@article { ISI:000232196200008, title = {TiO2 ceramic varistor modified with tantalum and barium}, journal = {Materials Science and Engineering B-Solid State Materials for Advanced Technology}, volume = {123}, number = {1}, year = {2005}, month = {NOV}, pages = {50-52}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

The non-linear current (I)-voltage (V) characteristics of titanium dioxide doped with small quantities of tantalum and barium (99.9 TiO2 + 0.1 Ta and 99.4 TiO2 + 0.1 Ta + 0.5 Ba, all are in at.\%) were investigated. These samples have the non-linear coefficient (alpha) values of (20-30) with high breakdown voltages (E-B similar to 400-700 V mm(-1)). The pentavalent tantalum acts as donor and increases the electronic conductivity. The higher electrical conductivity and decrease in the breakdown field strength with barium addition is attributed to higher density. The acceptor like surface states formed by barium ions segregate to grain boundaries due size misfit to thereby modifying the electrical barrier characteristics of grain boundaries. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Oxides, TiO2, varistor, X-ray diffraction}, issn = {0921-5107}, doi = {10.1016/j.mseb.2005.06.015}, author = {Gaikwad, A. B. and Navale, SC and Ravi, V} } @article { ISI:000237439300005, title = {Coprecipitation technique to prepare NaNbO3 and NaTaO3}, journal = {Bulletin of Materials Science}, volume = {29}, number = {2}, year = {2006}, month = {APR}, pages = {123-125}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

A simple coprecipitation technique has been used successfully for the preparation of pure, ultrafine, single phases of NaNbO3 (NN) and NaTaO3 (NT). An alcoholic solution of ammonium carbonate and ammonium hydroxide was used to precipitate Na+ and Nb5+ (or Ta5+) cations under basic conditions as carbonate and hydroxide, respectively. On heating at 700 degrees C, these precursors produce respective products. For comparison, both NN and NT powders were also prepared by the traditional solid state method. The phase purity and lattice parameters were studied by powder X-ray diffraction (XRD). The particle size and morphology were studied by scanning electron microscopy (SEM).

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, electronic materials, Oxides, X-ray methods}, issn = {0250-4707}, doi = {10.1007/BF02704604}, author = {Samuel, V and Gaikwad, A. B. and Ravi, V} } @article { ISI:000238866300004, title = {Coprecipitation technique to prepare Sr0.5Ba0.5Nb2O6}, journal = {Bulletin of Materials Science}, volume = {29}, number = {3}, year = {2006}, month = {JUN}, pages = {221-223}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

An aqueous mixture of ammonium oxalate and ammonium hydroxide was used to coprecipitate barium and strontium ions as oxalates and niobium ions as hydroxide under basic conditions. This precursor on calcining at 750 degrees C yielded Sr0.5Ba0.5Nb2O6 phase. This is a much lower temperature than that prepared by traditional solid state method (1000 degrees C) as reported for the formation of Sr0.5Ba0.5Nb2O6 (SBN). Transmission electron microscopic (TEM) investigations revealed that the average particle size was 80 nm for the calcined powders. The room temperature dielectric constant at I kHz was found to be 1100. The ferroelectric hysteresis loop parameters of these samples were also studied.

}, keywords = {Ceramics, Electron microscopy, ferroelectricity, Oxides, X-ray diffraction}, issn = {0250-4707}, doi = {10.1007/BF02706488}, author = {Murugan, A. Vadivel and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000244008300030, title = {Co-precipitation technique to prepare BaTa2O6}, journal = {Ceramics International}, volume = {33}, number = {2}, year = {2007}, month = {JAN}, pages = {297-299}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A mixture of ammonium oxalate and ammonium hydroxide was used to co-precipitate barium and tantalum ions as barium oxalate and tantalum hydroxide under basic conditions. On calcination at 750 degrees C, this precursor yielded BaTa2O6 (BT) ceramics. This is much lower temperature as compared to that prepared by traditional solid-state method (1000 degrees C) as reported for the formation of BaTa206. Transmission electron microscope (TEM) investigations revealed that the average particle size is 70 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 100. (c) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {barium tantalate, Ceramics, Electron microscopy, Oxides, X-ray diffraction}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2005.08.012}, author = {Navale, S. C. and Samuel, Violet and Gaikwad, A. B. and Ravi, V.} } @article { ISI:000246158300001, title = {Coprecipitation technique to prepare CoTa2O6 and CoNb2O6}, journal = {Materials Letter}, volume = {61}, number = {11-12}, year = {2007}, month = {MAY}, pages = {2127-2129}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

