@article { ISI:000232864800029, title = {Low temperature synthesis of MgTa2O6 powders}, journal = {Materials Letters}, volume = {59}, number = {29-30}, year = {2005}, month = {DEC}, pages = {3926-3928}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A combination of digestion and further low temperature calcination to crystallize the product is employed to prepare MgTa2O6 (MT) ceramics. Freshly prepared niobium hydroxide gel is mixed with magnesium hydroxide thoroughly and allowed to react at 100 degrees C under refluxing and stirring conditions for 6-12 h. The X-ray amorphous product so formed is heated at 550 degrees C to form crystalline MgTa2O6. This is the lowest temperature so far reported for the formation of MgTa2O6. For comparison, MT powders were also prepared by the traditional solid state method. Transmission electron microscope (TEM) investigations revealed that the average particle size is 40 nm for the low temperature calcined powders. (C) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Electron microscopy, magnesium tantalate, Oxides, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.07.035}, author = {Navale, SC and Samuel, V and Ravi, V} } @article { ISI:000230275100022, title = {Preparation of nanocrystalline LiNbO3 by citrate gel method}, journal = {Materials Letters}, volume = {59}, number = {19-20}, year = {2005}, month = {AUG}, pages = {2476-2478}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A gel was formed when an aqueous solution of Li(NO3) NbF5 and citric acid in stoichiometric ratio is heated in a water bath at 100 degrees C. This gel on decomposition at 700 degrees C produced the fine crystallites of ternary oxide, LiNbO3 (LN). The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Electron microscopy, electronic materials, lithium niobate, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.03.028}, author = {Navale, SC and Samuel, V and Ravi, V} } @article { ISI:000231605600002, title = {Preparation of ultrafine LiTaO3 powders by citrate gel method}, journal = {Bulletin of Materials Science}, volume = {28}, number = {5}, year = {2005}, month = {AUG}, pages = {391-393}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

A gel was formed when a aqueous solution of Li(NO3), TaF5 and citric acid in stoichiometric ratio was heated in a water bath. This gel on decomposition at 700 degrees C produced fine crystallites of ternary oxide, LiTaO3 (LT). The phase contents and lattice parameters were studied by powder X-ray diffraction (XRD). Particle size and morphology were studied by transmission electron spectroscopy (TEM).

}, keywords = {Ceramics, Electron microscopy, electronic materials, X-ray diffraction}, issn = {0250-4707}, doi = {10.1007/BF02711224}, author = {Navale, SC and Samuel, V and Ravi, V} }