@article { ISI:000228797100048, title = {Preparation of ferroelectric BaNb2O6 the urea method}, journal = {Materials Letters}, volume = {59}, number = {14-15}, year = {2005}, month = {JUN}, pages = {1929-1931}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A precipitate was formed when an aqueous solution of BaCl2, NbF5 and urea in required ratio (the ratio of total metal cations to the urea is five) is heated on a water bath at 100 degrees C. This precipitate on decomposition at 600 degrees C yielded the nanocrystallites of BaNb2O6 (BN), as confirmed by X-ray diffraction study (XRD). This is a much lower temperature as compared to that prepared by traditional solid state method (1000 degrees C) as reported for the formation of BaNb2O6. Transmission electron microscope (TEM) investigations revealed that the average particle size is 85 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 900. The ferroelectric hysteresis loop parameters of these samples were also studied. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.02.028}, author = {Dhage, S. R. and Pasricha, R. and Ravi, V.} } @article { ISI:000238298100027, title = {Co-precipitation technique for the preparation of ferroelectric BaBi2Ta2O9}, journal = {Materials Chemistry and Physics}, volume = {98}, number = {2-3}, year = {2006}, month = {AUG}, pages = {344-346}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

A simple co-precipitation technique had been successfully applied for the preparation of pure ultrafine single phase BaBi2Ta2O9 (BBT). Ammonium hydroxide and ammonium oxalate were used to precipitate Ba2+, Bi3+ and Ta5+ cations simultaneously. No pyrochlore phase was found while heating powder at 800 degrees C and pure BaBi2Ta2O9 phase was found to be formed by X-ray diffraction. Particle size and morphology was studied by transmission electron spectroscopy (TEM). The room temperature dielectric constant at 1 kHz is 350. The ferroelectric hysteresis loop parameters of these samples were also studied. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.09.036}, author = {Dhage, S. R. and Pasricha, R. and Murugan, A. Vadivel and Ravi, V.} } @article { ISI:000254698300035, title = {Co-precipitation method for preparation of Bi3TiNbO9 powders}, journal = {Ceramics International}, volume = {34}, number = {3}, year = {2008}, month = {APR}, pages = {675-677}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A simple co-precipitation technique has been successfully used for the preparation of pure, ultrafine, single phase Bi3TiNbO9 (BTN). An aqueous ammonium hydroxide solution was used to simultaneously precipitate Bi3+, Ti4+ and Nb5+, cations as hydroxides under basic conditions (pH similar to 9). No pyrochlore phase was found while heating powder at 500 degrees C and pure BTN phase was found to be formed by X-ray diffraction (XRD). For comparison, BTN samples were also synthesized by the traditional solid state method. The sequence of phase formation in both cases were investigated by XRD studies. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, electronic material, Oxides, XRD}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2007.02.002}, author = {Gupta, U. N. and Samuel, V. and Muthurajan, H. and Kumar, H. H. and Patil, S. D. and Ravi, V.} }