@article { ISI:000298175400132,
	title = {Novel synthesis of nano-calcium carbonate (CaCO3)/polystyrene (PS) core-shell nanoparticles by atomized microemulsion technique and its effect on properties of polypropylene (PP) composites},
	journal = {Polymers for Advanced Technologies},
	volume = {22},
	number = {12},
	year = {2011},
	month = {DEC},
	pages = {2571-2582},
	publisher = {WILEY-BLACKWELL},
	address = {111 RIVER ST, HOBOKEN 07030-5774, NJ USA},
	abstract = {<p>Calcium carbonate (CaCO3)/polystyrene (PS) nanoparticles (\&lt; 100 nm) with core-shell structure were synthesized by atomized microemulsion technique. The polymer chains were anchored onto the surface of nano-CaCO3 through triethoxyvinyl silane (TEVS) as a coupling agent. Ammonium persulfate (APS), sodium dodecyl sulfate (SDS) and n-pentanol were used as initiator, surfactant, and cosurfactant, respectively. Polymerization mechanism of core-shell latex particles was discussed. Encapsulation of nano-CaCO3 by PS was confirmed by using transmission electron microscope (TEM). Grafting percentage of core-shell particles was investigated by Thermogravimetric Analyzer (TGA). Nano-CaCO3/PS core-shell particles were characterized by Fourier transform infrared (FTIR) spectrophotometer and differential scanning calorimeter (DSC). The results of FTIR revealed existence of a strong interaction at the interface of nano-CaCO3 particle and PS, which implies that the polymer chains were successfully grafted onto the surface of nano-CaCO3 particle through the link of the coupling agent. In addition, TGA and DSC results indicated an enhancement of thermal stability of core-shell materials compared with the pure nano-PS. Nano-CaCO3/PS particles were blended with polypropylene (PP) matrix on Brabender Plastograph by melt process with different wt\% of loading (i.e. 0.1-1 wt\%). The interfacial adhesion between nano-CaCO3 particles and PP matrix was significantly improved when the nano-CaCO3 particles were grafted with PS, which led to increased thermal, rheological, and mechanical properties of (nano-CaCO3/PS)/PP composites. Scanning electron microscope (SEM) and atomic force microscope (AFM) images showed a perfect dispersion of the nano-CaCO3 particles in PP matrix. Copyright (C) 2011 John Wiley \&amp; Sons, Ltd.</p>},
	keywords = {atomized microemulsion, core-shell nanoparticles, mechanical properties, polypropylene (PP), Rheological properties, Thermal properties},
	issn = {1042-7147},
	doi = {10.1002/pat.1802},
	author = {Mishra, Satyendra and Chatterjee, Aniruddha and Singh, RajPal}
}