An aqueous solution of sodium hydroxide was used to coprecipitate cobalt and tantalum (or niobium) ions from their precursors as hydroxides under basic conditions. This precipitate yielded CoTa2O6 (CT) or CoNb2O6 (CN) ceramics on calcining at 700 degrees C, i.e. at a temperature much lower than 900 degrees C, reported for the formation of these powders prepared by the traditional solid state method. The X-ray diffraction (XRD) studies were employed to investigate phase contents and lattice parameters. The morphology of the synthesized powders was investigated by transmission electron microscopy (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, electronic materials, Oxides, X-ray methods}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.08.024}, author = {Mulla, Imtiaz S. and Natarajan, N. and Gaikwad, A. B. and Samuel, V. and Guptha, U. N. and Ravi, V.} } @article { ISI:000246158300058, title = {Coprecipitation technique to prepare NiNb2O6}, journal = {Materials Letter}, volume = {61}, number = {11-12}, year = {2007}, month = {MAY}, pages = {2354-2355}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A mixture of ammonium carbonate and ammonium hydroxide was used to coprecipitate nickel and niobium ions as nickel carbonate and niobium hydroxide under basic conditions. This precursor yielded NiNb2O6 (NN) ceramics on calcining at 700 degrees C (at a temperature lower than 800 degrees C which is necessary for the formation of NiNb2O6 when prepared by the traditional solid state method). The average particle size and morphology of these powders were investigated by transmission electron microscope (TEM). (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, Electron microscopy, electronic materials, Oxides, X-ray methods}, issn = {0167-577X}, doi = {10.1016/j.matlet.2006.09.010}, author = {Samuel, V. and Gaikwad, A. B. and Jadhav, A. D. and Natarajan, N. and Ravi, V.} } @article { ISI:000246260000011, title = {Preparation of nanocrystalline ferroelectric CaBi4Ti4O15 by citrate gel method}, journal = {Ceramics International}, volume = {33}, number = {4}, year = {2007}, month = {JAN}, pages = {569-571}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A gel was formed when an aqueous solution of CaCl2, BiNO3, TiOCl2 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 700 degrees C produced nano crystallites of the ternary oxide, CaBi4Ti4O15 (CBT). The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). The room temperature dielectric constant at 1 kHz is 390. The ferroelectric hysteresis loop parameters of these samples were also studied by a home-built Sawyer-tower circuit. (c) 2006 Elsevier Ltd and Techna Group S.H. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray methods}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2005.11.006}, author = {Murugan, A. Vadivel and Gaikwad, A. B. and Samuel, V. and Ravi, V.} } @article { ISI:000254820000016, title = {La0.67Ce0.03Sr0.3MnO3-coupled microwave assisted ultra-fast synthesis of nanocrystalline cobalt oxide and Bismuth oxide}, journal = {Materials Letters}, volume = {62}, number = {10-11}, year = {2008}, month = {APR}, pages = {1511-1513}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Bismuth hydroxide and Cobalt hydroxide gels were freshly prepared by adding aqueous sodium hydroxide to their corresponding nitrates under basic conditions. Then they were oven dried at 373 K and found to be amorphous in X-ray diffraction (XRD) study. They crystallized into their respective oxides by microwave irradiation (2.45 GHz) in merely 2 min using La0.67Ce0.03Sr0.3MnO3 (LCSMO) as couplant in a microwave domestic oven (similar to 100 W). This is the lowest temperature treatment and synthesis time so far reported in the literature for the formation of these systems. Formation of nanocrystallites of Bi2O3 (10 nm) and Co3O4 (15 nm) has been confirmed by XRD. Normally these hydroxides produce oxides only on heating at temperature \>673 K or digesting them at 373 K for 4 - 6 hours as reported by us earlier. Microwave assisted heating proves to be a novel technology whose applications can be carefully harnessed due to its unique effects compared to the conventional heating, such as rapid volumetric heating, shortened reaction time and energy saving. (C) 2007 Elsevier B.V. All rights reserved.

}, keywords = {Citrate gel method, Manganites, Microwave, Oxides}, issn = {0167-577X}, doi = {10.1016/j.matlet.2007.09.013}, author = {Rajagopal, Rajashree and Mona, J. and Joshi, Rakesh S. and Kale, Sangeeta N. and Pradhan, Sivararn and Gaikwad, A. B. and Ravi, V.} } @article { ISI:000255612400002, title = {Preparation of ferroelectric CaBi(4)Ti(4)O(15) powders from novel hydroxide precursors}, journal = {Materials Letters}, volume = {62}, number = {12-13}, year = {2008}, month = {APR}, pages = {1751-1753}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Ferroelectric CaBi(4)Ti(4)O(15) (CBT) powders were prepared for the first time from their respective hydroxides. Commercially purchased Ca(OH)(2) is mixed thoroughly with freshly prepared Bi(OH)(3) and Ti(OH)(4) in stoichiometrie ratio and heated at different temperatures ranging from 100 to 600 degrees C. The CBT phase found to be formed at 500 degrees C by the X-ray diffraction studies. This is the lowest temperature so far reported in the literature for the formation of CBT phase. The advantage of this method is that it also avoids the formation of calcium carbonate phase during synthesis. The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD) method. The average particle size and morphology were studied by scanning electron microscopy (SEM) technique. (c) 2007 Elsevier B.V All rights reserved.

}, keywords = {CaBi(4)Ti(4)O(15), Ceramics, Chemical synthesis, Electron microscopy, Oxides, X-ray methods}, issn = {0167-577X}, doi = {10.1016/j.matlet.2007.09.080}, author = {Deshmukh, Rupali G. and Vaishampayan, Mukta V. and Darshane, Sonali L. and Mulla, Imtiaz S. and Gaikwad, A. B. and Rao, N. Kotaserwara and Ravi, V.} }