@article { ISI:000241306000020, title = {Characterization of nanosized NiZn ferrite powders synthesized by an autocombustion method}, journal = {Materials Chemistry and Physics}, volume = {100}, number = {1}, year = {2006}, month = {NOV}, pages = {98-101}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Nanocrystalline Ni0.5Zn0.5Fe2O4 with average particle size of similar to 9 nm has been synthesized by an autocombustion method and characterized by powder XRD, TEM and room temperature magnetic measurements. High room temperature magnetization comparable to that of the bulk material is obtained for the nanosized powders annealed at 800 degrees C, with a maximum particle size of similar to 54 nm. The results show that optimum properties can be achieved for NiZn ferrite powders synthesized by the present autocombustion method and processed at relatively lower temperatures. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, Magnetic materials, magnetic properties, Oxides}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.12.012}, author = {Deka, Sasanka and Joy, Pattayil Alias} } @article {43899, title = {Copper Cobalt Sulfide Nanosheets Realizing a Promising Electrocatalytic Oxygen Evolution Reaction}, journal = {ACS Catalysis}, volume = {7}, year = {2017}, month = {SEP}, chapter = {5871-5879}, abstract = {

Nanostructured CuCo2S4, a mixed metal thiospinel, is found to be a benchmark electrocatalyst for oxygen evolution reaction (OER) in this study with a low overpotential, a low Tafel slope, a high durability, and a high turnover frequency (TOF) at lower mass loadings. Nanosheets of CuCo2S4 are realized from a hydrothermal synthesis method in which the average thickness of the sheets is found to be in the range of 815 nm. Aggregated nanosheets form a highly open hierarchical structure. When used as an electrocatalyst, CuCo2S4 nanosheets offer an overpotential value of 310 mV at a 10 mA cm(2) current density, which remains consistent for 10000 measured cycles in a 1 M KOH electrolyte. A chronoamperometric study reveals constant oxygen evolution for 12 h at a 10 mV s(-1) scan rate without any degradation of the activity. Furthermore, the calculated mass activity of the CuCo2S4 electrocatalyst is found to be 14.29 A/g and to afford a TOF value of 0.1431 s(-1) at 310 mV at a mass loading of 0.7 mg cm(-2). For comparison, nanostructures of Co3S4 and Cu0.5Co2.5S4 have been synthesized using a similar method followed for CuCo2S4. When compared to the OER activities among these three thiospinels and standard IrO2, CuCo2S4 nanosheets offered the highest OER activities at the same mass loading (0.7 mg/cm(-2)). Extensive X-ray photoelectron spectroscopy and electron paramagnetic resonance analyses for a mechanistic study reveal that introduction of Cu into the Co3S4 lattice enhances the oxygen evolution and kinetics by offering Cu2+ sites for utilitarian adsorption of OH, O, and OOH reactive species and also by offering a highly active high-spin state of octahedral Co3+ for OER catalysis.

}, keywords = {Bifunctional Electrocatalyst, Catalyst, Cuco2s4, Efficient Electrocatalyst, electrocatalyst, Electronic-structure, Nanoparticles, Nanosheet, oxide, oxygen evolution, performance, Recent Progress, Water oxidation, Water Splitting Hydrogen Evolution}, doi = { 10.1021/acscatal.7b01831}, author = {Chauhan, Meenakshi and Reddy, Kasala Prabhakar and Gopinath, Chinnakonda S. and Deka, Sasanka} }