@article { ISI:000309370500015, title = {Carbon dioxide reforming of methane over ruthenium substituted strontium titanate perovskite catalysts}, journal = {Indian Journal of Chemistry Section A-Inorganic Bio-Inorganic Physical Theoretical \& Analytical Chemistry}, volume = {51}, number = {9-10, SI}, year = {2012}, month = {SEP}, pages = {1339-1347}, publisher = {NATL INST SCIENCE COMMUNICATION-NISCAIR}, address = {DR K S KRISHNAN MARG, PUSA CAMPUS, NEW DELHI 110 012, INDIA}, abstract = {

Strontium titanate (SrTiO3) doped with varying amounts of ruthenium (7.9, 15.6 and 31 wt\%) have been prepared by the citrate gel synthesis method. Structural and textural characterizations reveal that at lower concentrations, a major part of Ru is incorporated in the lattice of SiTiO3. The content of surface Ru (outside lattice) increases with increasing amounts of the doped Ru. The surface Ru reduced at lower temperatures compared to Ru incorporated into the lattice. The reduction of the lattice substituted Ru occurs only at temperatures above the collapse of the perovskite structure. The catalyst sample with 7.9 wt\% of Ru shows good conversions in the dry reforming of methane with CO2. The conversion of CO2 is in excess compared to methane under the studied reaction conditions. As a result, H-2/CO ratio of the product gases which should have been equivalent to unity is lower than the stoichiometric value. This ratio is particularly low when lower reaction temperatures (873-973 K) were used. Similar was the case when high space velocities were used. Low methane conversion and reverse water gas shift reaction are the causes for the low H-2/CO ratios.

}, keywords = {Carbon dioxide reforming, Catalysts, Citrate gel method, Doped catalysts, Dry reforming, Methane reforming, Perovskites, Reverse water gas shift, Ruthenium doped catalysts, Strontium titanate, Syngas}, issn = {0376-4710}, author = {Gurav, Hanmant R. and Bobade, Richa and Das, Vineetha Lakshmi and Chilukuri, Satyanarayana V.} } @article { ISI:000380362700025, title = {Highly efficient nitrogen-doped hierarchically porous carbon supported Ni nanoparticles for the selective hydrogenation of furfural to furfuryl alcohol}, journal = {RSC Advances}, volume = {6}, number = {72}, year = {2016}, month = {JUL}, pages = {67662-67668}, publisher = {ROYAL SOC CHEMISTRY}, address = {THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND}, abstract = {

Nickel nanoparticles supported on nitrogen doped hierarchically porous carbon (Ni/CN) are found to be highly efficient and reusable catalysts for the selective hydrogenation of biomass-derived furfural to furfuryl alcohol (FA). Various characterization methods were used to study the structural and morphological features of the catalysts. Furfural conversion of 96\% and 95\% FA selectivity was obtained using a 5 wt\% Ni/CN catalyst. This catalyst showed excellent recyclability without any loss in activity and FA selectivity when it was reused four times. The higher catalytic performance is attributed to the nitrogen incorporated hierarchical porous 3D carbon network.

