@article { ISI:000250410500033, title = {Synthesis and characterization of new aromatic polyesters containing biphenyl side groups}, journal = {Journal of Applied Polymer Science}, volume = {106}, number = {5}, year = {2007}, month = {DEC}, pages = {3105-3110}, publisher = {JOHN WILEY \& SONS INC}, type = {Article}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

Aromatic polyesters containing biphenyl side groups were synthesized by phase-transfer catalyzed interfacial polycondensation of 1-(4-biphenylyl)-1,1-bis(4-hydroxyphenyl) ethane (BBHPE) with terephthaloyl chloride (TPC), isophthaloyl chloride (IPC), and a mixture of TPC/IPC (50: 50 mol ratio). Copolyesters were synthesized by utilizing different molar proportions of BBHPE and 4,4-isopropylidenediphenol (BPA) with IPC and TPC. The inherent viscosities of polyesters were in the range 0.44-1.26 dL/g. All the polyesters were soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, meta-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetamide, and 1-methyl-2-pyrrolidmone. Tough, transparent, and flexible films could be cast from chloroform solutions of these polyesters. WAXD measurements indicated that all the polyesters and copolyesters were amorphous in nature. Glass transition temperature of polyesters were in the range 198-256 degrees C, while the initial degradation temperature of polyesters were in the range 444-481 degrees C. Copolyesters derived from BBHPE exhibited improved solubility and higher glass transition temperatures compared to the corresponding polyesters based on BPA. (c) 2007 Wiley Periodicals, Inc.

}, keywords = {Aromatic polyesters, biphenyl side groups}, issn = {0021-8995}, doi = {10.1002/app.25862}, author = {Honkhambe, Pandurang N. and Avadhani, C. V. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000279996500008, title = {Synthesis and characterization of new aromatic polyesters containing pendent naphthyl units}, journal = {Journal of Applied Polymer Science}, volume = {117}, number = {5}, year = {2010}, month = {SEP}, pages = {2545-2552}, publisher = {JOHN WILEY \& SONS INC}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

Two bisphenols, viz., 4,4{\textquoteright}-[1-(2-naphthaleny-1)ethylidene]bisphenol and 4,4{\textquoteright}-[1-(2-naphthalenyl) ethylidene]bis-3-methylphenol were prepared by condensation of commercially available 2-acetonaphthanone with phenol and o-cresol, respectively. A series of new aromatic polyesters containing pendent naphthyl units was synthesized by phase-transfer-catalyzed interfacial polycondensation of these bisphenols with isophthaloyl chloride, terephthaloyl chloride, and a mixture of isophthaloyl chlorideiterephthaloyl chloride (50 : 50 mol \%). Inherent viscosities of polyesters were in the range 0.83-1.76 dL g(-1), while number average molecular weights (M(n)) were in the range 61,000-235,000 g mol(-1). Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, m-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetarnide, and 1-methyl-2-pyrrolidinone at room temperature. Tough, transparent, and flexible films were cast from a solution of polyesters in chloroform. X-Ray diffraction measurements displayed a broad halo at 20 congruent to 19 degrees indicating the amorphous nature of polyesters. Glass transition temperatures of polyesters were in the range 209-259 degrees C. The temperature at 10\% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of polyesters was in the range 435-500 degrees C indicating their good thermal stability. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 117: 2545-2552, 2010

}, keywords = {Aromatic polyesters, bisphenol, interfacial polycondensation, pendent naphthyl units}, issn = {0021-8995}, doi = {10.1002/app.32162}, author = {Honkhambe, Pandurang N. and Biyani, Mahesh V. and Bhairamadgi, Nagendra S. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000276790500011, title = {Synthesis and characterization of new aromatic polyesters containing cardo decahydronaphthalene groups}, journal = {European Polymer Journal}, volume = {46}, number = {4}, year = {2010}, month = {APR}, pages = {709-718}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

Three cardo bisphenols containing decahydronaphthalene group viz., 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bisphenol, 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bis-3-methylphenol and 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bis-3,5-dimethylphenol were synthesized starting from commercially available 2-naphthol and were utilized for synthesis of new aromatic polyesters by phase transfer-catalyzed interfacial polycondensation with isophthaloyl chloride, terephthaloyl chloride and a mixture of isophthaloyl chloride and terephthaloyl chloride (50:50 mol \%). Inherent viscosities and number average molecular weights (M(n)) of polyesters were in the range 0.35-0.84 dL/g and 13300-48,500 (Gel Permeation Chromatography, polystyrene standard), respectively. Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, meta-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetamide, and 1-methy1-2-pyrrolidinone at room temperature and could be cast into tough, transparent and flexible films from their chloroform solutions. Wide-angle X-ray diffraction measurements revealed the amorphous nature of polyesters. The glass transition temperature of polyesters was in the range 207-287 degrees C. The temperature at 10\% weight loss (T(10)), determined from thermogravimetric analysis of polyesters, was in the range 425-460 degrees C indicating their good thermal stability. (C) 2010 Elsevier Ltd. All rights reserved.

