cobalt ferrite nanocrystal system with a concomitant promotional influence on its electrocatalytic activity towards ORR. The nanoparticle composition with a Co, Fe and Zn molar ratio of 1.0:1.7:0.3, represented by the formula CoFe1.7Zn0.3O4(CFZn(0.3)), supported over N-rGO has shown 10 mV and 20 mV positive shift in the onset and half-wave potentials, respectively, for ORR in 0.1 M KOH in comparison to the nanoparticles of CoFe2O4 supported over N-rGO (CF/N-rGO). The optimum Zn substitution is found to be narrowing down the difference with the state-of-the-art Pt/C for ORR by 100 and 110 mV in terms of the onset and half-wave potentials, respectively. Most significantly, the homemade catalyst is found to be clearly outperforming the Pt catalyst in terms of the limiting current density and electrochemical durability.

}, keywords = {Carbon Nano-fiber, Cathod Catalyst, CoFe2O4, Evolution, Magnetic-properties, Membrane fuel- Cell, Metal-Air Batteries, N-doped graphene, Nanocrystalline, nanocrystals, oxygen reduction reaction, performance, Platinium, solvothermal synthesis, Zn substituted cobalt ferrite}, issn = {2365-6549}, doi = {10.1002/slct.201701684}, author = {Kashyap, Varchaswal and Singh, Santosh K. and Kurungot, Sreekumar} }