@article { ISI:000228633100020, title = {Silicotungstate-modified zirconia as an efficient catalyst for phenol tert-butylation}, journal = {Journal of Molecular Catalysis A-Chemical}, volume = {233}, number = {1-2}, year = {2005}, month = {MAY}, pages = {141-146}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The alkylation of phenol with tert-butanol was investigated using zirconia modified with silicotungstic acid (STA) as catalysts. The catalysts with different STA loading (5-25 wt.\% calcined at 750 degrees C) and calcination temperature (15 wt.\% calcined from 350 to 850 degrees C) were prepared and characterized by X-ray diffraction and NH3-TPD measurements. The XRD results indicate that STA stabilizes the tetragonal phase of zirconia. The catalyst with 15\% STA on ZrO2 calcined at 750 degrees C shows the highest acidity and hence highest activity. Under the reaction conditions of 140 degrees C, tert-butanol/phenol molar ratio of 2 and LHSV of 4 h(-1), phenol conversion was 95.4\% with selectivity to 2-tert-butyl phenol 4.3\%, 4-tert-butyl phenol 59.2\% and 2,4-di-tert-butyl phenol 35.8\%. The reaction was studied as a function of time for 50 It without appreciable change in phenol conversion and product selectivity. The deactivated catalyst could be regenerated by calcination with out appreciable lose in catalytic activity and product selectivity. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {phenol, Silicotungstic acid, tert-butylation, Zirconia}, issn = {1381-1169}, doi = {10.1016/j.molcata.2005.02.021}, author = {Devassy, Biju M. and Shanbhag, G. V. and Mirajkar, Subhash P. and Bohringer, Walter and Fletcher, Jack C. Q. and Halligudi, Shivaraj B.} } @article { ISI:000230389700024, title = {Synthesis of linear alkyl benzenes over zirconia-supported 12-molybdophosphoric acid catalysts}, journal = {Journal of Molecular Catalysis A - Chemical}, volume = {236}, number = {1-2}, year = {2005}, month = {JUL}, pages = {162-167}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The liquid-phase alkylation of benzene with 1-octene and 1-dodecene was investigated using zirconia-supported 12-molybdophosphoric acid (MPA) as catalyst. The catalysts with different MPA loading (5-25 wt.\% calcined at 700 degrees C) and calcination temperature (15 wt.\% calcined from 500 to 750 degrees C) were prepared by suspending zirconium oxyhydroxide in methanol solution of MPA followed by drying and calcination. These catalysts were characterized by X-ray diffraction, and P-31 MAS NMR spectroscopy measurements. The XRD results indicated that MPA stabilizes the tetragonal phase of zirconia. 3 1 P MAS NMR spectra show that the nature of phosphorous species depend on MPA loading and calcination temperature, and it show the existence of three types of phosphorous species, one is the Keggin unit and the other is the decomposition product of MPA and third one an unidentified species. FTIR pyridine adsorption on 15\% MPA catalyst calcined at 700 degrees C showed the presence both Bronsted and Lewis acidity. Under the reaction conditions of 83 C, benzene/1-olefin molar ratio of 10 (time, 1 h), the most active catalyst, 15\% MPA calcined at 700 C gave more than 90\% olefin conversion with selectivity to 2-phenyl octane, 55\% and 2-phenyl dodecane, 45\%. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {12-molybdophosphoric acid, benzene alkylation, linear alkyl benzene, Zirconia}, issn = {1381-1169}, doi = {10.1016/j.molcata.2005.03.033}, author = {Devassy, Biju M. and Lefebvre, F. and Bohringer, Walter and Fletcher, Jack C. Q. and Halligudi, Shivaraj B.