}, keywords = {bisphenol, Cardo, Decahydronaphthalene, polyester, Structure-property relationship}, issn = {0014-3057}, doi = {10.1016/j.eurpolymj.2009.12.028}, author = {Honkhambe, Pandurang N. and Bhairamadgi, Nagendra S. and Biyani, Mahesh V. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000291613900071, title = {Synthesis and characterization of organo-soluble poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing pendant pentadecyl chains}, journal = {Journal of Applied Polymer Science}, volume = {121}, number = {6}, year = {2011}, month = {SEP}, pages = {3689-3695}, publisher = {WILEY-BLACKWELL}, address = {111 RIVER ST, HOBOKEN 07030-5774, NJ USA}, abstract = {

Poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant pentadecyl chains were synthesized by polycondensation of each of the two bisphenol monomers viz, 1,1,1-[bis(4-hydroxyphenyl)-4{\textquoteright}-pentadecylphenyl] ethane and 1,1-bis(4-hydroxyphenyl)-3-pentadecyl cyclohexane with activated aromatic dihalides namely, 4,4{\textquoteright}-difluorobenzophenone, and 1,3-bis(4-fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene, in the presence of anhydrous potassium carbonate. Polymers were isolated as white fibrous materials with inherent viscosities and number average molecular weights in the range 0.70-1.27 dL g(-1) and 76,620-1,36,720, respectively. Poly(ether ether ketone) s and poly(ether ether ketone ketone) s were found to be soluble at room temperature in organic solvents such as chloroform, dichloromethane, tetrahydrofuran, and pyridine and could be cast into tough, transparent, and flexible films from their solutions in chloroform. Wide angle X-ray diffraction patterns exhibited a broad halo at around 2 theta = similar to 19 degrees indicating that the polymers containing pentadecyl chains were amorphous in nature. In the small-angle region, diffuse reflections of a typically layered structures resulting from the packing of pentadecyl side chains were observed. The temperature at 10\% weight loss, obtained from TG curves, for poly(ether ether ketone) s and poly(ether ether ketone ketone) s were in the range 416-459 degrees C, indicating their good thermal stability. A substantial drop in glass transition temperatures (68-78 degrees C) was observed for poly(ether ether ketone) s and poly(ether ether ketone ketone) s due to {\textquoteleft}{\textquoteleft}internal plasticization{\textquoteright}{\textquoteright} effect of flexible pendant pentadecyl chains. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 121: 3689-3695, 2011

}, keywords = {alkyl side-chain, Cashew nut shell liquid, CNSL, pentadecyl, poly(arylene ether)s, poly(ether ketone)s, polyethers, renewable}, issn = {0021-8995}, doi = {10.1002/app.34181}, author = {More, Arvind S. and Pasale, Sharad K. and Honkhambe, Pandurang N. and Wadgaonkar, Prakash P.} } @article { ISI:000319610100003, title = {Synthesis and characterization of poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant biphenyl and naphthyl groups}, journal = {High Performance Polymers}, volume = {25}, number = {3}, year = {2013}, month = {MAY}, pages = {260-267}, publisher = {SAGE PUBLICATIONS LTD}, address = {1 OLIVERS YARD, 55 CITY ROAD, LONDON EC1Y 1SP, ENGLAND}, abstract = {

New poly(ether ether ketone)s (PEEKs) and poly(ether ether ketone ketone)s (PEEKKs) containing pendant biphenyl and naphthyl groups were synthesized by nucleophilic substitution reaction of each of the four bisphenols viz., 1-(4- biphenylyl)- 1,1- bis(4- hydroxyphenyl) ethane, 1-(4- biphenylyl)- 1,1- bis(3- methyl, 4- hydroxyphenyl) ethane, 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-phenol and 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-3-methylphenol with 4,4{\textquoteright}- difluorobenzophenone and 1,3- bis(4- fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene in the presence of anhydrous potassium carbonate. Inherent viscosities and number-average molecular weights of polymers were in the range of 0.42-0.86 dl/g and 2.40-7.55 x 10(4), respectively. PEEKs and PEEKKs were amorphous in nature and were readily soluble in a wide range of organic solvents and could be cast into flexible and tough films from chloroform solution. Glass transition temperature of PEEKs and PEEKKs were in the range of 180 degrees C -200 degrees C. T-10 values of PEEKs and PEEKKs were in the range of 424 degrees C-512 degrees C in nitrogen atmosphere, indicating their good thermal stability.

}, keywords = {biphenyl, bisphenol, naphthyl, poly(ether ether ketone ketone)s, poly(ether ether ketone)s, Polycondensation, Thermal properties}, issn = {0954-0083}, doi = {10.1177/0954008312462731}, author = {Honkhambe, Pandurang N. and Dhamdhere, Neelam A. and Tawade, Bhausaheb V. and Salunkhe, Manikrao M. and Wadgaonkar, Prakash P.} }