@article {48157,
	title = {Morphology-tuned Pt3Ge accelerates water dissociation to industrial-standard hydrogen production over a wide pH range},
	journal = {Advanced Materials},
	volume = {34},
	year = {2022},
	month = {JUL},
	pages = {2202294},
	type = {Article},
	abstract = {<p>
	The discovery of novel materials for industrial-standard hydrogen production is the present need considering the global energy infrastructure. A novel electrocatalyst, Pt3Ge, which is engineered with a desired crystallographic facet (202), accelerates hydrogen production by water electrolysis, and records industrially desired operational stability compared to the commercial catalyst platinum is introduced. Pt3Ge-(202) exhibits low overpotential of 21.7 mV (24.6 mV for Pt/C) and 92 mV for 10 and 200 mA cm(-2) current density, respectively in 0.5 m H2SO4. It also exhibits remarkable stability of 15 000 accelerated degradation tests cycles (5000 for Pt/C) and exceptional durability of 500 h (@10 mA cm(-2)) in acidic media. Pt3Ge-(202) also displays low overpotential of 96 mV for 10 mA cm(-2) current density in the alkaline medium, rationalizing its hydrogen production ability over a wide pH range required commercial operations. Long-term durability (\&gt;75 h in alkaline media) with the industrial level current density (\&gt;500 mA cm(-2)) has been demonstrated by utilizing the electrochemical flow reactor. The driving force behind this stupendous performance of Pt3Ge-(202) has been envisaged by mapping the reaction mechanism, active sites, and charge-transfer kinetics via controlled electrochemical experiments, ex situ X-ray photoelectron spectroscopy, in situ infrared spectroscopy, and in situ X-ray absorption spectroscopy further corroborated by first principles calculations.</p>
},
	keywords = {Electrochemistry, hydrogen production, intermetallics, water electrolysis},
	issn = {0935-9648},
	doi = {10.1002/adma.202202294},
	author = {Mondal, Soumi and Sarkar, Shreya and Bagchi, Debabrata and Das, Tisita and Das, Risov and Singh, Ashutosh Kumar and Prasanna, Ponnappa Kechanda and Vinod, C. P. and Chakraborty, Sudip and Peter, Sebastian C.}
}
@article {48088,
	title = {Structure-tailored surface oxide on Cu-Ga intermetallics enhances CO2 reduction selectivity to methanol at ultralow potential},
	journal = {Advanced Materials},
	volume = {34},
	year = {2022},
	month = {MAY},
	pages = {2109426},
	type = {Article},
	abstract = {<p>
	Electrochemical CO2 reduction reaction (eCO(2)RR) is performed on two intermetallic compounds formed by copper and gallium metals (CuGa2 and Cu9Ga4). Among them, CuGa2 selectively converts CO2 to methanol with remarkable Faradaic efficiency of 77.26\% at an extremely low potential of -0.3 V vs RHE. The high performance of CuGa2 compared to Cu9Ga4 is driven by its unique 2D structure, which retains surface and subsurface oxide species (Ga2O3) even in the reduction atmosphere. The Ga2O3 species is mapped by X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) techniques and electrochemical measurements. The eCO(2)RR selectivity to methanol are decreased at higher potential due to the lattice expansion caused by the reduction of the Ga2O3, which is probed by in situ XAFS, quasi in situ powder X-ray diffraction, and ex situ XPS measurements. The mechanism of the formation of methanol is visualized by in situ infrared (IR) spectroscopy and the source of the carbon of methanol at the molecular level is confirmed from the isotope-labeling experiments in presence of (CO2)-C-13. Finally, to minimize the mass transport limitations and improve the overall eCO(2)RR performance, a poly(tetrafluoroethylene)-based gas diffusion electrode is used in the flow cell configuration.</p>
},
	keywords = {(2) reduction, CO, Electrochemistry, Methanol},
	issn = {0935-9648},
	doi = {10.1002/adma.202109426},
	author = {Bagchi, Debabrata and Raj, Jithu and Singh, Ashutosh Kumar and Cherevotan, Arjun and Roy, Soumyabrata and Manoj, Kaja Sai and Vinod, C. P. and Peter, Sebastian C.}
}