} } @article { ISI:000238502400034, title = {Shape selective synthesis of long-chain linear alkyl benzene (LAB) with AIMCM-41/beta zeolite composite catalyst}, journal = {Journal of Molecular Catalysis A-Chemical}, volume = {253}, number = {1-2}, year = {2006}, month = {JUL}, pages = {239-244}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The liquid-phase alkylation of benzene with long-chain olefins such as 1-decene, 1-octene and 1-dodecene was carried out over AIMCM-41/Beta zeolite composite material as catalyst. The catalyst was prepared by seeding method and characterized by XRD, N-2 sorption, FTIR pyridine adsorption, NH3-TPD and SEM. Powder XRD of AlMCM-41/Beta zeolite composite material showed the co-existence of well-structured microporous and mesophase of AlMCM-41. The typical textural characteristics of micro- and meso-structured phases were observed in the composite material. The effect of temperature, reactant molar ratios and catalyst weight on 1-dodecene conversion and products selectivity was studied. The composite catalyst was found to be the highly selective towards the formation 2-dodecylbenzene. Under the reaction conditions of 120 degrees C, benzene/1-dodecene molar ratio 10 and time 2h, the catalyst gave 48\% dodecene conversion with 76\%, 2-dodecylbenzene selectivity. Significant improvement in catalytic activity has been achieved by composite material as compared to Al-MCM-41. Although zeolite beta and composite material gave similar conversion of dodecene, the composite material showed higher selectivity towards 2-dodecylbenzene, which could be due to higher diffusibility of 2-dodecylbenzene isomer in the composite material. (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {AIMCM-41/beta zeolite composite, Alkylation, Benzene, long-chain olefins}, issn = {1381-1169}, doi = {10.1016/j.molcata.2006.03.045}, author = {Bordoloi, Ankur and Devassy, Biju M. and Niphadkar, P. S. and Joshi, P. N. and Halligudi, Shivaraj B.} } @article { ISI:000253450900027, title = {Synthesis of biodiesel over zirconia-supported isopoly and heteropoly tungstate catalysts}, journal = {Catalysis Communications}, volume = {9}, number = {5}, year = {2008}, month = {MAR}, pages = {696-702}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The liquid-phase synthesis of biodiesel by transesterification of sunflower oil with methanol is carried out by using zirconia-supported isopoly and heteropoly tungstates (HPAs) as catalysts. The isopoly and heteropoly tungstate catalysts were prepared by suspending zirconium oxyhydroxide in water/methanol solution of ammonium metatungstate/silicotungstic acid, phosphotungstic acid (WO3/HPA loading, 15\%,,) followed by drying and calcination at 750 degrees C. The catalysts were characterized by XRD, Raman spectroscopy, IR spectroscopy, NH3-TPD and FTIR pyridine adsorption spectroscopy. XRD results indicate that the presence of isopoly and heteropoly tungstates stabilizes ZrO2 in tetragonal phase. Raman and IR spectra of the catalysts show that tungstate species exist as zirconia-anchored octahedral mono-oxotungstate. The acidity measurements by NH3-TPD and FTIR pyridine adsorption spectroscopy show that zirconia-supported phosphotungstate has the highest total acidity and zirconia-supported isopoly tungstate has the highest Bronsted acidity. The zirconia-supported isopoly tungstate shows superior catalytic performance compared to zirconia-supported heteropoly tungstate catalysts. Under the reaction conditions of 200 degrees C and methanol/oil molar ratio 15, 15\% WO3/ZrO2 calcined at 750 degrees C gave 97\% conversion of oil. This catalyst also efficiently catalyzes methanolysis of other vegetable oils like mustard oil and sesame oil. The deactivated catalyst could be regenerated by calcination without appreciable loss in activity. (c) 2007 Elsevier B.V. All rights reserved.

}, keywords = {Biodiesel, phosphotungstic acids, Silicotungstic acid, transesterification, tungsten oxide, Zirconia}, issn = {1566-7367}, doi = {10.1016/j.catcom.2007.08.007}, author = {Sunita, G. and Devassy, Biju M. and Vinu, Ajayan and Sawant, Dhanashri P. and Balasubramanian, Veerappan V. and Halligudi, Shivappa B.} }