@article { ISI:000251631200005, title = {Effect of substituent polarity, bulk, and substitution site toward enhancing gas permeation in dibromohexafluorobisphenol-A based polyarylates}, journal = {Journal of Polymer Science Part B-Polymer Physics}, volume = {45}, number = {23}, year = {2007}, month = {DEC}, pages = {3156-3168}, publisher = {JOHN WILEY \& SONS INC}, type = {Article}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

The gas permeation properties of polyarylates were tuned by varying nature and site of substituents present on both of its monomers, viz., bisphenol and dicarboxylic acid. The phenyl rings of hexafluorobisphenol-A were substituted in asymmetric manner by polar bromine to obtain dibromohexafluorobisphenol-A. This bisphenol was polymerized with equimolar mixture of iso- and terephthalic acid (base case), bromo- and nitroterephthalic acid (polar group substituted acids), 4,4{\textquoteright}-hexafluoroisopropylidene bis(benzoic acid), and t-butyl isophthalic acid (bulky group containing acids). Physical properties and gas permeation properties of these polyarylates were investigated to assess combined effects of asymmetric nature of bisphenol substitution, polar nature of substituent bromine, hexafluoroisopropylidene group present at the bridge position of bisphenol, and substituent present on the acid moiety. The combination of these substituent types led these polyarylates to lie near Robeson upper bound. The gas sorption analysis and estimation of diffusivity in these polyarylates shed a light on observed variations in gas permeation properties by attempted structural variations. (c) 2007 Wiley Periodicals, Inc.

}, keywords = {asymmetric substitution, Diffusion, Gas permeation, gas sorption, polyarylates, selectivity, structure-property relations}, issn = {0887-6266}, doi = {10.1002/polb.21314}, author = {Ishole, Yogesh S. and Karadkar, Prasad R. and Kharul, Ulhas K.} } @article { ISI:000255339200058, title = {Synthesis, characterization, and gas permeability of aromatic polyimides containing pendant phenoxy group}, journal = {Journal of Applied Polymer Science}, volume = {108}, number = {6}, year = {2008}, month = {JUN}, pages = {3881-3889}, publisher = {JOHN WILEY \& SONS INC}, type = {Article}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

A diamine containing a pendant phenoxy group, 1-phenoxy-2,4-diaminobenzene, was synthesized and condensed with different aromatic dianhydrides [4,4{\textquoteright}-oxydiphthalic dianhydride, 4,4{\textquoteright}-(hexafluoroisopropylidene)diphthalic anhydride, 3,3{\textquoteright},4,4-benzophenone tetracarboxylic dianhydride, 3,3{\textquoteright},4,4{\textquoteright}-biphenyltetracorboxylic dianhydride, and pyromellitic dianhydride] by one-step synthesis at a high temperature in m-cresol to obtain polyimides in high yields. Most of the polyimides exhibited good solvent solubility and could be readily dissolved in chloroform, sym-tetrachloroethane, N,N-dimethylformamide, NN-dimethylacetamide, and nitrobenzene. Their inherent viscosities were in the range of 0.33-1.16 dL/g. Wide-angle X-ray spectra revealed that these polymers were amorphous in nature. All these polyimides were thermally stable, having initial decomposition temperatures above 500 degrees C and glass-transition temperatures in the range of 248-281 degrees C. The gas permeability of 4,4{\textquoteright}-oxydiphthalic dianhydride and 4,4{\textquoteright}-(hexafluoroisopropylidene)diphthalic anhydride based polyimides was investigated with pure gases: He, H-2, O-2, Ar, N-2, CH4, and CO2. A polyimide containing a -C(CF3)(2)- linkage showed a good combination of permeability and selectivity. (C) 2008 Wiley Periodicals, Inc.

}, keywords = {Gas permeation, membranes, polyimides, selectivity, structure-property relations}, issn = {0021-8995}, doi = {10.1002/app.28074}, author = {Kothawade, Sandeep S. and Kulkarni, Mahesh P. and Kharul, Ulhas K. and Patil, Anandrao S. and Vernekar, Subhash P.} } @article {44241, title = {Synthesis, characterization, and gas permeation properties of adamantane-containing polymers of intrinsic microporosity}, journal = {Journal of Polymer Science Part A-Polymer Chemistry}, volume = {56}, year = {2018}, month = {JAN }, pages = {16-24}, type = {Article}, abstract = {

A new bis(catechol) monomer, namely, 4,4-((1r,3r)-adamantane-2,2-diyl)bis(benzene-1,2diol) (THADM) was synthesized by condensation of 2-adamantanone with veratrole followed by demethylation of the formed (1r,3r)-2,2-bis(3,4 dimethoxyphenyl)adamantane. Polycondensation of THADM and various compositions of THADM and 5,5,6,6-tetrahydroxy-3,3,3,3-tetramethylspirobisindane was performed with 2,3,5,6-tetrafluoroterephthalonitrile (TFTPN) to obtain the homopolymer and copolymers. These polymers demonstrated good solubility in common organic solvents such as dichloromethane, chloroform, and tetrahydrofuran and could be cast into tough films from their chloroform solutions. GPC analysis revealed that number average molecular weights of polymers were in the range 48,100-61,700 gmol(-1), suggesting the formation of reasonably high molecular weight polymers. They possessed intrinsic microporosity with Brunauer-Emmett-Teller (BET) surface area in the range 703-741 m(2)g(-1). Thermogravimetric analysis of polymers indicated that 10\% weight loss temperature was in the range 513-518 degrees C demonstrating their excellent thermal stability. THADM-based polymer of intrinsic microporosity (PIM) showed P(CO2)=1080, P(O-2)=232 and appreciable selectivity [(CO2/CH4)=22.6, (CO2/N-2)=26.7, and (O-2/N-2)= 5.7]. The gas permeability measurements revealed that with increase in the content of adamantane units in PIMs, selectivity increased and permeability decreased, following the trade-off relationship. The gas separation properties of PIMs containing adamantane units were located close to 2008 Robeson upper bound for gas pairs such as CO2/CH4, CO2/N-2, H-2/N-2, and O-2/N-2. (c) 2017 Wiley Periodicals, Inc.

}, keywords = {adamantane, Gas permeation, intrinsic microporosity, membranes, structure-property relations}, issn = {0887-624X}, doi = {10.1002/pola.28710}, author = {Shrimant, Bharat and Shaligram, Sayali V. and Kharul, Ulhas K. and Wadgaonkar, Prakash P.} }