}, issn = {2046-2069}, doi = {10.1039/c6ra14078e}, author = {Kotbagi, Trupti V. and Gurav, Hanmant R. and Nagpure, Atul S. and Chilukuri, Satyanarayana V. and Bakker, Martin G.} } @article {43857, title = {Influence of preparation method on activity and stability of Ni catalysts supported on Gd doped ceria in dry reforming of methane}, journal = {Journal of CO2 Utilization}, volume = {20}, year = {2017}, month = {JUL}, pages = {357-367}, type = {Article}, abstract = {Nickel catalysts supported on Gd doped ceria (NGDC), with various Ni content, were prepared through different preparation routes and evaluated for dry reforming of methane (DRM). Their detailed characterization revealed that method of preparation plays an important role in Ni dispersion, with catalysts prepared through co-precipitation showing high Ni dispersion. The co-precipitated 12NGDC-cp catalyst with 12 wt\% NiO was found to be superior in terms of high CO2 and CH4 conversions compared to catalysts prepared through citrate gel or impregnation methods Even H-2 and CO yields are high on this catalyst, while it shows excellent durability with stable activity even after 100 h on-stream. Thermogravimetric analysis of spent catalyst showed presence of coke, with transmission electron microscopic studies pointing to the presence of Ni crystallites at the mouth of the carbon whiskers. These Ni crystallites appear to be still active for DRM reaction. Among the spent catalysts, the carbon formation was high on catalysts that have bigger Ni crystallites, with the catalysts prepared through impregnation and citrate gel methods having higher coke. Investigations also reveal that the conversion of active (amorphous) carbon into stable (graphitic) carbon depends on the Ni crystallite size, temperature and duration of the reaction. These studies demonstrate that Gd doped ceria is a good support for Ni, to obtain high DRM activity and very good on-stream stability provided the catalysts are prepared through an appropriate method.}, doi = {10.1016/j.jcou.2017.06.014}, author = {Gurav, Hanmant R. and Dama, Srikanth and Samuel, Violet and Chilukuri, Satyanarayana} } @article {44162, title = {Active and durable alkaline earth metal substituted perovskite catalysts for dry reforming of methane}, journal = {Applied Catalysis B - Environmental}, volume = {224}, year = {2018}, month = {MAY}, pages = {146-158}, type = {Article}, abstract = {Dry reforming of methane is an important process for the utilization of CO2 and to get valuable synthesis gas. Alkaline earth metal substituted MZr1-xNixO3-delta perovskites were synthesized by citrate gel method, characterized and evaluated for dry reforming methane. Characterization results show that the type of alkaline earth substituted at the A site of the perovskite oxide plays an important role in terms of structure, basicity, oxygen deficiency and Ni dispersion. Calcium substituted CaZr0.8Ni0.2O3-delta catalyst shows superior activity in terms of high CH4 and CO2 conversion, while maintaining the activity even after 500 h of reaction. Mechanistic investigations were carried out using transient pulse experiments and insitu FTIR-diffuse reflectance spectroscopy. These experiments reveal that redox property and basicity play important role in activation and sustaining the reforming reaction. Insitu FTIR measurements show that surface hydroxyl groups of the support are vital for high activity and durability of CaZr0.8Ni0.2O3-delta catalyst. XRD and TGA analysis of catalysts after reaction show the structures are retained, but peaks pertaining to coke were observed on SrZr0.8Ni0.2O3-delta and BaZr0.8Ni0.2O3-delta catalysts. On the otherhand, CaZr0.8Ni0.2O3-delta catalyst had only amorphous carbon even after 500 h of reaction. HRTEM studies revealed that SrZr0.8Ni0.2O3-delta and BaZr0.8Ni0.2O3-delta catalysts deactivated mostly due to the formation of carbon nanotubes with Ni embedded in them. Raman and XPS analysis helped in identifying types of coke precursors present on the catalysts. The investigation also illustrate that type of carbon formed depends on the basicity of perovskite oxide, metal to support interaction, Ni crystallite size, surface hydroxyl groups and oxygen defects. This study clearly demonstrated that CaZr0.8Ni0.2O3-delta is an excellent catalyst for dry reforming reaction with long life.}, doi = {10.1016/j.apcatb.2017.10.048}, author = {Dama, Srikanth and Ghodke, Seema R. and Bobade, Richa and Gurav, Hanmant R. and Chilukuri, Satyanarayana} } @article {44568, title = {Spinel-type mixed oxides for stable and selective partial oxidation of benzyl alcohol}, journal = {ChemistrySelect}, volume = {3}, year = {2018}, month = {APR }, pages = {3751-3761}, type = {Article}, abstract = {

Benzaldehyde is an important chemical intermediate, which need to be prepared through an eco-friendly process. Manganese oxides are active as catalysts for its preparation through partial oxidation of benzyl alcohol. In this study, Cu, Co and Mn containing spinel based mixed oxides (CuxMn3-xO4) were prepared and tested for partial oxidation of benzyl alcohol to get benzaldehyde with high selectivity. The catalytic activity strongly depended on chemical composition, acid-base properties and oxygen uptake. The influence of chemical composition, reaction temperature, oxygen partial pressure and the weight hourly space velocity (WHSV) were investigated to optimize benzaldehyde yield and to stabilize the catalyst activity. A high benzaldehyde selectivity of 98\%, accompanied with benzyl alcohol conversion of 84.5\% was obtained over Cu0.25Mn2.75O4 catalyst at 300 {\textdegree}C. It was evident from temperature programmed desorption (TPD) of CO2 that this catalyst was found to have optimum basicity and high oxygen uptake, thus imparting high activity and stability. Activity and catalyst life could be attributed to appropriate acid-base properties. Supporting Information

}, issn = {23656549}, doi = {10.1002/slct.201800321}, author = {Gurrala, Lakshmiprasad and Nagpure, Atul S. and Gurav, Hanmant R. and Chilukur, Satyanarayana} }