@article { ISI:000276284200019,
	title = {Synthesis and characterization of polyamides containing pendant pentadecyl chains},
	journal = {European Polymer Journal},
	volume = {46},
	number = {3},
	year = {2010},
	month = {MAR},
	pages = {557-567},
	publisher = {PERGAMON-ELSEVIER SCIENCE LTD},
	address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND},
	abstract = {<p>A new aromatic diacid monomer viz., 4-(4{\textquoteright}-carboxyphenoxy)-2-pentadecylbenzoic acid was synthesized starting from cardanol and was characterized by FTIR, (1)H- and (13)C NMR spectroscopy. A series of new aromatic polyamides containing ether linkages and pendant pentadecyl chains was prepared by phosphorylation polycondensation of 4-(4{\textquoteright}-carboxyphenoxy)-2-pentadecylbenzoic acid with five commercially available aromatic diamines viz., 1,4-phenylenediamine, 4,4{\textquoteright}-oxydianiline, 4,4{\textquoteright}-methylenedianiline, 1,3-phenylenediamine, and 4,4{\textquoteright}-(hexafluoroisopropylidene)dianiline. Inherent viscosities of the polyamides were in the range 0.45-0.66 dL/g in N,N-dimethylacetamide at 30 +/- 0.1 degrees C. The introduction of ether linkages and pendant pentadecyl chains into polyamides led to an enhanced solubility in N,N-dimethylacetamide and 1-methyl-2-pyrrolidinone at room temperature or upon heating. The polyamides could be solution-cast into tough, flexible and transparent films from their N,N-dimethylacetamide solution. Wide angle X-ray diffraction patterns exhibited broad halo indicating that the polymers were essentially amorphous in nature. X-Ray diffractograms also displayed a diffuse to sharp reflection in the small-angle region (20 = similar to 2-5 degrees) for the polyamides characteristics of formation of loosely to well-developed layered structure arising from packing of flexible pentadecyl chains. The glass transition temperature observed for the polyamides was in range 139-189 degrees C. The temperature at 10\% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of the polyamides was in the range 425-453 degrees C indicating their good thermal stability. (C) 2009 Elsevier Ltd. All rights reserved.</p>},
	keywords = {alkyl side-chain, Cardanol, Cashew nut shell liquid, Pentadecyl chains, polyamides},
	issn = {0014-3057},
	doi = {10.1016/j.eurpolymj.2009.11.014},
	author = {More, Arvind S. and Pasale, Sharad K. and Wadgaonkar, Prakash P.}
}
@article { ISI:000291613900071,
	title = {Synthesis and characterization of organo-soluble poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing pendant pentadecyl chains},
	journal = {Journal of Applied Polymer Science},
	volume = {121},
	number = {6},
	year = {2011},
	month = {SEP},
	pages = {3689-3695},
	publisher = {WILEY-BLACKWELL},
	address = {111 RIVER ST, HOBOKEN 07030-5774, NJ USA},
	abstract = {<p>Poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant pentadecyl chains were synthesized by polycondensation of each of the two bisphenol monomers viz, 1,1,1-[bis(4-hydroxyphenyl)-4{\textquoteright}-pentadecylphenyl] ethane and 1,1-bis(4-hydroxyphenyl)-3-pentadecyl cyclohexane with activated aromatic dihalides namely, 4,4{\textquoteright}-difluorobenzophenone, and 1,3-bis(4-fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene, in the presence of anhydrous potassium carbonate. Polymers were isolated as white fibrous materials with inherent viscosities and number average molecular weights in the range 0.70-1.27 dL g(-1) and 76,620-1,36,720, respectively. Poly(ether ether ketone) s and poly(ether ether ketone ketone) s were found to be soluble at room temperature in organic solvents such as chloroform, dichloromethane, tetrahydrofuran, and pyridine and could be cast into tough, transparent, and flexible films from their solutions in chloroform. Wide angle X-ray diffraction patterns exhibited a broad halo at around 2 theta = similar to 19 degrees indicating that the polymers containing pentadecyl chains were amorphous in nature. In the small-angle region, diffuse reflections of a typically layered structures resulting from the packing of pentadecyl side chains were observed. The temperature at 10\% weight loss, obtained from TG curves, for poly(ether ether ketone) s and poly(ether ether ketone ketone) s were in the range 416-459 degrees C, indicating their good thermal stability. A substantial drop in glass transition temperatures (68-78 degrees C) was observed for poly(ether ether ketone) s and poly(ether ether ketone ketone) s due to {\textquoteleft}{\textquoteleft}internal plasticization{\textquoteright}{\textquoteright} effect of flexible pendant pentadecyl chains. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 121: 3689-3695, 2011</p>},
	keywords = {alkyl side-chain, Cashew nut shell liquid, CNSL, pentadecyl, poly(arylene ether)s, poly(ether ketone)s, polyethers, renewable},
	issn = {0021-8995},
	doi = {10.1002/app.34181},
	author = {More, Arvind S. and Pasale, Sharad K. and Honkhambe, Pandurang N. and Wadgaonkar, Prakash P.}
}