@article { ISI:000238866300004, title = {Coprecipitation technique to prepare Sr0.5Ba0.5Nb2O6}, journal = {Bulletin of Materials Science}, volume = {29}, number = {3}, year = {2006}, month = {JUN}, pages = {221-223}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

An aqueous mixture of ammonium oxalate and ammonium hydroxide was used to coprecipitate barium and strontium ions as oxalates and niobium ions as hydroxide under basic conditions. This precursor on calcining at 750 degrees C yielded Sr0.5Ba0.5Nb2O6 phase. This is a much lower temperature than that prepared by traditional solid state method (1000 degrees C) as reported for the formation of Sr0.5Ba0.5Nb2O6 (SBN). Transmission electron microscopic (TEM) investigations revealed that the average particle size was 80 nm for the calcined powders. The room temperature dielectric constant at I kHz was found to be 1100. The ferroelectric hysteresis loop parameters of these samples were also studied.

}, keywords = {Ceramics, Electron microscopy, ferroelectricity, Oxides, X-ray diffraction}, issn = {0250-4707}, doi = {10.1007/BF02706488}, author = {Murugan, A. Vadivel and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000237158200003, title = {Phase evolution of NiTiO3 prepared by coprecipitation method}, journal = {Materials Letters}, volume = {60}, number = {15}, year = {2006}, month = {JUL}, pages = {1791-1792}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A simple coprecipitation technique was used for the preparation of NiTiO3 powders. Ammonium carbonate solution was added to a solution mixture containing stoichiometric amounts of Ni(NO3)(2) and TiOCl2 to precipitate nickel as carbonate and titanium as hydroxide under basic conditions. The precipitate was calcined at different temperatures ranging from 100 to 800 degrees C and phase evolution of NiTiO3 was investigated by X-ray diffraction (XRD) studies. It is observed that nickel titanate was formed at 750 degrees C. For comparison, NiTiO3 was also prepared by standard ceramic process. Particle size and morphology was studied by transmission electron microscopy (TEM). (c) 2005 Elsevier B.V. All fights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, NiTiO3, Oxides, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.12.023}, author = {Murugan, A. Vadivel and Samuel, V. and Navale, S. C. and Ravi, V.} } @article { ISI:000245760900020, title = {Low temperature route to prepare LaFeO3 and LaCoO3}, journal = {Materials Letters}, volume = {61}, number = {10}, year = {2007}, month = {APR}, pages = {2030-2032}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A combination of digestion and further low temperature calcination to crystallize the product was employed to prepare LaFeO3 (LF) and LaCoO3 (LC) powders. Freshly co-precipitated lanthanum and ferric (or cobalt) hydroxide gels by sodium hydroxide were allowed to react at 100 degrees C under refluxing and stirring conditions for 4-6 h. These oven dried powders were heated at 450 degrees C to from crystalline LF (or LC) powders. The phase contents and lattice parameters were investigated by X-ray diffraction (XRD). Transmission electron microscope (TEM) investigations were carried out to examine the morphology and average particle size of these powders. (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, LaFeO3, Precipitation, transmission electron microscopy, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.08.009}, author = {Jadhav, A. D. and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000243164000035, title = {Novel technique to prepare LiNbO3 at low temperature}, journal = {Materials Letter}, volume = {61}, number = {3}, year = {2007}, month = {FEB}, pages = {765-766}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Fresh niobium hydroxide was first precipitated from NbF5 solution using an aqueous ammonium hydroxide under basic conditions. Then a simple procedure of mixing lithium and niobium hydroxides together and heating at a low temperature (400 degrees C) produced pure ultrafine single phase LiNbO3 (LN). In the literature, this is the lowest temperature so far reported on the formation of LN. The phase content and lattice parameters are determined by X-ray diffraction (XRD). The average particle size and morphology were studied by transmission electron microscopy (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, Electron microscopy, electronic materials, LiNbO3, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.05.056}, author = {Samuel, V. and Gaikwad, A. B. and Jadhav, A. D. and Mirji, S. A. and Ravi, V.} } @article { ISI:000257538200034, title = {Co-precipitation technique to prepare BiNbO4 powders}, journal = {Ceramics International}, volume = {34}, number = {6}, year = {2008}, month = {AUG}, pages = {1565-1567}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A simple co-precipitation technique was successfully used for the preparation of pure ultrafine single phase BiNbO4. A standard ammonium hydroxide solution was used to precipitate Bi3+ and Ta5+ cations as hydroxides simultaneously under basic conditions. For comparison, BN powders were also prepared by the traditional solid-state method. It is observed that the co-precipitation technique produces BiNbO4 on heating at 600 degrees C, whereas complete phase formation occurs only at 800 degrees C in the solid-state method. The phase contents and lattice parameters were Studied by powder X-ray diffraction (XRD). (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {BiNbO4, Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray diffraction}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2007.03.022}, author = {Radha, R. and Gupta, U. N. and Samuel, V. and Muthurajan, H. and Kumar, H. H. and Ravi, V.} }