@article { ISI:000230375200016, title = {Synthesis of fine PbE (E = S, Se) powder from direct in situ reduction of sulphur or selenium}, journal = {Materials Chemistry and Physics}, volume = {93}, number = {1}, year = {2005}, month = {SEP}, pages = {91-94}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Lead sulphide and lead selenide have been prepared for the first time, by in situ reduction of elemental S or Se by using aqueous DMF or aqueous SFS as reducing agents and their reaction with lead acetate. The grayish-black powder has been characterized by powder XRD measurement, XPS and SEM/EDAX analysis. Powder X-ray diffraction pattern revealed that cubic PbE (E = S, Se) is formed with a little impurities of lead in case of PbSe. Slightly broader peaks in XRD measurement suggest small particles diameter in the powder. The particle size by using Scheffer{\textquoteright}s formula is found to be about 100 nm. Peaks due to free lead particles are observed in XPS and EDS (in case of PbSe) analysis and SEM analysis indicates agglomerated particles. (c) 2005 Elsevier B.V All rights reserved.

}, keywords = {Chemical synthesis, electronic materials, reduction, Semiconductor}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.02.025}, author = {Khanna, P. K. and Subbarao, VVVS and Wagh, M. and Jadhav, P. and Patil, K. R.} } @article { ISI:000238050700006, title = {Synthesis of beta-Ag2Se from organo-selenium precursor and silver nitrate in DMF via simultaneous reduction of selenium and silver salt}, journal = {Materials Letters}, volume = {60}, number = {17-18}, year = {2006}, month = {AUG}, pages = {2080-2085}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Reaction of selenium powder and silver nitrate in aqueous N,N{\textquoteright}-dimethylformamide (aq. DMF) leads to formation of silver selenide. Similar reaction with cycloalkeno-1,2,3-selenadiazole an organic compound of selenium upon thermolysis, also produces silver selenide. It is believed that DMF activates selenium and reduces silver salt via in-situ generated hydrogen ion simultaneously. Slightly broadened X-ray diffraction pattern for pure beta silver selenide (beta-Ag2Se) was observed. Scanning electron microscopy (SEM) indicated that the agglomerated particles could be in the range of about 100 to 200 nm in dimension. EDAX analysis showed non-stoichiometric elemental ratio between silver and selenium. It is found that the weight percent of Ag is slightly higher than Se. However, free amorphous selenium is also detected by XPS analysis when the product is made by use of elemental selenium. Thermal analysis (TGA) revealed a small (4\%) weight loss due to the presence of organics or the solvent from the reaction medium. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, nano powder, noble metal chalcogenides, Semiconductor}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.12.079}, author = {Khanna, P. K. and Singh, N. and Charan, Shobhit and Patil, K. R.} } @article { ISI:000256114400005, title = {Synthesis of oleic acid capped copper nano-particles via reduction of copper salt by SFS}, journal = {Materials Chemistry and Physics}, volume = {110}, number = {1}, year = {2008}, month = {JUL}, pages = {21-25}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Synthesis of oleic acid capped copper nano-particles has been carried out by use of sodium formaldehyde sulfoxylate (SFS) in aqueous medium. Nano-copper can be effectively coated with polyvinyl alcohol (PVA). Phase-pure nano-Cu can be obtained when water/acetone was used as aqueous medium. It is observed that the surface plasmon resonance (SPR) phenomena can be controlled during synthesis by the use of suitable reagent system, e.g. absorption band in presence of PVA can be blue shifted. As-prepared copper nano-particles were characterized by X-ray diffraction measurements (XRD), Scanning electron microscopy (SEM), energy dispersive analysis of X-rays (EDAX), thermo gravimetric analysis (TGA) and Fourier transform infra-red spectroscopy (FTIR). XRD analysis revealed broad pattern for fcc crystal structure of copper metal. The particle size by use of Scherrer{\textquoteright}s equation was calculated to be about 20 nm. TGA revealed similar to 10\% weight loss due to the presence of surfactant. FTIR spectroscopy confirmed the presence of oleic acid around the particles. (c) 2008 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, electronic materials, metals, Nanostructure}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2008.01.013}, author = {Khanna, P. K. and Kale, Trupti S. and Shaikh, Mushtaq and Rao, N. Koteswar and Satyanarayana, C. V. V.} } @article { ISI:000262987800024, title = {Solid state synthesis and room temperature magnetic properties of iron phosphide nanoparticles}, journal = {Journal of Nanoparticle Research}, volume = {11}, number = {2}, year = {2009}, month = {FEB}, pages = {491-497}, publisher = {SPRINGER}, address = {VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS}, abstract = {

Room temperature magnetic properties have been achieved for nano-crystalline iron phosphide synthesized from the direct solid state reaction of iron chloride and tri-octylphosphine (TOP). The magnetization continuously increased with higher magnetic fields, indicating a super-paramagnetic behavior. It is observed that room temperature magnetism is possible for the material showing antiferromagnetic nature at low temperatures. In the present synthesis, TOP acted as a source of phosphorus as well as a surfactant. X-ray diffraction (XRD) studies revealed that the black powder is a mixture of FeP and Fe(2)P. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) showed elongated as well spherical particles. Energy dispersion X-ray analysis (EDAX) confirmed a non-stoichiometric iron phosphide. Presence of TOP was confirmed by infra-red (IR) spectroscopy, and thermo-gravimetric analysis (TGA) indicated about 6\% wt. loss due to presence of organics.

}, keywords = {Iron phosphide, Semiconductors, Solid state reaction, synthesis, XRD}, issn = {1388-0764}, doi = {10.1007/s11051-008-9458-0}, author = {Singh, N. and Khanna, P. K. and Joy, Pattayil Alias} } @article { ISI:000305039700151, title = {Sono-chemical synthesis of ZnO nano-particles and their application in hydrogen sulphide gas sensing}, journal = {Journal of Nanoscience and Nanotechnology}, volume = {12}, number = {3}, year = {2012}, month = {MAR}, pages = {2791-2796}, publisher = {AMER SCIENTIFIC PUBLISHERS}, address = {26650 THE OLD RD, STE 208, VALENCIA, CA 91381-0751 USA}, abstract = {

Herein we describe synthesis of ZnO nanoparticles by using alkaline solution of ZnX2 (X = NO3, Cl) under ultrasound energy of 20 KHz. The reaction can be completed in about 1-2 hours. As prepared powders were analyzed by XRD measurement to find that the product is hexagonal phase pure ZnO. UV-Visible measurement of aq. solution showed absorption band at similar to 365 nm and photoluminescence (PL) indicated multiple bands in visible region due to deep traps owing to high temperature sintering. The hydrophilicity can be imparted by use of a suitable polyelectrolyte. Freshly prepared samples showed good dispersion in aqueous and alcoholic medium. The thick films derived from the ZnO nano-particles showed excellent sensing for hydrogen sulphide gas.

}, keywords = {Gas-Sensing, Sono-Chemical, synthesis, ZnO Nano-Particles}, issn = {1533-4880}, doi = {10.1166/jnn.2012.5732}, author = {Khanna, P. K. and Kate, Kunal and Dhanabalan, K. and Banerjee, Shaibal and Reji, Nedunnkandathil and Shinde, S. D. and Jain, G. H.} }