@article { ISI:000237158200003, title = {Phase evolution of NiTiO3 prepared by coprecipitation method}, journal = {Materials Letters}, volume = {60}, number = {15}, year = {2006}, month = {JUL}, pages = {1791-1792}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A simple coprecipitation technique was used for the preparation of NiTiO3 powders. Ammonium carbonate solution was added to a solution mixture containing stoichiometric amounts of Ni(NO3)(2) and TiOCl2 to precipitate nickel as carbonate and titanium as hydroxide under basic conditions. The precipitate was calcined at different temperatures ranging from 100 to 800 degrees C and phase evolution of NiTiO3 was investigated by X-ray diffraction (XRD) studies. It is observed that nickel titanate was formed at 750 degrees C. For comparison, NiTiO3 was also prepared by standard ceramic process. Particle size and morphology was studied by transmission electron microscopy (TEM). (c) 2005 Elsevier B.V. All fights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, NiTiO3, Oxides, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.12.023}, author = {Murugan, A. Vadivel and Samuel, V. and Navale, S. C. and Ravi, V.} } @article { ISI:000238624000017, title = {Synthesis of MgNb2O6 by coprecipitation}, journal = {Materials Research Bulletin}, volume = {41}, number = {7}, year = {2006}, month = {JUL}, pages = {1353-1356}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

A simple coprecipitation technique was used successfully to synthesize fine powders of MgNb2O6 (MN) phase. An aqueous mixture of ammonium carbonate and ammonium hydroxide was used to precipitate Mg2+ and Nb5+ cations as carbonate and hydroxide respectively under basic conditions. This precipitate on heating at 750 degrees C produced MN powders. For comparison MN powders were prepared by the traditional solid state method. The phase content and the lattice parameters were studied by powder X-ray diffraction (XRD). Particle size and morphology of the particles were studied by scanning electron microscopy (SEM). (C) 2006 Elsevier Ltd. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, electronic materials, X-ray diffraction}, issn = {0025-5408}, doi = {10.1016/j.materresbull.2005.12.009}, author = {Navale, S. C. and Gaikwad, A. B. and Ravi, V.} } @article { ISI:000244008300028, title = {Influence of surfactant on ZnO varistors}, journal = {Ceramics International}, volume = {33}, number = {2}, year = {2007}, month = {MAR}, pages = {289-291}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

ZnO varistors with and without surfactant such as sodium dodecyl sulphate (SIDS) are prepared by nitrate-combustion process. The samples were identically heat treated and sintered at 1000 degrees C for 12 h to study the influence of the surfactant on the nonlinear electrical properties of polycrystalline ZnO. It is observed that the nonlinear coefficient decreases marginally (alpha = 35) for samples prepared with surfactant, whereas breakdown field (E-B = 130 V/mm) decreased significantly. The corresponding parameters for the samples synthesized without surfactant are alpha = 45 and E-B = 400 V/mm. Hence, this method can be used for the manufacture of varistors with low to moderate breakdown fields. (c) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {Chemical synthesis, Semiconductors, X-ray methods, ZnO}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2005.08.010}, author = {Dhage, S. R. and Navale, S. C. and Ravi, V.} }