@article { ISI:000250410500033, title = {Synthesis and characterization of new aromatic polyesters containing biphenyl side groups}, journal = {Journal of Applied Polymer Science}, volume = {106}, number = {5}, year = {2007}, month = {DEC}, pages = {3105-3110}, publisher = {JOHN WILEY \& SONS INC}, type = {Article}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

Aromatic polyesters containing biphenyl side groups were synthesized by phase-transfer catalyzed interfacial polycondensation of 1-(4-biphenylyl)-1,1-bis(4-hydroxyphenyl) ethane (BBHPE) with terephthaloyl chloride (TPC), isophthaloyl chloride (IPC), and a mixture of TPC/IPC (50: 50 mol ratio). Copolyesters were synthesized by utilizing different molar proportions of BBHPE and 4,4-isopropylidenediphenol (BPA) with IPC and TPC. The inherent viscosities of polyesters were in the range 0.44-1.26 dL/g. All the polyesters were soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, meta-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetamide, and 1-methyl-2-pyrrolidmone. Tough, transparent, and flexible films could be cast from chloroform solutions of these polyesters. WAXD measurements indicated that all the polyesters and copolyesters were amorphous in nature. Glass transition temperature of polyesters were in the range 198-256 degrees C, while the initial degradation temperature of polyesters were in the range 444-481 degrees C. Copolyesters derived from BBHPE exhibited improved solubility and higher glass transition temperatures compared to the corresponding polyesters based on BPA. (c) 2007 Wiley Periodicals, Inc.

}, keywords = {Aromatic polyesters, biphenyl side groups}, issn = {0021-8995}, doi = {10.1002/app.25862}, author = {Honkhambe, Pandurang N. and Avadhani, C. V. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000279996500008, title = {Synthesis and characterization of new aromatic polyesters containing pendent naphthyl units}, journal = {Journal of Applied Polymer Science}, volume = {117}, number = {5}, year = {2010}, month = {SEP}, pages = {2545-2552}, publisher = {JOHN WILEY \& SONS INC}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

Two bisphenols, viz., 4,4{\textquoteright}-[1-(2-naphthaleny-1)ethylidene]bisphenol and 4,4{\textquoteright}-[1-(2-naphthalenyl) ethylidene]bis-3-methylphenol were prepared by condensation of commercially available 2-acetonaphthanone with phenol and o-cresol, respectively. A series of new aromatic polyesters containing pendent naphthyl units was synthesized by phase-transfer-catalyzed interfacial polycondensation of these bisphenols with isophthaloyl chloride, terephthaloyl chloride, and a mixture of isophthaloyl chlorideiterephthaloyl chloride (50 : 50 mol \%). Inherent viscosities of polyesters were in the range 0.83-1.76 dL g(-1), while number average molecular weights (M(n)) were in the range 61,000-235,000 g mol(-1). Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, m-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetarnide, and 1-methyl-2-pyrrolidinone at room temperature. Tough, transparent, and flexible films were cast from a solution of polyesters in chloroform. X-Ray diffraction measurements displayed a broad halo at 20 congruent to 19 degrees indicating the amorphous nature of polyesters. Glass transition temperatures of polyesters were in the range 209-259 degrees C. The temperature at 10\% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of polyesters was in the range 435-500 degrees C indicating their good thermal stability. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 117: 2545-2552, 2010

}, keywords = {Aromatic polyesters, bisphenol, interfacial polycondensation, pendent naphthyl units}, issn = {0021-8995}, doi = {10.1002/app.32162}, author = {Honkhambe, Pandurang N. and Biyani, Mahesh V. and Bhairamadgi, Nagendra S. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article {45702, title = {Aromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups: synthesis and characterization}, journal = {Journal of Polymer Research}, volume = {24}, year = {2017}, month = {MAR }, pages = {57}, type = {Article}, abstract = {

A new bisphenol, 1,1-bis-[(4-hydroxyphenyl)-1-(4-phenylsulfonyl) phenyl)] ethane (DPSBP) was synthesized starting from diphenylsulfide and was characterized by spectroscopic methods. DPSBP was polycondensed with isophthalic acid chloride (IPC), terephthalic acid chloride (TPC) and a mixture of IPC and TPC (50: 50 mol\%) by phase-transfer catalysed interfacial polymerization method to obtain aromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups. A series of copolyesters was also obtained by polycondensation of varying molar proportions of DPSBP and bisphenol-A (BPA) with TPC. (Co) polyesters exhibited inherent viscosities in the range 0.56-1.57 dLg(-1) and number average molecular weights (Mn) were in the range 28,650-80,230 g/mol. Polyesters dissolved readily in common organic solvents such as dichloromethane, chloroform, tetrahydrofuran and aprotic polar solvents such as N-methylpyrrolidone, and N, N-dimethylacetamide. Tough, transparent and flexible films of polyesters could be cast from their chloroform solutions. X-Ray diffraction studies indicated amorphous nature of aromatic polyesters. Polyesters showed T-g values in the range 223-257 degrees C while T-10 values were in the range of 469-484 degrees C indicating their excellent thermal stability.

}, keywords = {Aromatic polyesters, Bulky pendent group, solubility, thermal stability}, issn = {1022-9760}, doi = {10.1007/s10965-017-1217-4}, author = {Bapat, Snehalata P. and Jadhav, Sushilkumar A. and Valsange, Nitin G. and Tawade, Bhausaheb V. and Honkhambe, Pandurang N. and Chavan, Nayaku N. and Wadgaonkar, Prakash P.} }