@article { ISI:000227550500009, title = {Co-precipitation method for the preparation of nanocrystalline ferroelectric SrBi2Nb2O9 ceramics}, journal = {Journal of Electroceramics}, volume = {14}, number = {1}, year = {2005}, month = {JAN}, pages = {83-87}, publisher = {SPRINGER}, type = {Article}, address = {VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS}, abstract = {

A simple co-precipitation technique had been successfully applied for the preparation of pure ultrafine single phase SrBi2Nb2O9. Ammonium hydroxide and ammonium oxalate were used to precipitate Sr2+, Bi3+ and Nb5+ cations simultaneously. No pyrochlore phase was found while heating powder at 850 C and pure SrBi2Nb2O9 (SBN) phase was formed as revealed by the X-ray diffraction (XRD) studies. Particle size and morphology was studied by transmission electron microscopy (TEM). The room temperature dielectric constant at 1 kHz is 100. The ferroelectric hysteresis loop parameters of these samples were also studied.

}, keywords = {Ceramics, Chemical synthesis, electronic materials, ferroelectricity, Oxides}, issn = {1385-3449}, doi = {10.1007/s10832-005-6588-y}, author = {Gaikwad, S. P. and Dhage, S. R. and Potdar, H. S. and Samuel, V. and Ravi, V.} } @article { ISI:000230338900015, title = {Synthesis of rutile from ATO and stearic acid}, journal = {Materials Letters}, volume = {59}, number = {21}, year = {2005}, month = {SEP}, pages = {2673-2675}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Nanocrystalline titanium dioxide in the rutile phase has been obtained from the solid state reaction between ammonium titanyl oxalate (ATO) and stearic acid at 400 degrees C in air. The fine powders of ATO and stearic acid are mixed well using acetone in an agate mortar and pestle for 2 h. This mixture (weight ratio of ATO to stearic acid \> 5) on heating at 400 degrees C produces rutile powders. For the ratios of ATO to stearic acid \< 5, a mixture of anatase and rutile phases is obtained. Pure ATO yields anatase phase on decomposition at 400 degrees C. These powders were characterized by X-ray diffraction (XRD), BET surface area measurements and transmission electron microscopy (TEM) studies. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray techniques}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.04.016}, author = {Patil, M. M. and Deshpande, V. V. and Deshpande, S. B. and Samuel, V. and Ravi, V.} } @article { ISI:000237158200003, title = {Phase evolution of NiTiO3 prepared by coprecipitation method}, journal = {Materials Letters}, volume = {60}, number = {15}, year = {2006}, month = {JUL}, pages = {1791-1792}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A simple coprecipitation technique was used for the preparation of NiTiO3 powders. Ammonium carbonate solution was added to a solution mixture containing stoichiometric amounts of Ni(NO3)(2) and TiOCl2 to precipitate nickel as carbonate and titanium as hydroxide under basic conditions. The precipitate was calcined at different temperatures ranging from 100 to 800 degrees C and phase evolution of NiTiO3 was investigated by X-ray diffraction (XRD) studies. It is observed that nickel titanate was formed at 750 degrees C. For comparison, NiTiO3 was also prepared by standard ceramic process. Particle size and morphology was studied by transmission electron microscopy (TEM). (c) 2005 Elsevier B.V. All fights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, NiTiO3, Oxides, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.12.023}, author = {Murugan, A. Vadivel and Samuel, V. and Navale, S. C. and Ravi, V.} } @article { ISI:000246158300001, title = {Coprecipitation technique to prepare CoTa2O6 and CoNb2O6}, journal = {Materials Letter}, volume = {61}, number = {11-12}, year = {2007}, month = {MAY}, pages = {2127-2129}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

