@article { ISI:000228797100048, title = {Preparation of ferroelectric BaNb2O6 the urea method}, journal = {Materials Letters}, volume = {59}, number = {14-15}, year = {2005}, month = {JUN}, pages = {1929-1931}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A precipitate was formed when an aqueous solution of BaCl2, NbF5 and urea in required ratio (the ratio of total metal cations to the urea is five) is heated on a water bath at 100 degrees C. This precipitate on decomposition at 600 degrees C yielded the nanocrystallites of BaNb2O6 (BN), as confirmed by X-ray diffraction study (XRD). This is a much lower temperature as compared to that prepared by traditional solid state method (1000 degrees C) as reported for the formation of BaNb2O6. Transmission electron microscope (TEM) investigations revealed that the average particle size is 85 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 900. The ferroelectric hysteresis loop parameters of these samples were also studied. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.02.028}, author = {Dhage, S. R. and Pasricha, R. and Ravi, V.} } @article { ISI:000226803200008, title = {Synthesis of fine particles of ZnO at 100 degrees C}, journal = {Materials Letters}, volume = {59}, number = {7}, year = {2005}, month = {MAR}, pages = {779-781}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A simple gel to crystal conversion route has been followed for the preparation of fine ZnO at 80-100 degreesC under refluxing conditions. Freshly prepared zinc hydroxide gel is allowed to crystallize under refluxing and stirring conditions for 4-6 It. Formation of fine crystallites of ZnO is confirmed by X-ray diffraction (XRD) study. Transmission electron microscope (TEM) investigations revealed that the average particle size is 100 nm for these powders. (C) 2004 Elsevier B.V All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2004.11.019}, author = {Dhage, S. R. and Pasricha, R. and Ravi, V.} } @article { ISI:000227164000044, title = {Synthesis of Sr0.5Ba0.5Nb2O6 by urea method}, journal = {Materials Letters}, volume = {59}, number = {8-9}, year = {2005}, month = {APR}, pages = {1053-1055}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A precipitate was formed when an aqueous solution of SrCl2, BaCl2, NbF5 and urea in stoichiometric ratio (total metal cations to urea ratio is 5) is heated on a water bath.. This precipitate on decomposition at 750 degreesC yielded the nanocrystallites of ternary oxide, Sr0.5Ba0.5Nb2O6 (SBN) as confirmed by X-ray diffraction study (XRD). This is much lower temperature as compared to that prepared by traditional solid state method (1000 degreesC as reported for the formation of SBN ceramics. Transmission electron microscope (TEM) investigations revealed that the average particle size is 100 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 1050. The ferroelectric hysteresis loop parameters of these samples were also studied. (C) 2004 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Electron microscopy, ferroelectricity, Oxides}, issn = {0167-577X}, doi = {10.1016/j.matlet.2004.12.003}, author = {Dhage, S. R. and Pasricha, R. and Ravi, V.} } @article { ISI:000238298100027, title = {Co-precipitation technique for the preparation of ferroelectric BaBi2Ta2O9}, journal = {Materials Chemistry and Physics}, volume = {98}, number = {2-3}, year = {2006}, month = {AUG}, pages = {344-346}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

A simple co-precipitation technique had been successfully applied for the preparation of pure ultrafine single phase BaBi2Ta2O9 (BBT). Ammonium hydroxide and ammonium oxalate were used to precipitate Ba2+, Bi3+ and Ta5+ cations simultaneously. No pyrochlore phase was found while heating powder at 800 degrees C and pure BaBi2Ta2O9 phase was found to be formed by X-ray diffraction. Particle size and morphology was studied by transmission electron spectroscopy (TEM). The room temperature dielectric constant at 1 kHz is 350. The ferroelectric hysteresis loop parameters of these samples were also studied. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.09.036}, author = {Dhage, S. R. and Pasricha, R. and Murugan, A. Vadivel and Ravi, V.} }