@article { ISI:000229103900015, title = {Nanostructured tin oxide: synthesis and gas-sensing properties}, journal = {Materials Chemistry and Physics}, volume = {92}, number = {2-3}, year = {2005}, month = {AUG}, pages = {384-388}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Pure and Ru-doped nanostructured SnO2 sensing materials were synthesized using a modified Pechini route. Incorporation of Ru in SnO2 results in the reduction of particle size (8.3 nm) compared with that of the pure SnO2 (28.2 nm). Moreover, the sensor exhibited a reasonably good sensitivity towards both H-2 and liquified petroleum gas (LPG). The effect of Ru incorporation, operating temperature, and gas concentration on the structure, morphology, and sensitivity is discussed using the results of X-ray diffraction (XRD), and scanning electron microscopy (SEM) along with sensing performance. {\textcopyright} 2005 Elsevier B.V. All rights reserved.

}, keywords = {hydrogen and hydrocarbon sensor, Nanostructure, ruthenium, tin oxide}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.01.050}, author = {Niranjan, R. S. and Hwang, Young Kyu and Kim, D. K. and Jhung, S. H. and Chang, J. S. and Mulla, Imtiaz S.} } @article { ISI:000255692100010, title = {Fe-doped SnO(2) nanomaterial: a low temperature hydrogen sulfide gas sensor}, journal = {Materials Chemistry and Physics}, volume = {109}, number = {2-3}, year = {2008}, month = {JUN}, pages = {230-234}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

The effect of Fe-doping on the surface chemistry and gas-sensing properties of nanocrystalline tin oxide is analyzed. The pristine and Fe-doped SnO(2) are synthesized by the modified Pechini citrate route that produces around 40 and 18 nm sized nanoparticles, respectively. 1 at.\% Fe-doped SnO(2) shows significantly high selectivity towards hydrogen sulfide gas with capability to detect even 10 ppm of hydrogen sulfide at room temperature, with change of about one order of magnitude in the resistance within 5-15 s. In comparison, pristine SnO(2) shows negligible response towards H(2)S at room temperature. The ideal response and recovery of Fe-doped SnO(2) at low concentration of gas suggests Fe-doped SnO(2) nanomaterial as a potential low cost, low temperature H(2)S gas sensor. (C) 2007 Elsevier B.V. All rights reserved.

}, keywords = {Fe-doping, H(2)S, nanomaterial, Sensor, tin oxide}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2007.11.024}, author = {Vaishampayan, Mukta V. and Deshmukh, Rupah G. and Walke, Pravin and Mulla, Imtiaz S.} } @article { ISI:000256116100044, title = {Influence of Pd doping on morphology and LPG response of SnO2}, journal = {Sensors and Actuators B-Chemical}, volume = {131}, number = {2}, year = {2008}, month = {MAY}, pages = {665-672}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

In the present study nanocrystalline pristine and Pd-doped SnO2 (Pd:SnO2) with various mol\% Pd have been synthesized by a modified Pechini citrate route. Transmission electron microscopy and X-ray powder diffraction studies were used to characterize the morphology, crystallinity, and structure of the SnO2 and Pd:SnO2. The response of the pristine SnO2 and Pd:SnO2 was studied towards different reducing gases. The 1.5 mol\% Pd doping showed an enhanced response of 75 and 95\% towards LPG at as low as 50 and 100 degrees C, respectively, which were quite large high value as compared with pristine SnO2 (38 and 35\% at 50 and 100 degrees C, respectively). Structural characterization revealed that Pd doping reduced the crystallite size of SnO2 and helps in the formation of distinct spherical nanospheres at a calcinations temperature of 500 degrees C. Thus the increase in LPG response can be correlated with the spherical morphology, a decrease in the crystallite size (11 nm) due to doping with Pd as compared with the pristine SnO2 (26 nm) and main role of Pd as a catalyst. (c) 2008 Elsevier B.V. All rights reserved.

}, keywords = {LPG sensor, nanospheres, palladium doping, tin oxide}, issn = {0925-4005}, doi = {10.1016/j.snb.2007.12.055}, author = {Vaishampayan, Mukta V. and Deshmukh, Rupali G. and Mulla, Imtiaz S.} } @article { ISI:000258037300073, title = {RuO(2) doped SnO(2) nanobipyramids on Si (100) as a field emitter}, journal = {Thin Solid Films}, volume = {516}, number = {18}, year = {2008}, month = {JUL}, pages = {6388-6391}, publisher = {ELSEVIER SCIENCE SA}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Thin films of RuO(2): SnO(2) nanobipyramids have been grown on silicon (100) flat substrates, and their field emission behavior has been investigated. The field emission experiments have been performed in parallel plate configuration. In this experiment, the onset field for 0. 1 gA/ cm 2 current density has been found to be 0.2 V/mu m. The Fowler-Nordheim plot shows non-linear nature typical that of a semiconductor. The field enhancement factor has been estimated to be 35,600 cm(-1), indicating that the field emission originates from the nanometric features of the emitter. The current stability recorded at a preset value of I tA is observed to be good. Our field emission results on RuO(2): SnO(2) nanobipyramids indicate that, RuO(2): SnO(2) nanobipyramids are a potential candidate for futuristic field emission based devices. (c) 2008 Elsevier B.V. All rights reserved.

}, keywords = {doped semiconductor, field emitter, field enhancement factor, ruthenium oxide, tin oxide}, issn = {0040-6090}, doi = {10.1016/j.tsf.2007.12.160}, author = {Bhise, Ashok B. and Late, Dattatray J. and Ramgir, Niranjan S. and More, Mahendra A. and Mulla, Imtiaz S. and Pillai, Vijayamohanan K. and Joag, Dilip S.} }