An aqueous solution of sodium hydroxide was used to coprecipitate cobalt and tantalum (or niobium) ions from their precursors as hydroxides under basic conditions. This precipitate yielded CoTa2O6 (CT) or CoNb2O6 (CN) ceramics on calcining at 700 degrees C, i.e. at a temperature much lower than 900 degrees C, reported for the formation of these powders prepared by the traditional solid state method. The X-ray diffraction (XRD) studies were employed to investigate phase contents and lattice parameters. The morphology of the synthesized powders was investigated by transmission electron microscopy (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, electronic materials, Oxides, X-ray methods}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.08.024}, author = {Mulla, Imtiaz S. and Natarajan, N. and Gaikwad, A. B. and Samuel, V. and Guptha, U. N. and Ravi, V.} } @article { ISI:000246158300058, title = {Coprecipitation technique to prepare NiNb2O6}, journal = {Materials Letter}, volume = {61}, number = {11-12}, year = {2007}, month = {MAY}, pages = {2354-2355}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A mixture of ammonium carbonate and ammonium hydroxide was used to coprecipitate nickel and niobium ions as nickel carbonate and niobium hydroxide under basic conditions. This precursor yielded NiNb2O6 (NN) ceramics on calcining at 700 degrees C (at a temperature lower than 800 degrees C which is necessary for the formation of NiNb2O6 when prepared by the traditional solid state method). The average particle size and morphology of these powders were investigated by transmission electron microscope (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, Electron microscopy, electronic materials, Oxides, X-ray methods}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.09.010}, author = {Samuel, V. and Gaikwad, A. B. and Jadhav, A. D. and Natarajan, N. and Ravi, V.} } @article { ISI:000245760900020, title = {Low temperature route to prepare LaFeO3 and LaCoO3}, journal = {Materials Letters}, volume = {61}, number = {10}, year = {2007}, month = {APR}, pages = {2030-2032}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A combination of digestion and further low temperature calcination to crystallize the product was employed to prepare LaFeO3 (LF) and LaCoO3 (LC) powders. Freshly co-precipitated lanthanum and ferric (or cobalt) hydroxide gels by sodium hydroxide were allowed to react at 100 degrees C under refluxing and stirring conditions for 4-6 h. These oven dried powders were heated at 450 degrees C to from crystalline LF (or LC) powders. The phase contents and lattice parameters were investigated by X-ray diffraction (XRD). Transmission electron microscope (TEM) investigations were carried out to examine the morphology and average particle size of these powders. (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, LaFeO3, Precipitation, transmission electron microscopy, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.08.009}, author = {Jadhav, A. D. and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000243164000035, title = {Novel technique to prepare LiNbO3 at low temperature}, journal = {Materials Letter}, volume = {61}, number = {3}, year = {2007}, month = {FEB}, pages = {765-766}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Fresh niobium hydroxide was first precipitated from NbF5 solution using an aqueous ammonium hydroxide under basic conditions. Then a simple procedure of mixing lithium and niobium hydroxides together and heating at a low temperature (400 degrees C) produced pure ultrafine single phase LiNbO3 (LN). In the literature, this is the lowest temperature so far reported on the formation of LN. The phase content and lattice parameters are determined by X-ray diffraction (XRD). The average particle size and morphology were studied by transmission electron microscopy (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, Electron microscopy, electronic materials, LiNbO3, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.05.056}, author = {Samuel, V. and Gaikwad, A. B. and Jadhav, A. D. and Mirji, S. A. and Ravi, V.} } @article { ISI:000246260000011, title = {Preparation of nanocrystalline ferroelectric CaBi4Ti4O15 by citrate gel method}, journal = {Ceramics International}, volume = {33}, number = {4}, year = {2007}, month = {JAN}, pages = {569-571}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A gel was formed when an aqueous solution of CaCl2, BiNO3, TiOCl2 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 700 degrees C produced nano crystallites of the ternary oxide, CaBi4Ti4O15 (CBT). The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). The room temperature dielectric constant at 1 kHz is 390. The ferroelectric hysteresis loop parameters of these samples were also studied by a home-built Sawyer-tower circuit. (c) 2006 Elsevier Ltd and Techna Group S.H. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray methods}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2005.11.006}, author = {Murugan, A. Vadivel and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000254698300035, title = {Co-precipitation method for preparation of Bi3TiNbO9 powders}, journal = {Ceramics International}, volume = {34}, number = {3}, year = {2008}, month = {APR}, pages = {675-677}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A simple co-precipitation technique has been successfully used for the preparation of pure, ultrafine, single phase Bi3TiNbO9 (BTN). An aqueous ammonium hydroxide solution was used to simultaneously precipitate Bi3+, Ti4+ and Nb5+, cations as hydroxides under basic conditions (pH similar to 9). No pyrochlore phase was found while heating powder at 500 degrees C and pure BTN phase was found to be formed by X-ray diffraction (XRD). For comparison, BTN samples were also synthesized by the traditional solid state method. The sequence of phase formation in both cases were investigated by XRD studies. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, Oxides, XRD}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2007.02.002}, author = {Gupta, U. N. and Samuel, V. and Muthurajan, H. and Kumar, H. H. and Patil, S. D. and Ravi, V.} } @article { ISI:000257538200034, title = {Co-precipitation technique to prepare BiNbO4 powders}, journal = {Ceramics International}, volume = {34}, number = {6}, year = {2008}, month = {AUG}, pages = {1565-1567}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A simple co-precipitation technique was successfully used for the preparation of pure ultrafine single phase BiNbO4. A standard ammonium hydroxide solution was used to precipitate Bi3+ and Ta5+ cations as hydroxides simultaneously under basic conditions. For comparison, BN powders were also prepared by the traditional solid-state method. It is observed that the co-precipitation technique produces BiNbO4 on heating at 600 degrees C, whereas complete phase formation occurs only at 800 degrees C in the solid-state method. The phase contents and lattice parameters were Studied by powder X-ray diffraction (XRD). (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {BiNbO4, Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray diffraction}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2007.03.022}, author = {Radha, R. and Gupta, U. N. and Samuel, V. and Muthurajan, H. and Kumar, H. H. and Ravi, V.} }